Development of Electrically Conductive Nanocrystalline Thin Film for Optoelectronic Applications

• Autorzy: Das S K. , Islam J. M. M. , Hasan M. , Kabir H. , Gafur Md. A. , Hoque E. , Khan M. A.
• Języki publikacji: EN

Abstrakty

EN

Sodium alginate (TiO2) sand composites were prepared by solution casting. Purified sand was added in the composite films to increase electrical conductivity. Electrical properties such as conductivity, capacitance, dielectric constant, and loss tangent of the composites were investigated. The current voltage characteristics for all the composites showed ohmic behavior. All the electrical properties have been found to improve with the incorporation of sand (SiO2) but 6 % sand containing composite exhibits the best electrical properties. The mechanical properties tensile strength (TS), elongation at break (Eb) and Young modulus for 6 % sand containing composite film are found to be 4.445 MPa, 9.76 %, and 72.8 MPa respectively. The experimental results reveal that the blended films exhibit higher stability and improved mechanical properties of both tensile strength and elongation at break in dry state. Water absorption properties of the composites are found to decrease with the increase of sand content. Lowest water uptake properties and highest stability were demonstrated by 6 % sand containing sample. Electrically conductive composite films have useful applications for solar cells and optoelectronics. Thus, this study is very much expected to aid in the design and selection of proper composite for the potential application of solar cell and optoelectronics.

Słowa kluczowe

EN

Conductive thin film; composite; TiO2; Solar cell; Optoelectronics; Sodium alginate

• Wydawca: Przedsiębiorstwo Wydawnictw Naukowych "DARWIN"
• Czasopismo: International Letters of Chemistry, Physics and Astronomy
• Rocznik: 2013
• Tom: Vol. 10, iss. 1
• Strony: 90--101
• Opis fizyczny: Bibliogr. 25 poz., wykr.

Twórcy

autor

Das S K.

• Department of Physics, University of Chittagong, Chittagong - 4331, Bangladesh
• [e-mail]

autor

Islam J. M. M.

• Institute of Radiation and Polymer Technology, Bangladesh Atomic Energy Commission, Dhaka - 1000, Bangladesh

autor

Hasan M.

• Department of Physics, Jahangirnagar University, Savar, Dhaka - 1342, Bangladesh

autor

Kabir H.

• Department of Physics, Jahangirnagar University, Savar, Dhaka - 1342, Bangladesh

autor

Gafur Md. A.

• Pilot Plant and Process Development Centre, Bangladesh Council of Scientific and Industrial Research, Dhaka, Bangladesh

autor

Hoque E.

• Department of Physics, Jahangirnagar University, Savar, Dhaka - 1342, Bangladesh

autor

Khan M. A.

• Institute of Radiation and Polymer Technology, Bangladesh Atomic Energy Commission, Dhaka - 1000, Bangladesh

Bibliografia

• [1] Lay G., Rehm J., Stepto R. F., Thoma M., Sachetto J., Lentz D. J., Silbiger J., U.S. Patent No. 5,095,054 (1992).
• [2] Hamal D. B., Klabunde K. J., J. Colloid Interface Sci. 311 (2007) 514-522, http://dx.doi.org/10.1016/j.jcis.2007.03.001.
• [3] B. Tryba, A.W. Morawski, M. Inagaki, Appl. Catal. B: Environ. 46 (2003) 203-208, http://dx.doi.org/10.1016/S0926-3373(03)00214-5.
• [4] P. Chrysicopoulou, D. Davazoglou, Chr. Trapalis, G. Kordas, Thin Solid Films 323 (1998) 188-193, http://dx.doi.org/10.1016/S0040-6090(97)01018-3
• [5] Lee J. W., Kong S., Kim W. S., and Kim J., Mater. Chem. Phys. 106 (2007) 39-44, http://dx.doi.org/10.1016/j.matchemphys.2007.05.019.
• [6] Wang W., Tao J., Wang T., Wang L., Rare Met. 26 (2007) 136-141, http://dx.doi.org/10.1016/S1001-0521(07)60173-9.
• [7] Doh J. G., Hong J. S., Vittal R., et al., Chem. Mater. 16 (2004) 493-497. doi:10.1021/cm030542q.
• [8] Zhang D., Yoshida Y., Oekermann T., et al., Adv. Funct. Mater. 16 (2006) 1228-1234, doi:10.1002/adfm.200500700..
• [9] Rothschild, A., Edelman, F., Komem, Y., et al., Sensor Actuat., Ser. B, 67 (2000) 282-289, http://dx.doi.org/10.1016/S0925-4005(00)00523-2.
• [10] Shankar K., Tep K. C., Mor G. K., et al., J. Phys., Ser. D: Appl. Phys. 39 (2006) 2361-2366, doi:10.1088/0022-3727/39/11/008.
• [11] Diebold U., Appl. Phys., Ser. A 76 (2003) 681-687, doi:10.1007/s00339-002-2004-5.
• [12] Choi S. Y., Mamak M., Speakman S., et al., Small 1 (2005) 226-232. doi:10.1002/smll.200400038.
• [13] Chu S. Z., Inoue S., Wada K., Li D., et al., Langmuir 21 (2005) 8035-8041, doi:10.1021/la050902j.
• [14] Kim K. D., Han D. N., Lee J. B., et al., Scrip. Mater. 54 (2006) 143-146, http://dx.doi.org/10.1016/j.scriptamat.2005.09.054.
• [15] Wang H., Lewis J. P., J. Phys., Ser. C 17 (2006) L 209-213, doi:10.1088/0953-8984/17/21/L01.
• [16] Pan J. H., Lee W. I., Chem. Mater. 18 (2006) 847-853, doi:10.1021/cm0522782.
• [17] Bavykin D. V., Friedrich J. M., Walsh F. C., Adv. Mater. 18 (2006) 2807-2824, doi:10.1002/adma.200502696.
• [18] Standard Methods for the Sampling and Testing of Gelatins, Gelatin Manufacturers Institute of America, Inc., 501 fifth Ave., Room 1015, New York, NY.
• [19] Ali A., Studies on the Degradation of Jute fibre, An M.Sc. Thesis, Rajshahi University, Rajshahi, Bangladesh, 66 (1987) 29-31.
• [20] Leach D. C., Mechanical & Fire Properties of APC-2 Presented at SAMPLE at Albuqueeque, 1987, 9-11.
• [21] Bipasha Bose, Effect of water absorption on the mechanical properties of jute fiber reinforced polymer composites, 2005.
• [22] ASTM Designation: D570-81, Standard Test Method for water absorption of plastic, 1988, 141-143.
• [23] Farnades F. N., Riz A. I., Garder M., Aranda P., Ruiz-Hitzky E., Journal of Nanoscience and Nanotechnology, in press 2008.
• [24] Caio M. Paranhos, G. Bluma Soares, et al, Macromol. Mater. Eng. 292 (2007) 620-626.
• [25] Zanetti M., Lomakin S., Camino G., Macromal. Mater. Eng. 279 (2000) 1-9, doi:10.1002/1439-2054(20000601)279:1<1::AID-MAME1>3.0.CO;2-Q.