Diffusible hydrogen content in the deposited metal of multilayer welded joints

• Autorzy: Fydrych D. , Świerczyńska A. , Rogalski G.

Identyfikatory

DOI

10.7494/mafe.2014.40.4.221

Warianty tytułu

PL

Zawartość wodoru dyfundującego w stopiwie wielościegowych złączy spawanych

• Języki publikacji: EN

Abstrakty

EN

This article describes the manufacturing technology of multilayer joints in terms of controlling the diffusible hydrogen content. The diffusible hydrogen content in deposited metal for multilayer welded joints made of covered rutile electrodes or covered cellulosic and basic electrodes was determined. It was found that, after four beads, the diffusible hydrogen content decreases from 36 m l/100 g to 18 ml/100 g in the ca se of the first technology, and about 40 ml/100 g to a level of 12 ml/100 g in the second. The explanation of the mechanisms responsible for this phenomenon and direction s for further study have been proposed.

PL

W artykule scharakteryzowano technologię wytwarzania złączy wielościegowych w aspekcie kontroli ilości wodoru dyfundującego. Oznaczono zawartość wodoru dyfundującego w stopiwie dla wielościegowych złączy spawanych wykonanych dwoma technologiami: za pomocą elektrod o otulinie rutylowej oraz celulozowej i zasadowej. Ustalono, że po wykonaniu czte- rech ściegów ilość wodoru dyfundującego spada w przypadku pierwszej technologii z poziomu36 ml/100 g do 18 ml/100 g, natomiast w drugim z około 40 ml/100 g do poziomu 12 ml/100 g. Wyjaśniono mechanizmy odpowiedzialne za to zjawisko i zasugerowano kierunki kontynuacji badań.

Słowa kluczowe

EN

diffusible hydrogen; manual metal arc welding; rutile electrodes; cellulosic electrodes; basic electrodes

PL

wodór dyfundujący; spawanie elektrodami otulonymi; elektrody rutylowe; elektrody celulozowe; elektrody zasadowe

• Wydawca: AGH University of Science and Technology Press
• Czasopismo: Metallurgy and Foundry Engineering
• Rocznik: 2014
• Tom: Vol. 40, no. 4
• Strony: 221--229
• Opis fizyczny: Bibliogr. 24 poz., fot., rys., tab., wykr.

Twórcy

autor

Fydrych D.

• Gdańsk University of Technology, Faculty of Mechanical Engineering, Gdańsk, Poland

autor

Świerczyńska A.

• Gdańsk University of Technology, Faculty of Mechanical Engineering, Gdańsk, Poland

autor

Rogalski G.

• Gdańsk University of Technology, Faculty of Mechanical Engineering, Gdańsk, Poland

Bibliografia

• [1] Widgery D.: Spawanie rurociągów gazowych w nowym stuleciu. Biuletyn Instytutu Spawalnictwa, 3 (2000), 66–68 [in Polish]
• [2] Felber S.: Mechanical-technological and fracture mechanical properties of the high grade pipeline-steel X80 with results of different pipeline-projects. Welding in the World, 5–6 (2008), 42–50
• [3] Felber S.: Welding of the high grade pipeline-steel X80 and description of different pipeline-projects. Welding in the World, 5–6 (2008), 19–41
• [4] Lezzi F., Costa L.: The development of conventional welding processes in naval construction. Welding International, 10 (2013), 786–797
• [5] Wang G., Chen Z.G.: Welding Technology Research for the Train Bogie. Applied Mechanics and Materials, 423 (2013), 784–787
• [6] De Rissone N.M.R., Farias J.P., Bott I.D.S., Surian E.S.: ANSI/AWS A5.1-91 E6013 Rutile Electrodes: The Effect of Calcite. Welding Journal, 7 (2002), 113–124
• [7] Liu H., Li H., Li Z., Shi Y.: Experimental study on metal transfer and welding spatter characteristics of cellulose electrode. Chinese Journal of Mechanical Engineering, 23 (2010), 793–796
• [8] Ramirez J.E., Johnson M.: Effect of welding parameters and electrode condition on alloying enrichment of weld metal deposited with coated cellulosic electrodes. Welding Journal, 11 (2010), 232–242
• [9] Pakos R.: Ocena technologii spawania stali o podwyższonej wytrzymałości elektrodą celulozową. Przegląd Spawalnictwa, 4 (2011), 10–17 [in Polish]
• [10] Pakos R.: Właściwości złączy spawanych wykonanych elektrodami zasadowymi i celulozowymi. Przegląd Spawalnictwa, 5 (2011), 7–12 [in Polish]
• [11] Brózda J., Zeman M.: Zwijana na gorąco w kręgi stal z podwyższoną zawartością niobu na rurociągi przesyłowe i jej spawalność. XVII Seminar: Materials testing for the needs of power plants and power industry. Zakopane, 23–25.06.2010, 101–115 [in Polish]
• [12] Tasak E.: Welding metallurgy. JAK, Kraków, 2008 [in Polish]
• [13] Kozak T.: Resistance to cold cracking of welded joints made of P460NL1 steel. Advances in Materials Science, 3 (2011), 20–27
• [14] Pokhodnya I.K., Yavdishchin I.R., Paltsevich A.P., Shvachko V.I., Kotelchuk A.S.: Metallurgy of arc welding. Interaction metal with gases. Naukova Dumka, Kiev, 2004
• [15] Pańcikiewicz K., Zielińska-Lipiec A., Tasak E.: Cracking of high-strength steel welded joints. Advances in Materials Science, 3 (2013), 76–85
• [16] Fydrych D., Tomków J., Świerczyńska A.: Determination of diffusible hydrogen content in deposited metal of rutile electrodes by glycerin method. Metallurgy and Foundry Engineering, 1 (2013), 47–54
• [17] Świerczyńska A.: Effect of technological factors on diffusing hydrogen content in the weld deposit of rutile flux-cored wires. Institute of Welding Bulletin, 5 (2013), 66–71
• [18] Fydrych D., Świerczyńska A., Tomków J.: Diffusible Hydrogen Control in Flux Cored Arc Welding Process. Key Engineering Materials, 597 (2014), 171–178
• [19] Fydrych D., Malinowski P., Świerczyńska A., Rogalski G.: Pomiary ilości wodoru dyfundującego w stopiwie elektrod celulozowych i zasadowych. Przegląd Spawalnictwa, 8 (2014), 2–6 [in Polish]
• [20] Kotecki D.J.: Hydrogen reconsidered. Welding Journal, 8 (1992), 35–43
• [21] Padhy G.K., Komizo Y.: Diffusible hydrogen in steel weldments-a status review. Transactions of JWRI, 1 (2013), 39–62
• [22] Signes E.G., Howe P.: Hydrogen-assisted cracking in high-strength pipeline steels. Welding Journal, 8 (1988), 1635–1705
• [23] Yue X., Feng X.L., Lippold J.C.: Effect of diffusible hydrogen level on heat-affected zone hydrogen-induced cracking of high-strength steels. Welding in the World, 1 (2014), 101–109
• [24] PN–EN ISO 3690:2012 Welding and allied processes – Determination of hydrogen content in arc weld metal