Studies on the Corrosion Resistance of Laser-Welded Inconel 600 and Inconel 625 Nickel-Based Superalloys

• Autorzy: Łyczkowska K. , Michalska J.

Identyfikatory

DOI

10.1515/amm-2017-0100

• Języki publikacji: EN

Abstrakty

EN

The paper presents the results of the electrochemical corrosion tests of Inconel 600 and Inconel 625 laser-welded superalloys. The studies were conducted in order to assess the resistance to general and pitting corrosion in 3.5% NaCl solution. It was found that Inconel 600 possesses good corrosion resistance, however Inconel 625 is characterized by a greater resistance to general and also to pitting corrosion of the weld as well as the base metal.

Słowa kluczowe

EN

electrochemical corrosion; Inconel 600; Inconel 625; pitting corrosion; laser welding

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2017
• Tom: Vol. 62, iss. 2A
• Strony: 653--656
• Opis fizyczny: Bibliogr. 12 poz., rys., tab.

Twórcy

autor

Łyczkowska K.

• Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, Institute of Metals Technology, 8 Krasińskiego Str., 40-019 Katowice, Poland

autor

Michalska J.

• Silesian University Of Technology, Faculty Of Chemistry, Department Of Inorganic Chemistry, Analytical Chemistry And Electrochemistry,6 Krzywoustego Str., 44-100 Gliwice, Poland

Bibliografia

• [1] J. Adamiec, M. Więcek, G. Kokot, Przegląd Spawalnictwa 5, 3-9 (2014).
• [2] J. Adamiec, B. Piliszko, Inżynieria Materiałowa 6, 907-913 (2007).
• [3] A. Hernas, B. Kościelniak, J. Hajda, Mikrostruktura i właściwości złączy spawanych z nadstopu niklu Inconel 740H po starzeniu w 750°C, w: Charakterystyki nowej generacji materiałów dla energetyki, pod red. A. Hernasa, Bełchatów 175-176, 2015.
• [4] J. Dobrzański, Materiałoznawcza interpretacja trwałości stali dla energetyki, Open Access Library 3, 2011.
• [5] M. Drop, E. Włoczyk, Materiały stosowane na urządzenia energetyczne. Teraźniejszość i przyszłość. Dozór techniczny 1, 9-15 (2006).
• [6] P. M. Scott, An overview of materials degradation by stress corrosion in PWRs, in: D. Feron, J.M. Olive (Eds.), Corrosion Issues in Light Water Reactors: Stress Corrosion Cracking, Woodhead, England 3-24, (2007).
• [7] T. Fujii, K. Sue, S.I. Kawasaki, The Journal of Supercritical Fluids 95, 285-291(2014)
• [8] P. Berge, Stress Corrosion Cracking of Nickel Based Alloys in Water-cooled Nuclear Reactors 143-146, (2016).
• [9] J. Łabanowski, A. Świerczyńska, J. Michalska, Solid State Phenomena 227, 267-270 (2015).
• [10] J. Michalska, J. Łabanowski, J. Ćwiek, Materials Science and Engineering IOP Conference Series 35, 012012 (2012) (doi.org/10.1088/1757-899X/35/1/012012)
• [11] H. T. Lee, J. L. Wu, Corrosion Science 51, 733-743 (2009).
• [12] J. Brózda, G. Czaja, Żarowytrzymała stal T92/P92, jej spawanie i własności złączy spawanych, Przegląd Spawalnictwa 4, 51-61 (2014).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).