The method of production of thin-walled castings made of GX2CrNiMoN25-6-3 cast steel

• Autorzy: Nadolski M. , Stradomski G. , Zyska A.

Warianty tytułu

PL

Sposób wykonywania cienkościennych odlewów ze staliwa GX2CrNiMoN25-6-3

• Języki publikacji: EN

Abstrakty

EN

The possibility of production of thin-walled castings made of GX2CrNiMoN25-6-3 cast steel was assessed for the exemplary final casting with variable wall thickness. The assessment both of the solidification process of the GX2CrNiMoN25-6-3 alloy and of the final degree of mould cavity filling was done by means of the NovaFlow&Solid program. The body of the casting with its variable wall thickness, including sections thinner than 1 mm, demanded for the appropriate production technology. There are presented the results of technological tests with respect to the application of the centrifugal casting, which confirm the adopted technology of pattern and mould production. The analyzed technology makes possible the production of casting of high surface quality, while simultaneously the yield is increased, and by the same the unit cost of production is lower as compared with the production method used thus far.

PL

W pracy ocenie poddano możliwość wykonania cienkościennych odlewów ze staliwa GX2CrNiMoCuN25-6-3 na przykładzie docelowego odlewu o zmiennej grubości ścianki. Wykonano ocenę wypełniania i krzepnięcia stopu GX2CrNiMoN25-6-3 na podstawie symulacji komputerowej wykonanej przy użyciu programu NovaFlow&Solid. Bryła odlewu o zmiennej grubości ścianki, w tym nawet poniżej jednego 1 mm, wymogła zastosowanie odpowiedniej technologii wykonania. Przedstawiono wyniki prób technologicznych odlewania odśrodkowego, potwierdzające przyjętą technologię modelu i formy. W porównaniu do dotychczas stosowanej metody wykonania, analizowana technologia umożliwia wykonywanie odlewów o wysokiej jakości powierzchni przy jednoczesnym zwiększeniu uzysku i tym samym obniżając koszty wykonania jednostkowego odlewu.

Słowa kluczowe

EN

numerical modelling; centrifugal casting; duplex cast steel

• Wydawca: Wydawnictwa AGH
• Czasopismo: Computer Methods in Materials Science
• Rocznik: 2016
• Tom: Vol. 16, No. 2
• Strony: 104--109
• Opis fizyczny: Bibliogr. 18 poz., rys.

Twórcy

autor

Nadolski M.

• Technical University of Czestochowa, Faculty of Production Engineering and Materials Technology, al. Armii Krajowej 19, 42-201 Czestochowa, Poland

autor

Stradomski G.

• Technical University of Czestochowa, Faculty of Production Engineering and Materials Technology, al. Armii Krajowej 19, 42-201 Czestochowa, Poland

autor

Zyska A.

• Technical University of Czestochowa, Faculty of Production Engineering and Materials Technology, al. Armii Krajowej 19, 42-201 Czestochowa, Poland

Bibliografia

• Cassagne, T., Busschaert, F., 2007, Experience with duplex stainless steels in oil and gas production, Duplex Conference, Stainless Steel World, Grado.
• Charles, J., 2008, Duplex stainless steels, a review after DSS '07 held in Grado, Revue de Métallurgie, 105, 155-171.
• Dyja, D., Stradomski, Z., 2006, Solidification model of highly alloyed FE-Cr-Ni cast steels, Archives of Foundry, 6, 81-88.
• Dyja, D., Stradomski, Z., Kolan, C., Stradomski, G., 2012,Eutectoid decomposition of δ-ferrite in ferritic-austeniticduplex cast steel – structural and morphological study, Thermec, Materials Science Forum, 706-709, 2314-2319.
• Gołowin, S.J., 1963, Special methods of casting, WNT Warszawa (in Polish).
• Górny, Z., 1966, Cast in rotating molds, WNT, Warszawa (in Polish).
• Marken, L., 2005, Application of duplex and super duplex stainless steels in the offshore industry- Case histories, Stainless Steel World Conference & Expo, Maastricht, 318-323.
• Nadolski, M., Golański, G., Klimas, J., Szota, M., Szymański,J., 2015, Microstructure and functional properties of prosthetic cobalt alloys CoCrW, Archives of Metallurgy and Materials, 60, 1999-2003.
• Nowacki, J., 2013, Duplex steel in welded structures, WNT, Warszawa (in Polish)
• Olsson, J., Malin, S., 2007, Duplex – A new generation of stainless steels for desalination plants, Desalination, 205, 104-113.
• Pilarska, M., Nadolski, M., 2015, The Assessment of the Microstructure of CuZn39Pb2 Alloy Made by Centrifugal Casting. XXXIX Studencka Konferencja Naukowa Innowacje w Inżynierii Produkcji, Technologii Materiałów i Bezpieczeństwie, (in Polish).
• Shargay, C., 2005, Application of duplex stainless steels in refining, Stainless Steel World, 17, 19-27.
• Stradomski, G., 2014, The role of carbon in the mechanism of ferritic-austenitic cast steel solidification, Archives of Foundry Engineering, 14, 83-86.
• Stradomski, G., Nadolski, M., Stradomski, Z., 2015a, The Microstructure of thin-walled GX2CrNiMoN25-6-3 cast steel made by centrifugal casting, Archives of Foundry Engineering, 15, 77-82.
• Stradomski, G., Nadolski, M., Stradomski, Z., 2015b, Technological assessment of the possibility of making lightsection castings of GX2CrNiMoN25-6-3 cast steel by the centrifugal casting method, Archives of Foundry Engineering, 15, 57-60.
• Stradomski, G., Soiński, M.S., Nowak, K., Szarek, A., 2012, The assessment of tendency to develop hot cracks in the duplex casts, Steel Research International, Spec. Edition Conf. Metal Forming, 1231-1234.
• Stradomski, Z., 2010, The microstructure in problems of wearresistant steel castings, Technical University of Czestochowa (in Polish).
• Stradomski, Z., Soiński, M.S., Stradomski, G., 2010, The assessment of hot cracking susceptibility of ferriticaustenitic cast iron, Archives of Foundry Engineering, 10, 159-162.

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).