Porównanie struktury i właściwości włókien wełnianych i kaszmirowych po obróbce nadmanganianem potasu
Języki publikacji
Abstrakty
In this study, the weight loss and tensile property of wool fibers and cashmere fibers before and after various potassium permanganate solution treatment were investigated. The scale morphology andcrystallization index of the original and treated fibers were analysed with scanning electron microscopy and X-ray diffraction analysis. The experimental results showed that the weight loss of wool fibers is more than that of cashmere fibers under low potassium permanganate content treatment, but is less than that of cashmere fibers under high potassium permanganate content treatment. The force loss of cashmere fibers increased linearly with an increase in potassium permanganate content. The scales of cashmere fiber were damaged at a potassium permanganate content of 9%, but the scales of wool fiber were clear. The relative crystallisation index of treated wool is twice as that of treated cashmere at a potassium permanganate content of 9%.
W pracy zbadano utratę masy i wytrzymałość na rozciąganie włókien wełnianych i kaszmirowych przed i po zastosowaniu różnych roztworów nadmanganianu potasu. Morfologię i wskaźnik krystalizacji pierwotnych i poddanych obróbce włókien analizowano za pomocą skaningowej mikroskopii elektronowej i dyfrakcji rentgenowskiej. Wyniki eksperymentalne wykazały, że ubytek masy włókien wełnianych jest większy, niż w przypadku włókien kaszmirowych po zastosowaniu obróbki nadmanganianem potasu. Utrata wytrzymałości włókien kaszmirowych wzrastała liniowo wraz ze wzrostem zawartości nadmanganianu potasu. Stwierdzono, że względny wskaźnik krystalizacji wełny poddanej obróbce jest dwukrotnie większy, niż w przypadku kaszmiru poddanego obróbce przy zawartości nadmanganianu potasu wynoszącej 9%.
Czasopismo
Rocznik
Strony
29--33
Opis fizyczny
Bibliogr. 10 poz., rys., tab.
Twórcy
autor
- Xi’an Polytechnic University,School of Textile & Materials, China
autor
- Xi’an Polytechnic University,School of Textile & Materials, China
autor
- Xi’an Polytechnic University,School of Textile & Materials, China
Bibliografia
- 1. Shi X J, Yu W D, Yuan Z H. An identification method for cashmere and fine wool based on Bayes model. Journal of Textile Research 2008; 29: 26-33.
- 2. Yu W D, Chu C Y. Textile Physics. Donghua University Press, Shanghai, China, 2002, p.22.
- 3. João C, Bonner P L R, Martin G. Application of transglutaminases in the modification of wooltextile. Enzyme and Microbial Technology 2004; 34:64-72.
- 4. Lewis D M. Ancillary Processes in Wool Dyeing. Wool Dyeing Society of Dyers & Colourists, Bradford, 1992, p.111
- 5. Wang Y., Yu W D. Surface characterization of low temperature plasma-induced cashmere fibre byair gas.FIBRES & TEXTILE in Eastern Europe 2017; 25, 5(125): 37-41.
- 6. Zhang H Y. Wool fibers shrink-proof treatment using potassium permanganate. Textile Dyeing andFinishing Journal 1996;18(6):25-26.
- 7. Chen L, Liu Y S. Wang Y. Impact of different shrink-proof methods on wool properties. Journal of Textile Research 2010; 31(8):21-23.
- 8. Li L, Jiang F, Jia G. Q, Wang W. Anti-felting oxidation treatment of cashmere fiber. Journal of Engineered Fibers and Fabrics 2012; 7: 111-117.
- 9. Zhang H Y. Wool modification using potassium permanganate. Wool Textile Journal, 1996; 24（6）: 41-44.
- 10. Li L, Li H Y. Cashmere Processing Technology. Donghua University Press, Shanghai, China, 2004, p21.
Uwagi
PL
Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-ba954665-e7c0-47af-90c7-63e0a118b18a
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.