Use of zeolite dust in lime mortars

• Autorzy: Pavlik V. , Uzakova M.

Warianty tytułu

PL

Wykorzystanie pyłu zeolitowego w zaprawach wapiennych

• Języki publikacji: EN

Abstrakty

EN

Fine grained waste zeolite in the form of a zeolite dust or a finely ground zeolite can be used as an active pozzolanic admixture to lime mortars. Lime mortars containing various content of fine grained zeolite were prepared and tested. Development of compressive strength, shrinkage and weight loss of lime mortars stored in different conditions was then evaluated. X ray powder diffraction of lime-zeolite pastes was also used to evaluate lime-pozzolan reaction. The results confirmed that fine grained zeolite can be usefully used as pozzolanic addition to lime mortars. Positive effect of pozzolan on the compressive strength of mortars is effective when mortars are stored in humid atmosphere where favorable conditions for lime-pozzolan reaction are. However, compressive strength of mortars stored in open air at RH 65% cannot fully develop and after some time it even decreases.

PL

Drobnoziarnisty zeolit odpadowy w formie pyłu zeolitowego lub proszku zeolitowego może zostać użyty jako pucolanowa domieszka do zapraw wapiennych. Zaprawy wapienne zawierające różne ilości drobnoziarnistego zeolitu zostały przygotowane i przetestowane. Następnie określono wytrzymałość na ściskanie, kurczenie się oraz utrata masy zaprawy wapiennej składowanej w różnych warunkach. Widmo rentgenowskie proszkowe zostało również zastosowane w celu oznaczenia reakcji wapno-pucolana. Wyniki potwierdziły, że drobnoziarnisty zeolit może być z powodzeniem użyty jako pucolanowy dodatek do zaprawy wapiennej. Pozytywny efekt pucolanu na wytrzymałość na ściskanie jest skuteczny gdy zaprawa jest składowana w wilgotnej atmosferze gdzie występują dogodne warunki dla reakcji wapno-pucolana. Jednakże, wytrzymałość na ściskanie zaprawy wapiennej przetrzymywanej na otwartym powietrzu o wilgotności względnej 65% nie może się w pełni rozwinąć i po pewnym czasie wytrzymałość ta nawet maleje.

Słowa kluczowe

EN

lime; zeolite; paste; mortar; compressive strength; relative humidity; carbonation

PL

wapno; zeolit; zaprawa; naprężenia; wilgotność względna; uwęglenie

• Wydawca: Polskie Towarzystwo Przeróbki Kopalin
• Czasopismo: Inżynieria Mineralna
• Rocznik: 2013
• Tom: R. 14, nr 2
• Strony: 31--36
• Opis fizyczny: Bibliogr. 7 poz., rys., wykr., tab.

Twórcy

autor

Pavlik V.

• Department of Material Engineering, Faculty of Civil Engineering, STU – Slovak University of Technology in Bratislava; Radlinského 11, 813 68 Bratislava, Slovak Republic

autor

Uzakova M.

• Faculty of Civil Engineering, STU – Slovak University of Technology in Bratislava

Bibliografia

• 1. Feng N.-Q., Peng G.-F.: Applications of natural zeolite to construction and building materials in China. Construction and Building Materials 19, 2005, p. 579–584.
• 2. Cizer O.: Competition between carbonation and hydration on the hardening of calcium hydroxide and calcium silicate binders. PhD dissertation, K.U. Leuven, 2009.
• 3. Cizer O., Van Balen K., Van Gemert D.: Competition between hydration and carbonation in hydraulic lime and lime-pozzolana mortars. Advanced Materials Research, 133-134, 2010, p. 241-246.
• 4. Jana D.: Clinoptilolite – a promising pozzolan in concrete. Proceedings of the Twenty-Ninth Annual International Conference on Cement Microscopy, May 21- 24, 2007, Quebec City, Quebec, Canada.
• 5. Makýš O. a kolektív autorov: Ochrana zrúcanín v kultúrnej krajine. Združenie na záchranu Lietavského hradu, Lietava 2006. ISBN 80-969477-0-2.
• 6. Maravelaki-Kalaitzaki P., Bakolas A., Moropoulou A.: Physico-chemical study of Cretan ancient mortars. Cem. Concr. Res. 33, 2003. p. 651-661.
• 7. Mertens G., Snellings R., Van Balen, Bicer-Simsir K., Verlooy P., Elsen J.: Pozzolanic reactions of common natural zeolites with lime and parameters affecting their reactivity. Cement and Concrete Research 39, 2009, p. 233–240.