High durability coatings with advanced TiO₂ technology

• Autorzy: Pajunen E. , Lammanmäki R.

Warianty tytułu

PL

Powłoki o wysokiej trwałości przy zastosowaniu zaawansowanej technologii TiO₂

• Języki publikacji: EN PL

Abstrakty

EN

Sachtleben has a long experience to produce titanium dioxide pigments for demanding high performance exterior coatings. Classical approach to control durability of TiO₂ is to use inorganic surface treatment to cover titanium dioxide primary particles. The surface of TiO₂ is isolated to prevent photoactive reactions to occur. However, the basis of high durability is built up on the primary titanium dioxide particles. Future development to obtain advanced durability of titanium dioxide crystal lattice will be introduced. This advance in weather durability opens new sights to modify TiO₂ surfaces to tailor products for demanding coating applications. The progress is supported by a new versatile method to measure weather durability and photoactivity performance of TiO₂.

PL

Firma Sachtleben to producent TiO₂ z dużym doświadczeniem, wytwarzający ditlenek tytanu stosowany w wysokojakościowych wyrobach lakierowych zewnętrznych. Klasycznym podejściem do kontrolowania trwałości TiO₂ jest zastosowanie obróbki powierzchni związkami nieorganicznymi i pokrycie nimi cząsteczek ditlenku tytanu. W metodzie tej zwiększenie trwałości pigmentu uzyskuje się przez „dobudowanie” warstwy na powierzchni cząstek TiO₂. W artykule omówiono badania, które pozwalają na zwiększenie trwałości pigmentu poprzez zmiany w strukturze krystalicznej. Ten sposób zwiększenia odporności na warunki atmosferyczne otwiera nowe możliwości modyfikacji TiO₂ i jeszcze lepszego dopasowania jego właściwości do potrzeb wyrobów lakierowych. Oprócz nowej metody modyfikacji omówiono nową uniwersalną metodę pomiaru odporności na warunki atmosferyczne i fotoaktwności ditlenku tytanu.

Słowa kluczowe

EN

coating; high durability coating

PL

powłoka; powłoka o wysokiej trwałości

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Inżynierii Materiałów Polimerowych i Barwników
• Czasopismo: Farby i Lakiery
• Rocznik: 2011
• Tom: nr 2
• Strony: 7--22
• Opis fizyczny: Bibliogr. 8 poz., rys.

Twórcy

autor

Pajunen E.

• Sachtleben Pigments Oy, FIN-28840 Pori, Finland

autor

Lammanmäki R.

• Sachtleben Pigments Oy, FIN-28840 Pori, Finland

Bibliografia

• [1] W. Hughes, Photodegradation of Paint Films containing Titanium Dioxide Pigments, X Fatipec Congress, Montreaux, Switzerland (1970) 67-82.
• [2] Hans G. Völz, Guenther Kaempf, Hans Georg Fitzky, Aloys Klaeren, The Chemical Nature of Chalking in the Presence of Titanium Dioxide Pigments, ACS Symp. Ser. No. 151 (1981), p. 163-182.
• [3] Miia Salmi, Nikolai Tkachenko, Ralf-Johan Lamminmäki, Saila Karvinen,Visa Vehmanen, Helge Lemmetyinen, Femtosecond to nanosecond spectroscopy of transition metal-doped TiO2 particles, Journal of Photochemistry and Photobiology A: Chemistry 175 (2005) 8-14.
• [4] Juho-Pertti Jalava, Formation of TiO2 Pigment Particles in the Sulphate Process – A Methodological Study, PhD thesis, University of Turku, Finland, 2000, ISBN 952-91-2551-8.
• [5] Ulrich Gesenhues and Thomas Rentschler, Crystal Growth and Defect Structure of Al3+-Doped Rutile, Journal of Solid State Chemistry, 143 (1999) 210-218.
• [6] Novotnak, George. Applications of solid state Al-27 and Si-29 nuclear magnetic resonance (NMR) of surface treated TiO2 pigments. (1995) Unpublished results.
• [7] Ulrich Gesenhues, Calcination of Metatitanic Acid to Titanium Dioxide White Pigments, Chem. Eng. Technol. 24 (2001) 7, 685-694.
• [8] Leena-Sisko Johansson, Tuomo Losoi, Surface Characterization of Coated Powders: Al2O3-SiO2-coated TiO2, Surface and Interface Analysis, 17 (1991) 230-236