An inoculation phenomenon in cast iron

• Autorzy: Fraś E. , Górny M.

Warianty tytułu

PL

Zagadnienie modyfikacji żeliwa

• Języki publikacji: EN

Abstrakty

EN

The paper presents a solidification sequence of graphite eutectic cells of A and D types, as well as globular and cementite eutectics. The morphology of eutectic cells in cast iron, the equations for their growth and the distances between the graphite precipitations in A and D eutectic types were analysed. We observed a critical eutectic growth rate at which one type of eutectic transformed into another. A mathematical formula was derived that combined the maximum degree of undercooling, the cooling rate of cast iron, eutectic cell count and the eutectic growth rate. One type of eutectic structure turned smoothly into the other at a particular transition rate, transformation temperature and transformational eutectic cell count. Inoculation of cast iron increased the number of eutectic cells with flake graphite and the graphite nodule count in ductile iron, while reducing the undercooling. An increase in intensity of inoculation caused a smooth transition from a cementite eutectic structure to a mixture of cementite and D type eutectic structure, then to a mixture of D and A types of eutectics up to the presence of only the A type of eutectic structure. Moreover, the mechanism of modification of cast iron was studied.

PL

W pracy podano sekwencję krystalizacji ziaren eutektyki grafitowej typu A i D oraz kulkowej a także eutektyki cementytowej. Przeanalizowano morfologię tych ziaren w żeliwie oraz równania na prędkość wzrostu ziaren oraz odległość miedzy wydzieleniami grafitu typu A i D. Wykazano, że istnieją krytyczne prędkości wzrostu eutektyki, przy których jeden rodzaj eutektyki przekształca sie w drugi. Wyprowadzono ogólne równanie wiążące stopień przechłodzenia eutektyk z szybkością stygnięcia żeliwa, liczba ziaren eutektycznych i prędkością ich wzrostu. Wykazano, że istnieje prędkość transformacji, temperatura transformacji i transformacyjna liczba ziaren, przy których jeden rodzaj eutektyki przechodzi płynnie w drugi. Modyfikacja żeliwa zwiększa liczbę ziaren eutektycznych w żeliwie z grafitem płatkowym i liczbę kulek grafitu w żeliwie sferoidalnym oraz zmniejsza przechłodzenie. Powiększenie intensywności modyfikacji powoduje płynne przejście od eutektyki cementytowej poprzez mieszaniny eutektyk typu D i cementytowej, eutektyk typu D i A aż do wyłącznie eutektyki typu A. Podano mechanizm modyfikacji żeliwa.

Słowa kluczowe

EN

cast iron; solidification; inoculation; structure; eutectic cells

PL

ziarna eutektyki; modyfikacja żeliwa; żeliwo sferoidalne

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2012
• Tom: Vol. 57, iss. 3
• Strony: 768--777
• Opis fizyczny: Bibliogr. 15 poz., rys., tab., wykr.

Twórcy

autor

Fraś E.

autor

Górny M.

• AGH University of Science and Technology, Faculty of Foundry Engineering, 30-059 Kraków, 30 Mickiewicza av., Poland

Bibliografia

• [1] T. Turner, The Metallurgy of Cast iron. Griffin Co.Ltd. London, 1920.
• [2] A. Meehan, US Patent 1 499 068 (1924).
• [3] E. Fras, C. Podrzucki, Zeliwo modyfikowanwe, Skrypt AGH, nr. 675, Kraków 1978.
• [4] E. Fras, Krystalizacja metali WNT, Warszawa 2003.
• [5] J. Park, J. Verhoven, Transitions between type A flake, type D flake and coral graphite eutectic structures in cast iron, Metallurgical and Materials Transactions A 27A, 2740-2753 (1996).
• [6] E. Fras, M. Górny, H. Lopez, The Transition from gray to white iron during solidification, part I – theoretical background, Metallurgical and Materials Transactions A, 2005, vol. 36A, p.3075-3082,
• [7] G. Ohira, T. Sato, Y. Sayama, Eutectic growth unidierectionally solidified iron-carbon alloys, Georgi Publishing Company, St.Shaporin, Switzeland 296-313 (1974).
• [8] W.S. Wołczynski, Lamella/Rod Transformation as described by the Criterion of Minimum Entropy Production, International Journal of Thermodynamics 13, 2, 35-42 (2010).
• [9] P. Magnin, W. Kurz, Competitive growth of stable and metastable FE-C-X eutectics: Part II. Mechanism, Metallurgical Transactions A 19A, 1965-1971 (1988).
• [10] E. Fras, H. López, Eutectic cells and nodule count – an index of molten iron quality, International Journal of Metalcasting, Summer, 35-61 (2010).
• [11] E. Fras, M. Górny, H. Lopez, Eutectic cell, chilling tendency and chill in flake graphite cast iron, part I – theoretical analysis, Transactions of American Foundry Society 115, 435-451 (2007).
• [12] E. Fras, M. Górny, H. Lopez, Eutectic cell, chilling tendency and chill in flake graphite cast iron, part III – thermal analysis, Transactions of American Foundry Society 115, 476-480 (2007).
• [13] E. Fras, H. Lopez, Generation of internal pressure during solidification of eutectic cast iron. AFS Transactions 102, 597-601 (1994).
• [14] B. Lux, Nucleation and graphite In Fe-C-Si alloys In Recent Research on Cast iron, Gordon and Breach, New York 1968, p. 241.
• [15] E. Fras, H. Lopez, C. Podrzucki, The influence of oxygen on the inoculation process of cast iron, Journal Cast Metal Research 13, 107-121 (2000).