Influence of notch (TIP) radius on fatigue crack growth rate

• Autorzy: Rozumek D. , Macha A. , Lazzarin P. , Meneghetti G.

Warianty tytułu

PL

Wpływ promienia (wierzchołka) karbu na prędkość wzrostu pęknięć zmęczeniowych

• Języki publikacji: EN

Abstrakty

EN

The paper deals with the problem of fatigue crack propagation from notches in plates made of FeP04 steel and AA356-T6 aluminium alloy. The tests were performed under different stress ranges by keeping the nominal load ratio (R=0.1) constant. The specimens were weakened by nearly sharp and blunt two sided notches. The results of the fatigue tests were then reanalysed in terms of the J-integral range including influence of the notch. It was observed that the blunter notches are, the higher fatigue crack growth rate is.

PL

W pracy przedstawiono propagację pęknięć zmęczeniowych, w próbkach płaskich z karbami, wykonanych ze stali FeP04 i stopu aluminium AA356- T6. Badania wykonywano przy różnych zakresach naprężeń i stałym współczynniku asymetrii cyklu (R = 0.1). Próbki były osłabione przez dwustronne ostre i łagodne karby. Wyniki badail zmęczeniowych opisano za pomocą zakresu całki J z uwzględnieniem wpływu karbu. Stwierdzono, że im łagodniejszy karb, tym większa prędkość wzrostu pęknięć zmęczeniowych.

Słowa kluczowe

EN

fatigue crack growth; J-integral range; load ratio; notch

PL

zakres integralny; stosunek ładunku; karby

• Wydawca: Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej
• Czasopismo: Journal of Theoretical and Applied Mechanics
• Rocznik: 2006
• Tom: Vol. 44 nr 1
• Strony: 127--137
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Rozumek D.

autor

Macha A.

autor

Lazzarin P.

autor

Meneghetti G.

• Faculty of Mechanical Engineering, Technical University of Opole, Poland,

Bibliografia

• 1. Atzori B., Lazzarin P., Meneghetti G., 2003, Fracture mechanics and notch sensitivity, Fatigue and Fracture of Engineering Materials and Structures, 26, 257-267
• 2. Dowling N.E., Begley J.A., 1976, Fatigue crack growth during gross plasticity and the J-integral, In: Mechanics of Crack Growth, ASTM STP 590, American Society for Testing and Materials, 82-103
• 3. El Haddad M.H., Dowling N.E., Topper T.H., Smith K.N., 1980, J-integral applications for short fatigue cracks at notches, International Journal of Fracture, 16, 15-30
• 4. El Haddad M.H., Topper T.H., Smith K.N., 1979, Prediction of nonpropagating cracks, Engineering Fracture Mechanics, 11, 573-584
• 5. Jiang Y., Feng M., 2004, Modelling of fatigue crack propagation, Journal of Engineering Materials and Technology, 126, 77-86
• 6. Lazzarin P., Tovo R., Meneghetti G., 1997, Fatigue crack initiation and propagation phases near notches in metals with low notch sensitivity, International Journal of Fatigue, 19, 647-657
• 7. Macha E., Rozumek D., 2003, Fatigue crack path development in a onesided restrained bar with a rectangular section and stress concentrator under bending, Proc. Int. Conference on Fatigue Crack Paths (FCP 2003), Parma, CD-ROM, 8 ps
• 8. Ogura K., Miyoshi Y., Nishikawa I., 1987, Fatigue crack growth and closure of small cracks at the notch root, Current Research on Fatigue Cracks, Ed. Tanaka T. et al., Elsevier Applied Science, London and New York, 1, 67-91
• 9. Rice J.R., 1968, A path independent integral and the approximate analysis of strain concentration by notches and cracks, Journal of Applied Mechanics, 35, 379-386
• 10. Rozumek D., 2004, The ΔJ-integral range applied for the description of fatigue crack growth rate, Proc. 12th Int. Conference on Experimental Mechanics (ICEM12), Bari, 275-276 and CD-ROM, 8 ps