Influence of the mean loading on fatigue crack growth rate and life under bending

• Autorzy: Rozumek D.

Warianty tytułu

PL

Wpływ obciążenia średniego na prędkość wzrostu pękania zmęczeniowego i trwałość przy zginaniu

• Języki publikacji: EN

Abstrakty

EN

The paper contains the results of experimental tests of the fatigue crack growth rate of steels 10HNAP and 18G2A under bending for different load ratios. In the tests, plane specimens with external unilateral sharp notches as stress concentrators were used. The results of the experimental tests are described by a nonlinear formula based on the ...J-integral range. The proposed formula for description of the fatigue crack growth rate, including the ...J-integral range, satisfactorily describes the results obtained experimentally.

PL

W pracy przedstawiono wyniki badań doświadczalnych wzrostu prędkości pęknięć zmęczeniowych przy zginaniu w stalach 10HNAP i 18G2A dla różnych wartości współczynnika asymetrii cyklu R. Do badań użyto próbek płaskich z koncentratorem naprężeń w postaci zewnętrznego jednostronnego karbu ostrego. Wyniki badań doświadczalnych opisano nieliniowym związkiem zawierającym zakres całki ...J. Zaproponowany związek do opisu prędkości rozwoju pęknięcia zmęczeniowego, zawierający zakres całki ...J, w sposób zadowalający opisuje wyniki uzyskane doświadczalnie.

Słowa kluczowe

EN

fatigue crack growth; integral range; number of cycles; load ratio

• Wydawca: Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej
• Czasopismo: Journal of Theoretical and Applied Mechanics
• Rocznik: 2004
• Tom: Vol. 42 nr 1
• Strony: 83--93
• Opis fizyczny: Bibliogr. 12 poz., rys., tab.

Twórcy

autor

Rozumek D.

• Faculty of Mechanical and Engineering, Technical University of Opole

Bibliografia

• 1. Achtelik H., Jamroz L., 1982, Patent PRL No. 112497, CSR No. 200236, HDR No. 136544, Warsaw (in Polish)
• 2. ASTM E813-89, 1989, Standard test method for JIc, a measure of fracture toughness, American Society for Testing and Materials, Philadelphia
• 3. Dowling N.E., Begley J.A., 1976, Fatigue crack growth during gross plasticity and the J-integral, American Society for Testing and Materials, ASTM STP 590, 82-103
• 4. Gasiak G., Rozumek D., 2001, Fatigue crack propagation in notched specimens under bending with the influence of mean stress, Materials Technology, 2, 108-112 (in Polish)
• 5. Kocańda S., Szala J., 1997, Basics of Fatigue Calculations, PWN, Warsaw (in Polish)
• 6. Macha E., Pawliczek R., Rozumek D., 2000, Fatigue tests of smooth and notched specimens under combined bending and torsion with influence of mean stress, Materials Technology, 2, 79-85 (in Polish)
• 7. Neimitz A., 1998, Fracture Mechancis, PWN, Warsaw (in Polish)
• 8. Pickard A.C., 1986, The application of 3-dimensional finite element methods to fracture mechanics and fatigue life prediction, London
• 9. Rice J.R., 1968, A path independent integral and the approximate analysis of strain concentration by notches and cracks, Journal of Applied Mechanics, 35, 379-386
• 10. Rozumek D., 2002, Investigation of the influence of specimen geometry, concentrator type and kind of the material on fatigue life under cyclic bending, Doctoral Thesis, Technical University of Opole (in Polish)
• 11. Tanaka K., 1983, The cyclic J-integral as a criterion for fatigue crack growth, Int. J. Fracture, 22, 91-104
• 12. Thum A., Petersen C., Swenson O., 1960, Verformung, Spannung und Kerbwirkung, VDI, Duesseldorf