The microstructure and mechanical properties of Ni78Ag2P20 alloy

Wybrane pełne teksty z tego czasopisma
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Purpose: The aim of the work was to investigate the influence of silver as a modifying constituent on structure formation in Ni-P based glass forming matrix and to characterize mechanical properties of the alloys. Design/methodology/approach: Nickel-silver-phosphorus Ni78Ag2P20 alloy was produced using arc melting in argon protective atmosphere from commercial powders. The alloy was melt spun. The microstructure of the arc melted droplet is investigated in scanning electron microscope with EDS and micro-hardness tester and the melt spun ribbon is investigated using light microscope and transmission electron microscope. Then the mechanical properties are evaluated with use of micro-hardness measurements. Findings: A strong tendency for demixing of Ni-P-rich and Ag-rich liquids is observed leading to formation of the primary structure consisting of slightly hypo-eutectic Ni-P-rich regions and Ag rich regions. The melt spinning process produced the amorphous Ni-P and Ag-rich crystalline structure. The alloys hardness and elasticity modulus were characterized. The melt spun ribbons are slightly softer than the crystalline Ni-P regions. In case of the melt spun ribbons, a softening influence of silver was observed giving the lower hardness for Ni78Ag2P20 than Ni80P20. The alloy constituents in a bulk crystalline state present the higher values of elasticity modulus when compared to the melt spun ribbons. Research limitations/implications: It has been shown that the criterion of a high positive values of mixing enthalpies can be applied to design the materials that should separate before the solidification to form a hard glassy matrix/soft crystalline composite. The amorphization of the crystalline Ni-P-based alloys can lead to formation of more flexible materials with a lower elasticity modulus and lower hardness. Practical implications: The main limits for application of the glassy alloys are the high prices of the materials used for alloying and the low plasticity of the amorphous metals. Therefore, the work provides the alloy produced from a low-cost commercial purity precursors that are able to form a glassy matrix composite with a crystalline soft particles included. The future works on the development of the idea can lead to a successful manufacturing of a hard and ductile metallic composite parts. Originality/value: The work delivers a new information on possibility of amorphous/crystalline composite formation starting from Ni Ag P system. This includes the original microstructural and mechanical characteristics of the arc melt and melt spun alloy. The information could be used by researchers for future works on development of Ni-P based composites complementary to the electroless coatings.
Rocznik
Strony
657--660
Opis fizyczny
Bibliogr. 20 poz., il., wykr.
Twórcy
autor
autor
autor
Bibliografia
  • [1] A. Inoue, Materials Science and Engineering A, Stabilization and High Strain-Rate Superplasticity of Metallic Supercooled Liquid 267 (1999) 171-183.
  • [2] T. Zhang, A. Inoue, Thermal and Mechanical Properties of Ti-Ni-Cu-Sn Amorphous Alloys with a Wide Supercooled Liquid Region before Crystallinzation, Materials Transactions JIM 39 (1998) 1001-1006.
  • [3] W. Zhang, A. Inoue, Formation and mechanical properties of Ni-based Ni-Nb-Ti-Hf bulk glassy alloys, Scripta Materialia 48 (2003) 641-645.
  • [4] A. Inoue, B. L. Shen, C. T. Chang, Super-High Strength of over 4000 MPa for Fe-based Bulk Glassy Alloys in [(Fe1-xCox)0.75B0.2Si0.05]96Nb4 System, Acta Materialia 52 (2004) 4093-4099.
  • [5] B. Kostrubiec, R. Wiśniewski, J. Rasek, Crystallisation kinetics and magnetic properties of a Co-based amorphous alloy, Journal of Achievements in Materials and Manufacturing Engineering, 16, 2006, 30-34.
  • [6] S. Lesz, D. Szewieczek, J. E. Frąckowiak, Structure and magnetic properties of amorphous and nanocrystalline Fe85.4Hf1.4B13.2 alloy, Journal of Achievements in Materials and Manufacturing Engineering 19/2 (2006) 29-34.
  • [7] C. C. Hays, C. P. Kim, W. L. Johnson, Microstructure Controlled Shear Band Pattern Formation and Enhanced Plasticity of Bulk Metallic Glasses Containing in situ Formed Ductile Phase Dendrite Dispersion, Physical Review Letters, 84/13 (2000) 2901-2904.
  • [8] W. Kühn, J. Eckert, N. Mattern, L. Schultz, ZrNbCuNiAl bulk metallic glass matrix composites containing dendritic bcc phase precipitates, Applied Physics Letters 80 (2002) 2478-2490.
  • [9] K. Ziewiec, P. Kurtyka, Determination of the Thermal and Mechanical Properties of Ni63Cu9Fe8P20 alloy, Archives of Metallurgy and Materials 51 (2006) 217-220.
  • [10] K. Ziewiec, P. Kurtyka, K. Bryła, S. Kąc, Thermal Stability and Behaviour during Compression of the Cu68.5Ni12P19.5 Alloy, Archives of Metallurgy and Materials 52 (2007) 73-76.
  • [11] F. R. Boer, R. Boom, W. C. M. Mattens, A. R. Miedema, A. K. Niessen, Cohesion and structure, Cohesion in metals, vol. 1, Amsterdam; Elsevier Science; 1988; ISBN 0-444-87098-9; 291-322.
  • [12] T. B. Massalski, H. Okamoto, P. R. Subramanian, L. Kacprzak, Binary phase diagrams, 2nd ed. Metals Park, OH, ASM International 1992.
  • [13] A. Bai, C.-C. Hu, Influences of the Phosphorus Content on Physicochemical Properties of Nickel-Phosphorus Deposits, Materials Chemistry and Physics 79 (2003) 49-57.
  • [14] C. Shou-Yi, L. Yu-Shuien, H. Hsiang-Long, C. Ting-Kui, Mechanical Propeties and Deformation Behavior of Amorphous Nickel-Phosphorus Films Measured by Nanoindentation Test, Metallurgical and Materials Transactions A 37A (2006) 2939-2945.
  • [15] I. Apachietei, J. Duszczyk, L. Katgerman and P. J. B. Overkamp, Electroless Ni-P Composite Coatings The Effect of Heat Treatement on The Microhardness of Substrate and Coating, Scripta Materialia 38 (1998) 1347-1353.
  • [16] K. Hari Krishnan, S. John, K. N. Srinivasan, J. Praveen, M. Ganesan and P. M. Kavimani, An Overall Aspects of Ni-P Depositions-A Review Article, Metallurgical and Materials Transactions A 37A (2006) 1917-1926.
  • [17] C.-C. Hu, A. Bay, Surface Coating Technology, Influences of The Phosphorus Content on Physicochemical Properties of Nickel-Phosphorus Deposits, 137 (2001) 181-186.
  • [18] C.-J. Chen, K.-L. Lin, The Deposition and Crystallization Behaviors of Electroless Ni-Cu-P Deposits, Journal of Electrochemical Society 146 (1999) 137-143.
  • [19] K. Przybyłowicz, Metal Science, WNT, 1992, 431 (in Polish).
  • [20] S. Ichikawa, K. Miyazawa, H. Ichinose, K. Ito, The Microstructure of the Deformed Nanocrystalline Ag and Ag/Fe Alloy, NanoStructured Materials 11 (1999) 1301-1311.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BWAN-0002-0018
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.