Composite insulation mass decrements due to electric tensions influence

• Autorzy: Subocz L.
• Konferencja: II International Conference on Advances in Processing, Testing and Application of Dielectric Materials, 15-17 September, Wrocław 2004
• Języki publikacji: EN

Abstrakty

EN

The composite insulation exposed to electric tension turns out to show mass decrements. The size of mass decrements depend on the level and duration of electric tension, on insulation surface conductivity and type of material. The process results in electric insulation surface changes. The relationship between the mass decrements and electric tension duration time proves to be similar to lime relationship of surface current leakage. Mass decrements in time function show either rapid exponential increase or get stabilized at the level that does not imperil the insulation durability, depending on the tension level and material type. The determination of mass decrement characteristics in function of insulation performance time is of great significance for prediction estimates of insulation durability.

Słowa kluczowe

EN

composite insulation; mass decrements

• Wydawca: Oficyna Wydawnicza Politechniki Wrocławskiej
• Czasopismo: Prace Naukowe Instytutu Podstaw Elektrotechniki i Elektrotechnologii Politechniki Wrocławskiej. Konferencje
• Rocznik: 2004
• Tom: Vol. 40, nr 15
• Strony: 188--191
• Opis fizyczny: Bibliogr. 8 poz., rys.

Twórcy

autor

Subocz L.

• Technical University of Szczecin, Poland

Bibliografia

• [1] TANAKA T., OKAMOTO T., .NAKANISHI K.,. MIYAMOTO T., Aging and Related Phenomena in Modern Electric Power System, IEEE Trans.Insul. (1993), Vol. 28, No 5, p. 826-843.
• [2] KÖNIG.D., QUINT.I., RAO.Y.N., Investigations on the Very Early Stage of Surface Aging of Lightly Contaminated Epoxy Resin Post Insulators, (1991). Proc. 7-th ISH,Dresden, p. 24.02.
• [3] SCHOOLENBERG G.E., VINK P., Ultra-violet degradation of polypropylene: 1. Degradation profile and thickness of the embrittled surface layer, (1991). Polymer, Vol. 32, No 3, p. 432-437.
• [4] STARR.W.T., Polymeric Outdoor Insulation, (1990) IEEE Trans. El. Insul., Vol. 25, No 1, p. 125-136.
• [5] DAS-GUPTA.D.K., Electrical Properties of Surface of Polymeric Insulators, (1992). IEETrans.El.Insul.,Vol. 27, No 5, p. 909-923.
• [6] SUBOCZ.L., Badania wpływu powierzchniowych wyładowań niezupełnych na erozje tworzyw sztucznych stosowanych w izolacji napowietrznej, Prace IPEiE Politechniki Wrocławskiej, (1986), 24, 5. 124-129.
• [7] SUBOCZ L., Starzenie laboratoryjne kompozytowej izolacji wnętrzowej. Wiadomości Elektrotechniczne maj (1994), s. 178-180
• [8] SUBOCZ L., The silicone rubber protective coating h.v. insulator models. UESS NUSSE'95, (1995), July 10-15, Sewastopol, Ukraine