Comparison of the tribological properties of the surface layers oF TiN and CrN

• Autorzy: Lubas P.
• Języki publikacji: EN

Abstrakty

EN

This work revealed the results of comparative surveys of the impact of formed surface layer TiN and CrN and two component surfaces layer TiN-steel and CrN-steel. The slide couple worked in conditions of lubricating the friction area with Lotos Syntetyk 5W/40 and Castrol GTX Magnatec 5W/40 engine oils. In the friction couple the counter sample was made from CuPb30 bearing alloy. The tribological survey was carried out on a Tester T-05. The results of the tests proved the possibility of implementing two component surface layers in slide couples, which work under mixed friction conditions. The surveys revealed that the friction force, temperature within the friction area and wear of bearing material, depend on friction conditions and combination of mating surface layers of friction couple. Beneficial friction parameters were observed in case of friction couples with binary CrN-steel surface layers of the journal.

Słowa kluczowe

EN

TiN; CrN; TiN-steel; CrN-steel; Lotos Syntetyk 5W/40; Castrol GTX Magnatec 5W/40 engine oils

• Wydawca: Łukasiewicz Research Network - Institute of Aviation ; European Science Society of Powertrain and Transport KONES Poland ; Wydawnictwo Instytutu Technicznego Wojsk Lotniczych
• Czasopismo: Journal of KONES
• Rocznik: 2005
• Tom: Vol. 12, No. 1-2
• Strony: 195--200
• Opis fizyczny: Bibliogr. 5 poz., rys.

Twórcy

autor

Lubas P.

• Instytut Techniki Universytet Rzeszowski ul. Rejtana 16a 35-959 Rzeszów tel.: [phone], fax: [phone],

Bibliografia

• [1] Kula P., Inżynieria warstwy wierzchniej. Politechnika Łódzka, Łódź, 2000.
• [2] Nakonieczny A., Powierzchniowe obróbki wyrobów metalowych. IMP, Warszawa 2000.
• [3] Sęp J., Zielecki W., Preliminary evaluation of the application possibility of bearing journal with two component surface layer. Tribologia, nr 3, 1995.
• [4] Szczerek M., Metodologiczne problemy systematyzacji eksperymentalnych badań tribologicznych. ITE, Radom 1997.
• [5] Wierzchoń T. Precht W., Ulbin-Pokorska I., Sikorski K., Struktura i odpornośćwarstw azotku chromu wytwarzanych na stali metodą próżniowego odparowania łukowego. InżynieriaMateriałowa, nr 6, 2000.