Cement and sulphate free autoclaved aerated concrete

• Autorzy: Stumm A.
• Konferencja: 5th International Conference on Autoclaved Aerated Concrete "Securing a sustainable future" to be held at Bydgoszcz to celebrate 60 years of AAC experience in Poland, Bydgoszcz, September 14-17, 2011
• Języki publikacji: PL

Abstrakty

EN

New laws are likely which will make putting autoclaved aerated concrete (AAC) into landfills more difficult in the future. Consequently, a project was launched at Xella to reduce the sulphate content in AAC to almost zero. Positive side effects are no risk of thaumasite, agglomeration residue of lime and grey stains. The biggest source of sulphate besides cement is the pure calcium sulphate, which is added either as gypsum or anhydrite to the mixture. Additional calcium sulphate has been used in AAC to improve its material properties for many years. The reduction of calcium sulphate in ordinary cementitious AAC recipes leads to high shrinkage and less compressive strength of the material. Sulphate free AAC with a low bulk density is not yet being made in mass production. Due to the retarding effect on of the hydraulic binder cement, completely sulphate free recipes could not be handled in technologies like Durox, Hebel or Ytong yet. Cement and sulphate free AAC cakes tend to collapse either in the demoulding or autoclaving process, and especially low densities are difficult to process. Technological solutions and recipes were found to produce cement and sulphate free AAC with low bulk densities in moulds with the size of 5.4 m3. The material meets the requirements for the German bulk density class PP2/0.35 with Gamma 0.09 W/(mK). The shrinkage tests show values under 0.20 mm/m according to DIN EN 680. Finally, it was shown that cement free recipes lead to fewer transportation damages due to less brittle surfaces. Further research is currently in progress.

Słowa kluczowe

PL

beton komórkowy; zawartość siarczanów; zamiennik cementu; taumazyt

EN

autoclaved aerated concrete; sulphates content; thaumasite

• Wydawca: Fundacja Cement, Wapno, Beton
• Czasopismo: Cement Wapno Beton
• Rocznik: 2011
• Tom: nr spec.
• Strony: 26--28
• Opis fizyczny: Bibliogr. 3 poz., il.

Twórcy

autor

Stumm A.

• Xella Technologie- und Forschungsgesellschaft mbH, Produkt- und Prozessforschung, Hohes Steinfeld 1, 14797 Kloster Lehnin, Germany

Bibliografia

• [1] Clementi F. 1967, Verfahren zur Herstellung von dampfgehärtetem Gasbeton, German patent, Aktenzeichen DE 16 46 580.8-45 (H 62442), Bundesrepublik Deutschland, Deutsches Patentamt
• [2] Straube B., Langer P., Stumm A. 2008, Durability of Autoclaved Aerated Concrete, 11DBMC International Conference on Durability of Building Materials and Components, Istanbul Turkey, May 11-14th, 2008.
• [3] Zürn S.G. 1997, Einfluss der Sandminerale auf die Bildung von Calciumsilikathydraten (C-S-H-Phasen), das Gefüge und die mechanischen Eigenschaften von Porenbetonprodukten, Logos Verlag Berlin.