Wpływ stabilizatorów na hydratację Beta-C2S

• Autorzy: Gawlicki M.

Warianty tytułu

PL

Effect of stabilizers on Beta-C2S hydration

• Języki publikacji: EN

Abstrakty

EN

The effect of stabilizers, added as 0.5% by mole, on the Beta-C2S hydration process was investigated. The hydraulic activity of Beta-C2S with stabilizers was related to results for Beta-C2S stabilized by thermal treatment. The hydration of dicalcium silicate doped with Ba2+ added as 1 and 3% (by mole) was also studied. The experiments were carried out at room temperature on the pastes produced at w/c ratio 0.5, as well as on the suspensions with l/s ratio 100 or 200. The accelerating effect of Ba2+ introduced to the Beta-C2S structure was found as well as the retardation of the hydration process in the samples stabilized with As5+, B3+, Cr6+, P5+ and V5+ ions.

PL

Dokonano oceny wpływu na hydratację Beta-C2S szeregu stabilizatorów, które wprowadzono do krzemianu dwuwapniowego w ilości 0,5% mol. i porównano ją z aktywnością hydrauliczną Beta-C2S uzyskanego na drodze stabilizacji termicznej. Przedmiotem badań była również hydratacja krzemianu dwuwapniowego zawierającego 1 i 3% mol Ba2+. Hydratację prowadzono w temperaturze pokojowej w zaczynach, w których stosunek masy wody do masy Beta-C2S (l/s) = 0,5 oraz w zawiesinach wodnych o stosunku l/s =100 lub 200. Stwierdzono, że wprowadzenie do struktury Beta-C2S jonów Ba2+ przyspiesza hydratację krzemianu dwuwapniowego, podczas gdy jony As5+, B3+, Cr6+, P5+ i V5+ opóźniają postęp hydratacji Beta-C2S.

Słowa kluczowe

EN

Portland cement; dicalcium silicate; hydration; stabilization; stabilizing factor

PL

cement portlandzki; krzemian dwuwapniowy; hydratacja; stabilizacja; czynnik stabilizacji

• Wydawca: Fundacja Cement, Wapno, Beton
• Czasopismo: Cement Wapno Beton
• Rocznik: 2008
• Tom: R. 13/75, nr 3
• Strony: 147--154
• Opis fizyczny: Bibliogr. 26 poz., il.

Twórcy

autor

Gawlicki M.

• Akademia Górniczo-Hutnicza, Kraków

Bibliografia

• 1. K. Quillin, Cem. Concr. Res., 34, 1341 (2004).
• 2. W. Kurdowski, A. Thiel, Cem. Concr. Res., 21, 29 (1981).
• 3. M. Gawlicki, Ceramika, 104, 7 (2008).
• 4. W. Kurdowski, Chemia cementu. Wyd. Nauk. PWN. Warszawa 1991.
• 5. M. Gawlicki, Ceramika, 103, 989 (2008).
• 6. E. Duczymińska, Praca doktorska, Kraków, AGH, 1969.
• 7. M. Handke, W. Ptak, Ceramurgia International, 4(2), 75 (1978).
• 8. l. Odler, Rozdział w: Lea's chemistry of cement and concrete. (ed. P.C Hewlett). Elsevier Ltd. 4łh ed. 1988, reprinted 2006, 241-297.
• 9. H. Ishida, K. Sasaki, T. Mitsuda: J. Am. Ceram. Soc., 75(2), 353 (1992).
• 10. K. Yanagisawa, X. Hu, A. Onada, K. Kajiyoshi, Cem. Concr. Res., 36, 81 (2006).
• 11. D.L Kantro C.H. Weise, J. Am. Ceram. Soc., 62(11-12), 621 (1979).
• 12. K. Fujii, W.Kondo, J. Am. Ceram. Soc., 62(3-4), 161 (1979).
• 13. D. M Roy, S.O. Oyefesobi, J. Am. Ceram. Soc., 60(3-4), 161 (1979).
• 14. H. Funk, Z. Anorg. und Algem. Chem., 291, 276 (1957).
• 15. P. Fierens, J. Tirlocq, Cem. Concr. Res., 13, 267 (1983).
• 16. I.M. Pritts, K.E. Daugherty, Cem. Concr. Res., 6, 783 (1976).
• 17. R. Parkash, S.K. Mehta, Termochimica Acta, 424, 17 (2004).
• 18. L. Cussino, L. Montanaro, A. Negro, II Cemento, 4, 435 (1986).
• 19. W. Kurdowski, Prace Komisji Ceramicznej PAN, Ceramika, 18, 1 (1972).
• 20. A. Kiyoshi, Proc. 9th Int. Congr. Chem. Cem., New Delhi, Vol. IV, 181 (1992).
• 21. P.W. Brown, J. Am. Ceram. Soc., 75(1), 17 (1992).
• 22. E. Moudilou, F. Amin, B. Bollotte, Proc. 12th Int. Congr. Chem. Cem., Montreal, Canada, 8-13 July 2007. CD, T1-04.1.
• 23. M. Gawłicki, W. Nocuń-Wczelik, Proc. 8łh Int. Congr. Chem. Cem., Rio de Janerio, vol. III, 183 (1986).
• 24. M. Hanna, R.L. Cook, D.L. Kantro, Journal of Applied Chem., 20, 334(1970).
• 25. J.N. Maycock., M. McCarthy, Cem. Concr. Res., 3, 701 (1973).
• 26. A. Bobrowski, M. Gawlicki, J Małolepszy, Env. Sci. & Technol., 31, 745(1997).