Odporność chemiczna zapraw cementowych z dodatkiem metakaolinitu

• Autorzy: Pytel Z.

Warianty tytułu

EN

Resistance of cement mortars with metakaolinite to chemical corrosion

• Języki publikacji: EN

Abstrakty

EN

The effect of metakaolinite on the chemical corrosion resistance of laboratory cements was studied. The cements were produced from industrial clinkers. Six cement samples, differing with C3A content (in clinker: 3% and 11% respectively) were prepared. The metakaolinite content was 20 and 30 % and subsequently they corresponded to the standard cements CEM II/A-Q and CEM II/B-Q (EC standards). The standard mortars were produced and stored in sodium and magnesium sulfate corrosive solutions for 360 days. It has been found that the corrosion resistance of mortars with metakaolinite increased, particularly after one year curing. The significant strength development in case of samples stored in water was also observed.

PL

Badano wpływ dodatku metakaolinitu na odporność chemiczną cementów przygotowanych w laboratorium, z klinkierów przemysłowych. Do badań przygotowano sześć cementów różniących się zawartością C3A w klinkierze portlandzkim, która wynosiła odpowiednio 3 i 11%. Do cementów dodano 20 i 30% metakaolinitu, dzięki czemu spełniały wymagania dla cementów CEM II/A-Q i CEM II/B-Q. Z cementów tych przygotowano zaprawy normowe, które poddano korozji w roztworach siarczanów sodu i magnezu w okresie 360 dni. Stwierdzono, że dodatek metakaolinitu zwiększył odporność zapraw na działanie siarczanów. Dodatek ten zwiększył także wytrzymałość zapraw dojrzewających w wodzie po dłuższym okresie twardnienia, szczególnie po roku.

Słowa kluczowe

PL

odporność chemiczna; zaprawa cementowa; dodatek mineralny; metakaolinit; właściwości; cement; korozja chemiczna; korozja siarczanowa; badanie; mikrostruktura; zaprawa stwardniała; porowatość

• Wydawca: Fundacja Cement, Wapno, Beton
• Czasopismo: Cement Wapno Beton
• Rocznik: 2005
• Tom: R. 10/72, nr 6
• Strony: 330--338
• Opis fizyczny: Bibliogr. 13 poz., il., tab.

Twórcy

autor

Pytel Z.

• Akademia Górniczo-Hutnicza, Katedra Technologii Materiałów Budowlanych, Wydział Inżynierii Materiałowej i Ceramiki, Kraków

Bibliografia

• 1. H. F. W. Taylor, Cement Chemistry, Academic Press, London 1990.
• 2. W. Kurdowski, Chemia cementu, Wydawnictwo Naukowe PWN, Warszawa 1991.
• 3. K. Takemoto, H. Uchicawa, Hydration of pozzolanic cement. 7th ICCC Paris, t. IV, pp. IV-2/1-29, Paris 1980.
• 4. P. S. de Silva, F.P. Glasser, Hydration of cements based on metakaolin: thermochemistry, Advances in Cement Research, 3 (1990), pp. 167-177.
• 5. H. Uchikawa, Effect of blending components on hydration and structure formation, 8th ICCC, Rio de Janeiro, t. I, pp. 249-280, Rio de Janeiro 1986.
• 6. P. S. de Silva, F. P. Glasser, Pozzolanic activation of metakaolin, Advances in Cement Research, 4 (1992), pp. 167-178.
• 7. J. Małolepszy, Z. Pytel, "Effect of metakaolinite on the strength and chemical resistance of cement mortars", Proceedings Fifth International Conference CANMET-ACI, Barcelona, Spain 04 - 09. 06 2000, Volume I, pp. 189-204.
• 8. B. D. Barens, S. Diamond, W. L. Dolch, ''The contact zone between portland cement pasta and glass "aggregate" surfaces", Cem. Concr. Res., 8 (1978), p. 233,244.
• 9. Z. Pytel, J. Małolepszy, "Badanie produktów hydratacji metakaolinitu w obecności jonów wapniowych i aktywatorów chemicznych w warunkach hydrotermalnych", Cement-Wapno-Beton, R. VIII/LXX, 2003 r., nr 3, s. 152-155.
• 10. P. S. de Silva, F. P. Glasser, Phase Relations in the system CaO-Al2O3- SiO2-H2O relevant to metakaolin-calcium hydroxide hydration, Cem. Concr. Res., 23 (1993), pp. 627-639.
• 11. Z. Pytel, J. Małolepszy, "Wpływ warunków prażenia gliny kaolinowej na jej własności pucolanowe", Cement-Wapno-Beton, Vol. IV/LXVI, 1999, nr 3, s. 80-83.
• 12. PN-B-19707:2003 - Cement. Cement specjalny. Skład, wymagania i kryteria zgodności.
• 13. J. Małolepszy, J. Deja., Brylicki W., Gawlicki M., "Technologia betonu. Metody badań", Wyd. AGH, Kraków 1995.