Service durability of the first welded bridges in Poland in the light of their butt joint investigation

• Autorzy: Wichtowski B.

Warianty tytułu

PL

Trwałość eksploatacyjna pierwszych spawanych mostów w Polsce w świetle badań ich złączy doczołowych

• Języki publikacji: EN

Abstrakty

EN

According to Polish Standard PN-82/S-10052 special quality joints assigned to defectiveness class R1 or R2 are allowed in new bridge structures; usual quality joints on the other hand should have the quality not inferior to class R3 joints. No physical state of deterioration whatsoever is allowed in structures. These requirements are not satisfied in case of structures in operation. For example in 9 welded bridges built in the years 1935-1939, presented in this paper, underbead cracks have been found in 88.9% of butt joints on examined structures and joints of R4 and R5 defectiveness class were present on all objects. In order to determine the further safe period of utilization of these bridges, fatigue strength investigation of welded butt joints in these structures was carried out and stress analysis made.

PL

Według normy PN-82/S-10052 w nowych konstrukcjach mostowych dopuszczalne są spoiny specjalnej jakości zaliczane do klasy wadliwości R1lub R2, natomiast spoiny normalnej jakości powinny charakteryzować się jakością nie gorszą niż spoiny klasy R3. Jakikolwiek stan fizycznego zniszczenia jest w konstrukcjach niedopuszczalny. Wymogi te nie są spełnione w konstrukcjach eksploatowanych. Przykładowo w przedstawionych w artykule 9 mostach spawanych wybudowanych w latach 1935-1939 stwierdzono pęknięcia wewnętrzne w złączach doczołowych 88,9% przebadanych obiektów, a spoiny klasy wadliwości R4 i R5 występują we wszystkich obiektach. W celu określenia dalszego bezpiecznego czasookresu użytkowania tych mostów wykonano badania wytrzymałości zmęczeniowej spawanych złączy doczołowych w nich występujących oraz przeprowadzono ich analizę naprężeniową.

Słowa kluczowe

PL

trwałość eksploatacyjna; most spawany; złącze doczołowe; Polska; badanie złącza; wytrzymałość zmęczeniowa

• Wydawca: Komitet Inżynierii Lądowej i Wodnej PAN ; Politechnika Warszawska, Wydział Inżynierii Lądowej
• Czasopismo: Archives of Civil Engineering
• Rocznik: 2003
• Tom: Vol. 49, nr 2
• Strony: 165--190
• Opis fizyczny: Bibliogr. 29 poz., il.

Twórcy

autor

Wichtowski B.

• Theory of Structures Department, Szczecin University of Technology, Szczecin

Bibliografia

• 1. B. WICHTOWSKI, On some consequences of failure during the construction of a welded railway viaduct [in Polish], Inż. i Bud., 8, 425-427, 1998.
• 2. A. JAROMINIAK, A. ROSSET, Bridge disasters and failures [in Polish], WKŁ, Warszawa 1986.
• 3. M. RYBAK, Empirical investigations of structures as a field of science [in Polish], Inż. i Bud., 10, 400-402, 1991.
• 4. J. W. FISHER, D. R. MERTZ, Hundreds of bridges-thousands of cracks, Civil Engineering (ASCE), No 4, 64-67, 1985.
• 5. H. OSTAPIUK, B. WICHTOWSKI,Condition of welded joints in operating railway bridges in the light of X-ray investigations [in Polish], Inż. i Bud., 10, 369-372, 1991.
• 6. B. WICHTOWSKI, 55 years of operation of the first welded railway bridges in Poland [in Polish], Inż. i Bud., 5, 200-204, 1994.
• 7. B. WICHTOWSKI, Non-destructive diagnostic investigations of steel railway bridges [in Polish], Przegląd Kolejowy, 4, 31-34, 1997.
• 8. M. RYBAK, B. WICHTOWSKI,The state of bridges on E-20 line in the light of X-ray investigations [in Polish], Inż. i Bud., 10, 528-531, 1995.
• 9. B. WICHTOWSKI, Durability of steel bridges on Katowice-Tczew railway line in the light of X-ray investigation [in Polish], Prace IBDiM, 1-2, 183-193, 1997.
• 10. Z. K. LEŚNIAK, Cracks in steel railway bridges [in Polish], Inż. i Bud. 8-9, 299-302, 1965.
• 11. 60 years of the first welded bridge in the world, Joint edition of SKL, KILW PAN, KKM PZITB & others, Warszawa 1989.
• 12. W. KARŚNICKI, History of two welded bridges near Łowicz [in Polish], Przegląd Spawalnicwa, 10-11, 220-221, 1976.
• 13. F. SZELĄGOWSKI, First railway bridge in Poland witn welded girders [in Polish], Inżynier Kolejowy, 11, 388-390, 1936.
• 14. F. SZELĄGOWSKI, Railway bridge over Sierpienica river on Nasielsk-Sierpc line [in Polish], Inżynier KoLejowy, 12, 478-480, 1937.
• 15. F. SZELĄGOWSKI, Railway bridge on Warsaw-Gdynia line [in Polish], Inżynier Kolejowy, 3, 129-131,1939.
• 16. First welded truss railway bridge on Polish State Railways [in Polish], Drogi Kolejowe, 11, 240-242, 1988.
• 17. First completely welded bridge in France (supplement "Review of foreign railway press") [in Polish], Inżynier Kolejowy, 10, 173-175, 1937.
• 18. B. WICHTOWSKI,The behaviour of the oldest welded railway bridge in Poland, Proc. II International Scientific Conference, Durability and service life of bridge structures, Poznań 1994, 351-356.
• 19. Stahl im Hochbau, Techenbuch für Entwurf, Berechnung und Auführung von Stahlbauten, Verlag Stahlleisen m.b.H., Düsseldorf und J. Springer, Berlin 1935.
• 20. W. PONIŻ, A. WITKOWSKI, Welded road bridge over Słudwia river in the light of X-ray investigation after 34 years in service [in Polish], Inż. i Bud., 10, 373-375, 1962.
• 21. A. KLIMPEL, Inspection and quality control in welding [in Polish], vol. 1, Wyd. Politechniki Śląskiej, Gliwice 1998.
• 22. A. SZYMAŃSKI, Inspection and quality control in welding [in Polish], vol. 2, Wyd. Politechniki Śląskiej, Gliwice 1998.
• 23. W. BOGUCKI, Examination of behaviour of Słudwia river bridge [in Polish], Inż. i Bud., 10, 375-377, 1962.
• 24. B. WICHTOWSKI, Fatigue strength of welded joints in flanges of railway bridge plate girders [in Polish], Inż. i Bud., 10, 574-577, 1998.
• 25. B. WICHTOWSKI, T. CZAJKOWSKI, Fatigue life of railway bridge welded joints, Proc. IABSE Report "Saving Buildings in Central and Eastern Europe", Berlin 1998.
• 26. H. CZUDEK, T. PIETRASZEK, Durability of steel bridge structures under variable loading [in Polish], WKŁ, Warszawa 1980.
• 27. A. A. WELLS, Rupture fragile des reciplens á pression et informations nécessaires sur les moyens de veriter par une conception appropriée, Soud et Techn, 14, 449-454, 1960.
• 28. B. WICHTOWSKI, Laboratory investigation of joints with underbead cracks [in Polish], Przegląd Spawalnictwa, 5, 15-18, 2000.
• 29. H. CZUDEK, On service durability of railway steel bridges [in Polish], part I, Drogi Kolejowe, 3, 58-63, 1988; part II, Drogi Kolejowe, 4-5, 73-76, 1988.