Crack resistance research of concrete protective coatings

• Autorzy: Głodkowska W.

Warianty tytułu

PL

Badania rysoodporności powłok ochronnych

• Języki publikacji: EN

Abstrakty

EN

The paper presents innovative approach to crack resistance problem of polymer and polymer-cement coatings used for surface protection of concrete structures. In a result of analysis of operating conditions of the arrangement elements: coating - concrete and loads assisting them in different situations but also anticipated results of their effects, evaluation criteria of crack resistance of protective polymer coatings and polymer-cement ones subject to the activity of short-term and long-term load were work out. On the basis of six coating materials there was made a research verification of crack resistance criteria and effects of mechanical short-term and long-term thermal load and weather factors in regard to crack resistance were defined. Subject to research were the following coating properties: tensile strength, tensile strain, modulus of elasticity under tension and tensile strength adhesion of coatings to the concrete. On the basis of value changes of these properties in reaction to weather conditions, natural ageing curve was worked out for selected polymer coatings and polymer-cement ones. Tests carried out showed correctness of worked out criteria for crack resistance and proved their usage in designing protective coatings for concrete structures.

PL

Artykuł przedstawia nowatorskie podejście do problemu rysoodporności powłok polimerowych i cementowo-polimerowych stosowanych do ochrony powierzchniowej konstrukcji z betonów. W wyniku przeanalizowania warunków pracy elementów układu: powłoka — beton oraz towarzyszących im w różnych sytuacjach obciążeń, a także przewidywanych skutków ich oddziaływania opracowano kryteria oceny rysoodporności powłok polimerowych i cementowo-polimerowych poddanych działaniu obciążeń krótko- i długotrwałych. Na podstawie sześciu materiałów powłokowych dokonano doświadczalnej weryfikacji kryteriów rysoodporności oraz określono wpływ obciążeń mechanicznych krótko- i długotrwałych, obciążeń cieplnych i czynników atmosferycznych na rysoodporność powłok. Badaniami objęto takie cechy powłok jak: wytrzymałość na rozciąganie, odkształcenie przy rozciąganiu, moduł sprężystości przy rozciąganiu i przyczepność do betonu. Na podstawie zmian wartości tych cech, w czasie działania czynników atmosferycznych, opracowano krzywe starzenia naturalnego dla wybranych powłok polimerowych i cementowo-polimerowych. Przeprowadzone badania wykazały poprawność opracowanych kryteriów rysoodporności i wskazały na ich przydatność w projektowaniu powłok ochronnych dla konstrukcji z betonów.

Słowa kluczowe

PL

powłoka ochronna; rysoodporność; badanie rysoodporności; powłoka polimerowa; powłoka cementowo-polimerowa; obciążenie; starzenie naturalne

• Wydawca: Komitet Inżynierii Lądowej i Wodnej PAN ; Politechnika Warszawska, Wydział Inżynierii Lądowej
• Czasopismo: Archives of Civil Engineering
• Rocznik: 2003
• Tom: Vol. 49, nr 2
• Strony: 131--149
• Opis fizyczny: Bibliogr. 21 poz., il.

Twórcy

autor

Głodkowska W.

• Koszalin University of Technology

Bibliografia

• 1. Z. ŚCIŚLEWSKI, Protection of reinforced concrete constructions [in Polish], Arkady, Warszawa 1999.
• 2. D.W.S. Ho, D. RITCHIE, Surface coatings and their influence on the quality of the concrete substrate, Polymers in Concrete (Ed. Ohama Y., Kawakami M., Fukuzawa K.), Published by E & FN Spon 1997.
• 3. L. CZARNECKI: Repairing and protection of reinforced concrete constructions [in Polish], Polski Cement, Kraków 2002.
• 4. G. RISCHE, H. ROSS, Messung der Verbundlänge von rissüberbrückenden Kunstharzbeschichtungen, Int. Koll. Werkstoffwissenschaften und Bausanierung, Esslingen 1983.
• 5. G. RISCHE, Rissüberbrückende Kunststoffeschichtungen für Mineralische Baustoffe, Farbe-Lack, Zentrablatt der Farben und Lackindustrie und des Handels, 85, 10, 824-831, 1979.
• 6. W. TEEPE, Mechanische Beanspruchungen der Kunstoffe im Massivbau, Kunststoffe, 52, 1962.
• 7. T. BRONIEWSKI, Anti-corrosion coatings resistant to cracks of concrete foundation [in Polish], Building Engineering, Scientific Journal, Kraków Technical University, 2, 1974.
• 8. A. ALMAHDI, Limiting state of crack opening for reinforced concrete constructions protected with chemo-resistant coatings from synthetic resins [in Polish], Dissertation, Warsaw Technical University, Warszawa 1983.
• 9. H.H. ABRISHAMI, W.D. COOK, D. MITCHELL, The effect of epoxy-coated reinforcement and concrete quality on cracking of flat plate slab-column connections, ACI Materials Journal, 121-128, 1996.
• 10. W. GŁODKOWSKA, Z. PIĄTEK, Crack resistance of the protective coatings subjected to long-term load [in Polish], XLVI Conference on Civil Engineering KILiW PAN and KN PZITB, Krynica 2000, 169- 176, Vol. 2.
• 11. W. GŁODKOWSKA, Z. PIĄTEK, Ageing of polymer and polymer-cement composites used for concrete repairs [in Polish], XLVII Conference on Civil Engineering KILiW PAN and KN PZITB, Krynica 2001,315-322, Vol. 1.
• 12. T. Hop, Polymer concrete [in Polish], Silesian University of Technology, Gliwice 1992.
• 13. W. GŁODKOWSKA, The crack resistance criteria of protective coating [in Polish]. XLVIII Conference on Civil Engineering KILiW PAN and KN PZITB, Krynica 2002, 19-26, Vol. 3
• 14. L. CZARNECKI, A. GARBACZ, Evaluation of polymer coating crack-bridging ability, International Colloquium, Industrial Floors '95, Esslingen 1995.
• 15. K. WAGNER, W. DIECKE, Rissüberbrückung bei Betonbauwerken durch Kunst-harzbeläge, Bauplanung Bautechnik, 1974.
• 16. W. GŁODKOWSKA, Compatibility of polymer composite-cement concrete system [in Polish], Dissertation, Warsaw Technical University, Warszawa 1994.
• 17. W. GŁODKOWSKA, Z. PIĄTEK, Experimental verification of the model of compatibility between concrete and certain coats [in Polish], Scientific Journals WBiIŚ Technical University of Koszalin, 13, 27-34, 1998.
• 18. D. PLUM, Materials - what to specify, Construction Maintenance & Repair,7-8, 1001, 37.
• 19. Draft Test recommendations, Technical Committee 113-CPT, RILEM 1995.
• 20. BS 2782: Part 3. Methods 320A to 320F. Tensile strength, elongation and elastic modulus.
• 21. W.I. SYTNIK, Stroicielnyje konstrukcji iz polimiemych materiałow, Urożaj, Kijew 1988.