Calcium germanates and their hydraulicity

• Autorzy: Bensted J.

Warianty tytułu

PL

Germaniany wapniowe i ich własności hydrauliczne

• Języki publikacji: EN PL

Abstrakty

EN

Calcium germanates and their hydraulicity have been surveyed. Calcium germanates often form similar compositions to the analogous calcium silicates, which are correspondingly isostructural. Only two calcium germanates are known to be hydraulic, tricalcium germanate C3G and dicalcium germanate C2G. C3G reacts very rapidly with water to form calcium germanate hydrate C-G-H, a strong binder. Unlike C-S-H formation from C3S, there is no period of induction during the early part of hydration. C2G reacts at a much slower rate than C3G with water, although still faster than the different C2S varieties in their hydration, to form a similar type of C-G-H. The potential for C-G-H as a binder is discussed.

PL

Podano przegląd germanianów wapniowych i ich własności hydraulicznych. Germaniany wapniowe często tworzą związki zbliżone do analogicznych krzemianów wapniowych, z którymi są odpowiednio izostrukturalne. Tylko dwa germaniany wapniowe mają własności hydrauliczne: germanian trójwapniowy C3G i germanian dwuwapniowy C2G. C3G reaguje bardzo szybko z wodą tworząc uwodniony germanian wapniowy C-G-H, materiał silnie wiążący. W odróżnieniu od powstawania C-S-H z C3S nie występuje tu okres indukcji w początkowym okresie hydratacji. C2G reaguje z wodą ze znacznie mniejszą szybkością niż C3G, choć szybciej niż różne odmiany C2S, z utworzeniem podobnego rodzaju C-G-H. Omówiono potencjalne możliwości zastosowania C-G-H jako spoiwa.

Słowa kluczowe

PL

germanian wapniowy; właściwości hydrauliczne; hydratacja; cement; zastosowanie

• Wydawca: Fundacja Cement, Wapno, Beton
• Czasopismo: Cement Wapno Beton
• Rocznik: 2002
• Tom: R. 7/69, nr 1
• Strony: 8--14
• Opis fizyczny: Bibliogr. 23 poz., il.

Twórcy

autor

Bensted J.

• Brikbeck College, University of London

Bibliografia

• 1. J. Bensted: Zement-Kalk-Gips International 53 (12), 704 (2000).
• 2. J. Bensted: Kurdowski Symposium, Science of Cement and Concrete, Kraków, June 20-21, (Ed. W. Kurdowski, M. Gawlicki), p. 189, Wydawnictwo Naukowe "Akapit", Kraków (2001).
• 3. A.K. Shirvinskaya, R.G. Grebenshchikov, N.A. Toropov, lzvest. Akad. Nauk SSR, Neorg. Mater. No. 2, 332 (1966).
• 4. H. Strunz, Naturwissenschaften 47, 154 (1960).
• 5. J. Bensted, S.P. Varma, Klei en Keramiek 23, No. 2, 66 (1973).
• 6. W. Eysel, Th. Hahn, Neues Jahrbuch für Mineralogie, Monatshefte No. 6, 137 (1963).
• 7. H.F.W. Taylor, Mineralogical Magazine 38, 26 (1971).
• 8. Th. Hahn, W. Eysel, Naturwissenschaften 50, 471 (1963).
• 9. G. Eulenberger, A. Wittmann, H. Nowotny, Monatshefte für Chemie 93, 1046 (1962).
• 10. J. Bensted, II Cemento 75 (3),129 (1978).
• 11. Th. Hahn, G. Eysel, Zeitschrift für Krystallographie 131, 40 (1970).
• 12. A.I. Boikova, A.I. Domansky, Cement and Concrete Researeh 4.773 (1974).
• 13. M. Moranville-Regourd, A.I. Boikova, Proc. 9th Int. Congr. Chem. Cem., New Delhi 1 (1992) 23
• 14. A.I. Boikova, N.A. Toropov, V.T. Vavilonova, Doklady Akad. Nauk SSR 175, No. 3, 654 (1967).
• 15. D. Sample, P.W. Brown, Journal of the American Ceramic Society 75, 3070 (1992).
• 16. R.Trettin, I. Odler, A. Gerdes, G. Oliew, Advanees in Cement Research 7, No. 27, 117 (1995).
• 17. J. Bensted, II Cemento 91 (3),169 (1994).
• 18. J. Bensted, in 'Advances in Cement Technology', (Ed. S.N. Ghosh), p. 307, Pergamon Press, Oxford, New York (1983).
• 19. J. Bensted, Chemistry and Industry (London) 885 (1975).
• 20. J. Bensted, Cement and Concrete Research 8 (1), 73 (1978).
• 21. R. Trettin, I. Odler, A. Gerdes, Advances in Cement Research 7, No. 28, 139 (1995).
• 22. American Petroleum Institute, Specification for Materials and Testing for Well Cements, API Specification 10, 5th Edition (1990).
• 23. J. Bensted, in 'Lea's Chemistry of Cement and Concrete', 4th Edition, (Ed. P.C. Hewlett), p. 821, Arnold Publishers, London (1998).