Modellization of cyclic extrusion compression using elastoplastic model

• Autorzy: Richert M. , Baczmański A. , Richert J.

Warianty tytułu

PL

Modelowanie procesu cyklicznego wyciskania ściskającego (CWS) przy użyciu modelu elastoplastycznego

• Języki publikacji: EN

Abstrakty

EN

In this work the development of texture and microstructure in the range of very large deformations exerted by the CEC process were studied. The elastoplastic models were used to predict the behaviour of aluminium subjected to the reversible tensile and compressive deformations. The theoretical pole figures well fit to the experimental ones. During the CEC process the texture changes periodically leading to relatively low sample anisotropy for large degree of deformation. The evolution of microstructure was not reversible, however, some parameters (for example hardening) reached the saturation after a few cycles.

PL

W pracy przedstawiono ewolucję tekstury i mikrostruktury w zakresie bardzo dużych odkształceń wywieranych metodą cyklicznego wyciskania ściskającego (CEC). Modele elastoplastyczne zostały użyte do przewidywania zmian tekstury w próbkach aluminiowych poddanych na przemian rozciąganiu i ściskaniu. Stwierdzono dobrą zgodność doświadczalnych i modelowych figur biegunowych. Podczas procesu CWS tekstura zmienia się periodycznie, powodując niską anizotropię materiału w- zakresie bardzo dużych odkształceń. Stwierdzono, że ewolucja struktury nic była cykliczna, jednakże pewne parametry materiału (np. umocnienie plastyczne) osiągało stan nasycenia już po kilku cyklach odkształcenia metodą CWS.

Słowa kluczowe

EN

cyclic extrusion compression; CEC; elastoplastic model

PL

cykliczne wyciskanie ściskające; CWS; model elastoplastyczny

• Wydawca: Wydawnictwo Naukowe PWN SA
• Czasopismo: Archives of Metallurgy
• Rocznik: 2000
• Tom: Vol. 45, iss. 4
• Strony: 381--392
• Opis fizyczny: Bibliogr. 24 poz., rys., tab.

Twórcy

autor

Richert M.

• Wydział Metali Nieżelaznych, AGH, 30-059 Kraków, Al. Mickiewicza 30

autor

Baczmański A.

• Wydział Fizyki i Techniki Jądrowej, AGH, 30-059 Kraków, Al. Mickiewicza 30

autor

Richert J.

• Wydział Metali Nieżelaznych, AGH, 30-059 Kraków, Al. Mickiewicza 30

Bibliografia

• [1] J. Richert, M. Richert Aluminium 62, 8, 604 (1986)
• [2] M. Richert, A. Korbel, Journal of Materials Processing. Technology 53, 331 (1995).
• [3] M. Richert, Journal of the Mechanical Behaviour of Materials 8, No. 4, 295 (1997).
• [4] M. Richert, IX Conference on Electron Microscopy of Solids. A. Czyrska-Filemonowicz, at all. (eds.) 6-9 May, Krakow-Zakopane, Poland, 235 (1996).
• [5] M. Richert, A. Korbel, Materials Science & Engineering A A234-236, 908 (1997).
• [6] M. Richert, H. McQueen, 35th Annual Conference of Metallurgists, H. McQueen at all. (eds.) 25-29 August 1996 - Queen Elizabeth Hotel, Montreal, Quebec, Canada, 15 (1996).
• [7] M. Richert, H. McQueen, J. Richert, Canadian Metal. Quart. 37, 449 (1998).
• [8] M. Richert, Q. Liu, N. Hansen, Materials Science & Engineering A260. 275 (1999).
• [9] M. Richert, Inżynieria Materiałowa 2, 59 (1998).
• [10] T. Loffers, Phys. Slat Sol. 25, 337 (1968).
• [11] J. Tarasiuk, K. Wierzbanowski, J. Kuśnierz, Arch. Metall. 38, 35 (1993).
• [12] M. Berveiller, P. Lipiński. Int. Journ. of Pasticity 3, 162 (1987).
• [13] P. Lipiński, M. Berveiller, Int. Journ. of Plasticity 5, 149 (1989).
• [14] P. Franciosi. M. Berveiller, A. Zaoui, Acta Met 28, 273 (1980).
• [15] E Kroner, E. Z. Phys. 151, 504 (1958).
• [16] R. Hill, J. Mech. Phys. Solids 13, 89 (1965).
• [17] J. W. Hutchinson, Proc. Roy. Soc. A319, 247 (1970).
• [18] M. Berveiller, M. Zaoui, A. J. Mech. Phys. Solids 26, 325 (1979).
• [19] G. J. Wenig, Int. J. Engng. Sci. 18, 1385 (1980).
• [20] M. Berveiller, A. Zaoui, J. Mech. Phys. Solids 106, 295 (1984).
• [21] R. Hill, J. R. Rice, J. Mech. Phys. Solids. 20, 401 (1972).
• [22] R. Hill, Proc Roy. Soc. London A326, 131 (1972).
• [23] H. J. Bunge, Texture Analysis in Materials Sciences, London, Butterwort (1982).
• [24] T. Ungar, A. Borbely, Appl. Phys. Lett 69, 3173 (1996).