Electrodeposition of catalytically active Ni-Mo alloys

• Autorzy: Mech K. , Żabiński P. , Mucha M. , Kowalik R.

Warianty tytułu

PL

Elektroosadzanie aktywnych katalitycznie stopów Ni-Mo

• Języki publikacji: EN

Abstrakty

EN

The work presents results of researches over the deposition of Ni-Mo alloys through the electrolysis conducted in galvanostatic conditions. In order to improve adhesion and aesthetic properties of the deposited alloys, SLS was added to the bath as a surface active agent. The influence of electrolyte pH was tested as well as concentrations of particular components on the composition, structure, cathodic current efficiency of the electrolysis process and catalytic activity of alloys in the process of hydrogen evolution. A positive influence of addition of molybdenum on catalytic activity was observed occurring in lowering the Tafel’s slope within the activation control range from 122 mV/dec (Ni) to 21 mV/dec (Ni-28.5Mo) for a reaction of water molecules reduction in 8 M NaOH at 90°C.

PL

W pracy zaprezentowano wyniki badań nad otrzymywaniem stopów Ni-Mo na drodze elektrolizy prowadzonej w warunkach galwanostatycznych. Celem poprawy przyczepności oraz walorów estetycznych otrzymywanych stopów do kąpieli dodano SLS w roli środka powierzchniowo czynnego. Przebadano wpływ pH elektrolitu oraz stężenia poszczególnych składników na skład, strukturę, katodową wydajność prądowa procesu elektrolizy oraz właściwości katalityczne stopów w procesie wydzielania wodoru. Zaobserwowano pozytywny wpływ dodatku molibdenu na aktywność katalityczną przejawiający się w spadku nachylenia Tafela w zakresie kontroli aktywacyjnej z 122mV/dec (Ni) do 21 mV/dec (Ni-28.5Mo) dla reakcji redukcji cząsteczek wody w 8 M NaOH w 90 C.

Słowa kluczowe

EN

Ni-Mo alloys; electrodeposition; hydrogen evolution reaction

PL

stopy Ni-Mo; elektroosadzanie; wydzielanie wodoru

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 1
• Strony: 227--229
• Opis fizyczny: Bibliogr. 8 poz., rys., tab.

Twórcy

autor

Mech K.

autor

Żabiński P.

autor

Mucha M.

autor

Kowalik R.

• AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Department of Physical Chemistry and Metallurgy of Non - Ferrous Metals, 30-059 Kraków, Al. Mickiewicza 30, Poland

Bibliografia

• [1] A. Brenner, Electrodeposition of Alloys, Academic Press, New York (1963).
• [2] P. R. Zabinski, K. Mech, R. Kowalik, Co-Mo and Co-Mo-C alloys deposited in a magnetic field of high intensity and their electrocatalytic properties, Archives of Metallurgy and Materials 57, 127 (2012).
• [3] P. Żabiński, M. Górski, R. Kowalik, Influence of Superimposed External Magnetic Field onto Electrodeposition of Co-P Alloys for Hydrogen Evolution, Archives of Metallurgy and Materials 54, 1157 (2009).
• [4] P. Prioteasa, F. Golgovici, G. Sbircea, L. Anicai, T. Visan, Electrodeposition, Structure and Corrosion Behaviour of Ni-Mo Alloys from Citrate Aqueous Electrolyte, Rev. Chim-Bucharest 61, 1046 (2010).
• [5] Q. Han, S. A. Cui, N. W. Pu, J. S. Chen, K. R. Liu, X. J. Wei, A study on pulse plating amorphous Ni-Mo alloy coating used as HER cathode in alkaline medium, Int. J. Hydrogen Energ. 35, 5194 (2010).
• [6] R. K. Shervedani, A. Lasia, Study of the hydrogen evolution reaction on Ni-Mo-P electrodes in alkaline solutions, J. Electrochem. Soc. 145, 2219, (1998).
• [7] Y. Zeng, S. W. Yao, X. Q. Cao, H. X. Huang, Z. Y. Zhong, H. T. Guo, Electrodeposition mechanism of Ni-Mo-P alloy in the solution of ammoniac citrate, Chinese J. Chem. 15, 193 (1997).
• [8] Y. Zeng, M. Ma, X. M. Xiao, Z. L. Li, S. X. Lian, S. M. Zhou, Kinetic model of induced codeposition of Ni-Mo alloys, Chinese J. Chem. 18, 29 (2000).