Dielectric and mechanical properties of BaBi2(Nb0.99V0.01)2O9 Ceramics

• Autorzy: Adamczyk M. , Kozielski L. , Pawełczyk M. , Pilch M.

Warianty tytułu

PL

Własności mechaniczne ceramiki BBN domieszkowanej wanadem

• Konferencja: Composites and Ceramic Materials - Technology, Application and Testing (12 ; 16-18 May 2011 ; Białowieża, Poland)
• Języki publikacji: EN

Abstrakty

EN

The BBN ceramics doped by vanadium have been broadly recognized by using nano indentation techniques and ultrasound velocity and measurements. The results affirm that the vanadium admixture significantly improved the mechanical quality of ceramics. Such a small dopant doesn't change the dielectric properties, but we obtain visible increasing of the dielectric permittivity value and shifts the temperature of the ?max to higer values. The vanadium admixture decreased the diffusion degree ? as well as influenced on the parameters characteristic for the relaxor behaviour. Our suggestion is that partial substitution of the smaller vanadium ions into the niobium sites renders for example ordering of the dipoles.

PL

Własności mechaniczne ceramiki BBN domieszkowanej wanadem były szeroko badane przy użyciu zarówno techniki nanoindentacji, jak i pomiaru prędkości rozchodzenia się fal ultradźwiękowych w materiale. Otrzymane wyniki potwierdziły przypuszczenie, że domieszka wanadu znacznie poprawia własności mechaniczne ceramiki. Tak mała ilość domieszki nie wpływa w znaczący sposób na własności dielektryczne ceramiki, jednak wpływ ten jest zauważalny. Mianowicie wzrasta wartość maksymalna przenikalności dielektrycznej przy jednoczesnym przesunięciu odpowiadającej jej temperatury ku wyższym wartością. Ponadto domieszka wanadu powoduje zmniejszenie stopnia rozmycia przejścia fazowego oraz wpływa na własności relaksorowe ceramiki.

Słowa kluczowe

EN

BBN ceramics; mechanical properties; vanadium

PL

ceramika BBN; własności mechaniczne; wanad

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2011
• Tom: Vol. 56, iss. 4
• Strony: 1163--1168
• Opis fizyczny: Bibliogr. 14 poz., rys., tab.

Twórcy

autor

Adamczyk M.

autor

Kozielski L.

autor

Pawełczyk M.

autor

Pilch M.

• Department of Materials Science, University of Silesia, 41-200 Sosnowiec, 2 Śnieżna Str., Poland

Bibliografia

• [1] C. Miranda, M. E. V. Costa, M. Avdeev, A. L. Kholkin, J. L. Baptista, J. Europ. Ceram. Soc. 21, 1303-1306 (2001).
• [2] M. Adamczyk, Z. Ujma, M. Pawełczyk, Journal of Materials Science 41 (16), 531 (2006).
• [3] D. Nuzhnyy, S. Kamba, P. Kuzel, S. Veljko, V. Bovtun, M. Savinov, J. Petzelt, H. Amorin, M. E. Costa, A. L. Kholkin, Ph. Boullay, M. Adamczyk, Physical Review B 74(13), 134105 (2006).
• [4] M. Adamczyk, M. Pawełczyk, Sintering dependence of BaBi2Nb2O9 ceramic properties, Archives of Metallurgy and Marterials 54, 4, 979 (2009).
• [5] C. Karthik, K. B. R. Varma, Materials Science and Engineering B 129, 245 (2006).
• [6] Kaushik Das, C. Karthik, K. B. R. Varma, U. Ramamurty, Journal of Non-Crystalline Solids 354, 3793 (2008).
• [7] L. E. Cross, Ferroelectrics 76, 241 (1987).
• [8] R. Skulski, P. Wawrzała, K. Ćwikiel, D. Bochenek, Journal of Intelligent Material Systems and Structures 18(10), 1049 (2007).
• [9] W. Piekarczyk, D. Kata, J. Lis, K. Galos, The methodology of ultrasonic study of the gres porcelana to tiles, Materiały Ceramiczne/Ceramic Materials 60, 4 208-212 (2008).
• [10] S. M. Blake, M. J. Falconer, M. McCreedy, P. Lightfoot, J. Mater. Chem. 7, 1609 (1997).
• [11] R. Macquart, B. J. Kennedy, T. Vogt, Ch.J. Howard, Phys. Rev. B 66, 2121021 (2002).
• [12] Ismunadar, B. J. Kennedy, J. Mater. Chem. 9, 541 (1999).
• [13] B. J. Kalaiselvi, R. Sridarane, Ramaswamy Murugana, Materials Science and Engineering B 127, 224 (2006).
• [14] W. C. Oliver, G. M. Pharr, J. Mater Res. 19, 3 (2004).