Influence of cobalt admixture on the microstructure and dielectric properties of PFN ceramics

• Autorzy: Bochenek D. , Grabowski F. , Niemiec P.

Warianty tytułu

PL

Wpływ domieszki kobaltu na mikrostrukturę i dielektryczne właściwosci ceramiki PFN

• Konferencja: Composites and Ceramic Materials - Technology, Application and Testing (12 ; 16-18 May 2011 ; Białowieża, Poland)
• Języki publikacji: EN

Abstrakty

EN

Within our work a ceramic of the PFN type was obtained by a single stage method and it was subjected to a cobalt modification in the amount of: 1.0, 2.0, 3.0, 4.0 and 6.0 mol%. Studies of the influence of the cobalt admixture on the crystalline structure, microstructure and ferroelectric properties of PFN ceramics were performed. It was shown that the iso-valence PFN admixing with cobalt had a positive influence on the density and ceramic microstructure. Higher cobalt admixtures (above 1.0 mol%) in PFN eliminate pyrochlore phase formation, and at the same time they reduce maximum electric permittivity values. The ferroelectric to paraelectric phase transition in the modified PFN compositions undergoes diffusion.

PL

W pracy otrzymano ceramikę typu PFN metodą jednoetapowej syntezy, modyfikowaną kobaltem w ilości: 1,0, 2,0, 3,0, 4,0 i 6,0% mol. Przeprowadzono badania wpływu domieszki kobaltu na strukturę krystaliczna, mikrostrukture i podstawowe właściwości ceramiki typu PFN. Wykazano, że izowalencyjne domieszkowanie PFN kobaltem wpływa pozytywnie na gęstość i mikrostrukturę ceramiki. Większe ilości domieszki kobaltu (pow. 1,0%mol) w PFN eliminują powstawanie fazy pirochlorowej, a jednocześnie zmniejszają wartości maksymalnej przenikalności elektrycznej. Przemiana fazowa z ferroelektrycznej do paraelektrycznej fazy, w modyfikowanych składach PFN, ulega rozmyciu.

Słowa kluczowe

EN

multiferroics; smart materials; ferroelectromagnetics; PFN ceramics

PL

materiały inteligentne; PFN

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2011
• Tom: Vol. 56, iss. 4
• Strony: 1071--1071
• Opis fizyczny: –-1076, Bibliogr. 14 poz., rys.

Twórcy

autor

Bochenek D.

autor

Grabowski F.

autor

Niemiec P.

• Department of Materials Science, University of Silesia, 41-200 Sosnowiec, 2 Śnieżna Str., Poland

Bibliografia

• [1] S. B. Majumder, S. Bhattacharyya, R. S. Katiyar, A. Manivannan, P. Dutta, M. S. Seehra, Journal of Applied Physicss 99, 024108 (2006).
• [2] D. Bochenek, Z. Surowiak, J. Krok-Kowalski, J. Poltierova-Vejpravova, Journal of Electroceramics 25, 122 (2010).
• [3] D. Khomskii, Physics 2, 20 (2009).
• [4] O. Raymond, R. Font, N. Suarez, J. Portelles, J. M. Siqueiros, Ferroelectrics 294, 141 (2003).
• [5] H. Brunckova, L. Medvecky, J. Mihalik, Journal of European Ceramic Society 28, 123 (2008).
• [6] D. Bochenek, R. Zachariasz, Archives of Metallurgy and Materials 54, 903 (2009).
• [7] D. Bochenek, Z. Surowiak, Journal of Alloys and Compounds 480, 732 (2009).
• [8] K. Singh, S. A. Band, W. L. Kinge, Ferroelectrics 306, 179, (2004).
• [9] M. H. Lente, J. D. S. Guerra, G. K. S. de Souza, B. M. Fraygola, C. F. V. Raigoza, D. Garcia, J. A. Eiras, Physical Review B 78, 054109 (2008).
• [10] Z. Surowiak, D. Bochenek, Materiały ceramiczne/Ceramic Materials 4, 124 (2004).
• [11] K. Osińska, J. Maszybrocka, J. Plewa, D. Czekaj, Archives of Metallurgy and Materials 54, 911 (2009).
• [12] B. Wodecka-Duś, D. Czekaj, Archives of Metallurgy and Materials 54, 923 (2009).
• [13] D. Bochenek, Z. Surowiak, Physica Status Solidi A 206, 12, 2857 (2009).
• [14] O. Raymond, R. Font, N. Suarez, J. Portelles, J. M. Siqueiros, Ferroelectrics 294, 141 (2003).