Influence of metallic die temperature in the solidification of Cu-10%Al-2%Fe alloy

• Autorzy: Cenoz I.

Warianty tytułu

PL

Rola temperatury odlewania ciśnieniowego w trakcie krystalizacji stopu Cu-10%Al-2%Fe

• Języki publikacji: EN

Abstrakty

EN

The phases obtained in copper aluminium bronze alloy (Cu-Al10-Fe2) cast into a permanent die were investigated. The parameters examined were the pre-heating temperatures of the die and the graphite coating thickness. The phases α and γ2 were detected as well as the metastable phases β' and γ'. The intermetallics of the system Fe-Al were obtained in various stoichiometric compositions. The different cooling rates of the casting resulted in two mechanisms of transformation to α grains out of the unstable β phase, one being nucleation and growth producing needle shaped α grains, the other exhibiting a massive transformation to spherical α grains. These two mechanisms determine the changes in the size of the α grains as a result of changes in the cooling rate in its various ranges.

PL

Zbadane zostały fazy brązu aluminiowego (Cu-Al10-Fe2) odlewanego ciśnieniowo w sposób ciągły. Kontrolowanymi parametrami była temperatura wstępnego ogrzewania kokili oraz grubość powłoki grafitowej. Stwierdzono występowanie faz α i γ2, metastabilnych faz β' oraz γ', podobnie jak stechiometrycznych faz międzymetalicznych o różnych składach z układu Fe-Al. Różne prędkości chłodzenia odlewu powodowały występowanie dwóch mechanizmów transformacji fazy α, nie związanych z niestabilną fazę β - jednego w formie zarodkowania i wzrostu igiełkowatych ziaren α oraz drugiego, poprzez występowanie masywnej przemiany do kulistych ziaren ?. Mechanizmy te wywoływały zmiany wielkości α - ziaren jako rezultat zmian szybkości chłodzenia ustalanego w różnych zakresach.

Słowa kluczowe

EN

aluminium bronze; metallography; cooper; iron die

PL

brąz aluminiowy; metalografia; odlewanie ciśnieniowe

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2010
• Tom: Vol. 55, iss. 4
• Strony: 1029--1033
• Opis fizyczny: Bibliogr. 9 poz., rys.

Twórcy

autor

Cenoz I.

• Department of Mech. Eng., Energy and Materials, Public University of Navarre, Spain

Bibliografia

• [1] I. Cenoz, J. Fernandez, Rev. Metal. Madrid 43, 272-283 (2007).
• [2] V. Callcut, Metallurgy of copper and copper alloys, aluminium bronze, Part 1, The copper page innovations, The Copper Development Association Inc., USA 3-6 (2002).
• [3] C. M. Friend, Scr. Metall. 23, 1.817-1.820 (1989).
• [4] W. S. Li, Z. P. Wang, Y. Lu, Y. H. Jin, L. H. Yuan, Y F. Wang, Wear 261, 155-163 (2006).
• [5] M. Kaplan, A. K. Yildiz, Mater. Lett. 57, 4.402-4.411 (2003).
• [6] A. Al-Hashem, Y. W. Riad, Mater. Carácter. 48, 37-41 (2002).
• [7] M. Eddahbi, Y. O. A. Ruano, Rev. Metal. Madrid 41, 251-257 (2005).
• [8] A. Monsalve, R. Morales, Rev. Metal. Madrid 40, 431-435 (2004).
• [9] E. Van Der Heide, E.D. Stam, H. Giraud, G. Lovato, N. Akdut, F. Clarisse, P. Caenen, E.I. Heikilla, Wear 261, 68-7 (2006).