Odporność na zużycie ścierne wybranych gatunków stali spiekanej
Języki publikacji
Abstrakty
In this work, the influences of the processing conditions (applied load, cooling rate) on the wear resistance of sintered steels were presented. The wear behaviour of various sintered steels, including Astaloy LH, Astaloy CrL, Distaloy AE, PASC60, 316 L and 430 L were carried out by a pin-on-disk test. The effect of chemical composition and different applied loads in vacuum furnace related to a wear resistance (mass loss versus sliding distance) was investigated. The results showed that the microstructure constituents along with relevant hardness values represent an important parameter affecting the wear behaviour of sintered steels and the sinter hardening is suitable heat treatment for improving the wear resistance of sintered steels.
W pracy przedstawiono wpływ parametrów wytwarzania (ciśnienia prasowania, szybkości chłodzenia) na zużycie ścierne stali spiekanych. Mechanizm zużycia ściernego różnych typów stali określono przy użyciu testu pin-on-disk. Zbadano wpływ składu chemicznego oraz ciśnienia prasowania podczas spiekania w próżni na odporność na zużycie ścierne (ubytek masy w funkcji drogi tarcia). Wyniki badań wykazały, że składniki strukturalne wraz z ich charakterystyczną twardością stanowią ważny czynnik wpływający na mechanizm zużycia ściernego, a zastosowanie obróbki cieplnej typu "sinter hardening" jest właściwe dla polepszenia odporności na użycie ścierne stali spiekanych.
Wydawca
Czasopismo
Rocznik
Tom
Strony
623--629
Opis fizyczny
Bibliogr. 20 poz., rys., tab.
Twórcy
autor
autor
autor
autor
autor
- TECHNICAL UNIVERSITY OF KOSICE, FACULTY OF METALLURGY, LETNA 9, 042 00 SLOVAKIA
Bibliografia
- [1] T. Kvackaj, Acta Metallurgica Slovaca, 8, 2, 100-108 (2002).
- [2] C. H. Caceres, Metallurgical and Materials Transactions A, 38, 7, 1649-1662 (2007).
- [3] J. Bidulska, T. Kvackaj, R. Bidulsky, M. Actis Grande, High Temperature Materials and Processes 27, 3, 203-207 (2008).
- [4] T. Kvackaj, I. Pokorny, Metalurgija 41, 1, 37-42 (2002).
- [5] J. Kusnierz, M. H. Mathon, J. Dutkiewicz, T. Baudin, Z. Jasienski, R. Penelle, Archives of Metallurgy and Materials 50, 2, 367-377 (2005).
- [6] T. Kvackaj, L. Sokolova, M. Vlado, V. Vrchovinsky, High Temperature Materials and Processes 24, 2, 139-144 (2005).
- [7] D. L. Schaefer, C. J. Trombino, In: Advances in Powder Metallurgy & Particulate Materials, Metal Powders Industries Federation, Princeton, NJ 1, 11-17 (2003).
- [8] http://www.ametekmetals.com/metal-powder/ automotive.cfm 1.12.2008.
- [9] I. Cremer, In: Proceedings EURO PM 2007, plenary presentation, Toulouse, EPMA, Shewsbury, 1-28 (2007).
- [10] A. Danielson, In: Proceedings EURO PM 2007, plenary presentation, Toulouse, EPMA, Shewsbury, 1-11 (2007).
- [11] J. Tengzelius, Metal Powder Report 62, 5, 20-21 (2007).
- [12] S. Philippon, G. Sutter, A. Molinari, Wear 257, 7-8, 777-784 (2004).
- [13] M. Sulowski, K. Faryj, Archives of Metallurgy and Materials 54, 1 121-127 (2009).
- [14] R. Bidulsky, M. Actis Grande, High Temperature Materials and Processes 27, 4, 249-256 (2008).
- [15] R. Bidulsky, M. Actis Grande, J. Bidulska, M. Vlado, T. Kvackaj, High Temperature Materials and Processes 28, 3, 175-180 (2009).
- [16] R. Bidulsky, M. Actis Grande, J. Bidulska, T. Kvackaj, Materiali in Tehnologije 43, 6, 303-307 (2009).
- [17] Z. Yang, M. G. S. Naylor, D. A. Rigney, Wear 105, 1, 73-86 (1985).
- [18] G. D. Straffelini, A. Trabucco, A. Molinari, Metallurgical and Materials Transactions A 33, 3, 613-624 (2002).
- [19] N. Candela, R. Plaza, M. Rosso, F. Velasco, J. M. Torralba, Journal of Materials Processing Technology 119, 1-3, 7-13 (2001).
- [20] K. V. Sudhakar, P. Sampathkumaran, E. S. Dwarakadasa, Wear 242, 1-2, 207-212 (2000).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BSW3-0092-0001