Tensile Strength and Microstructure in Directionally Crystallized Al-CuAl2 Eutectic Alloy

• Autorzy: Góral A. , Jura J. , Piątkowski A.

Warianty tytułu

PL

Wytrzymałość na rozciąganie i mikrostruktura eutektycznego stopu Al-CuAl2 krystalizowanego kierunkowo

• Języki publikacji: EN

Abstrakty

EN

In the study the morphology and the microtexture developed in the eutectic Al-CuAl2 alloy obtained at three different rates of the directional crystallization were investigated in correlation with the tensile strength changes. The orientations of (Al) and CuAl2 phases in the piane perpendicular to the direction of crystallization and the orientation relationships in the areas near the Al/CuAl2 interface were determined using the orientation mapping with the application of the formalisms of a quantitative texture analysis. The observed morphology and microstructure were dependent on the crystallization ratę. Tensile strength was found to increase with the increasing crystallization rate.

PL

W pracy analizowano morfologię oraz mikroteksturę w korelacji ze zmianami wytrzymałości na rozciąganie eutektycznego stopu Al-CuAl2 otrzymanego w procesie kierunkowej krystalizacji z trzema różnymi prędkościami. Przy wykorzystaniu mikroskopii orientacji oraz formalizmów ilościowej analizy tekstur określono orientację faz (Al) i CuAl2 w płaszczyźnie prostopadłej do kierunku krystalizacji oraz relacje orientacji faz przy powierzchni międzyfazowej Al/Cu Al2. Stwierdzono, że wzrost prędkości krystalizacji powoduje podwyższenie wytrzymałości na rozciąganie.

Słowa kluczowe

EN

eutectic alloy; tensile strength; microstructure; Al-CuAl2

PL

stop eutektyczny; wytrzymałość na rozciąganie; mikrostruktura; Al-CuAl2

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2010
• Tom: Vol. 55, iss. 1
• Strony: 281--285
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Góral A.

autor

Jura J.

autor

Piątkowski A.

• INSTITUTE OF METALLURGY AND MATERIALS SCIENCE, POLISH ACADEMY OF SCIENCES, 30-059 KRAKÓW, 25 REYMONTA ST., POLAND

Bibliografia

• [1] R. W. Kraft, D. L. Albright, Micro struture of unidirectionally solidified AI-G1AI2 eutectic. Transaction of the Metallurgical Society of AIME 221, 95-102 (1961).
• [2] R. W. Kraft, D. L. Albright, Crystallography of equilibrium phase interfaces in AI-CUAI2 eutectic al-loys. Transactions of Metallurgical Society of AIME 224, 65-74 (1962).
• [3] A. Goral, J. Jura, E. Bouzy, M. Bieda, L. Lityńska-Dobrzyńska, Effect of directional crystallization ratę on microtexture of AI-CUAI2 eutectic alloy. Archives of Metallurgy and Materials 51, 565-368 (2006).
• [4] R. W. Hertzberg, F. D. Lemkey, J. A. Ford, Mechanical behavior of lamellar (AI-G1AI2) and whisker type (Al-A13Ni) unidirectionally-solidified eutectic alloys. Transactions of the Metallurgical Society of AIME 233, 342-354 (1965).
• [5] A. S. Yue, R W. Crossman, Vidoz, M. I. Jacobson, Controlled microstructures of Al-CuA12 eutectic composities and their compressive properties. Transactions of the Metallurgical Society of AIME 242, 2441-2451 (1968).
• [6] P. K. Skiff, N. Stoloff, The influence of growth speed, orientation and emdronment on fracture of aligned Al-CuAl2. Scripta Metallurgica 11, 7-12 (1977).
• [7] F. W. Crossman, A. S. Yue, A. E. Vidoz, Tensile properties of unidirectionally solidified Al-CuAl2 eutectic composites. Transactions of the Metallurgical Society of AIME 245, 397-406 (1968).
• [8] N. A. El-Mahallawy, M. A. Taba, Structure and mechanical properties of Al-40%Cu directionally solidified alloy. Z. Werksofftech 8, 340-343 (1977).
• [9] E. R. Thompson, Lemkey, Directionally solidified eutectic superalloys. Mettalic Matrix Composites 4, 124-134 (1974).