The Influence of Temperature and Time of Exhibition on a Change of Al-Si Coating Thickness and Surface Texture on the Steel Plates

• Autorzy: Żaba K.

Warianty tytułu

PL

Wpływ temperatury i czasu ekspozycji na zmianę grubości i struktury geometrycznej powierzchni powłoki siluminowej na stalowych taśmach

• Języki publikacji: EN

Abstrakty

EN

The paper presents the results of the testing of the influence of temperaturę and time of heat treatment of aluminized steel plates on the change of the Al-Si thickness, Al-Fe-Si inter-metallic layer thickness and the geometrical structure of the coating surface. Also, tests on the influence of heat treatment on the changes in the surface appearance such as partial or total graying and dulling due to iron diffusion to the coating surface have been conducted. Characteristics showing the dependence of temperaturę on the speed with which initial and total changes in the appearance of the surface coating occur have been madę. Tests have been conducted on samples of DX52D+AS120 aluminized steel plate with the surface coating thickness of ca 20 [im, before and after heat treatment in temperaturę 250-700° C within 1 - 10620min. Eąuipment for non-destructive measurements of coatings thickness and roughness has been used in these tests. A digital camera, an optical microscope and a scanning electron microscope have been used to show surface changes after heat treatment.

PL

W artykule przestawiono wyniki badań wpływu temperatury i czasu obróbki cieplnej, aluminiowanych taśm stalowych, na zmianę grubości powłoki Al.-Si, grubości warstwy międzymetalicznej Al.-Fe-Si oraz struktury geometrycznej powierzchni powłoki. Dodatkowo przeprowadzono badania wpływu obróbki cieplnej na zmianę wyglądu powierzchni powłoki, w postaci częściowego lub całkowitego jej zszarzenia i zmatowienia na skutek dyfuzji żelaza do powierzchni powłoki. Opracowano charakterystyki przedstawiające zależności wpływu temperatury na szybkość pojawienia się początkowych i całkowitych zmian wyglądu powierzchni powłoki. Doświadczenia prowadzono na próbkach z aluminiowanej taśmy stalowej z gatunku DX52D+AS120, o grubości powłoki ok. 20 [im, w stanie przed i po obróbce cieplnej, w temperaturze 250-700°C, w czasie 1 - 10620 minut. W badaniach wykorzystano przyrządy do nieniszczących pomiarów grubości i chropowatości powłok. Do zobrazowania zmian powłoki po obróbce cieplnej wykorzystano cyfrowy aparat fotograficzny, mikroskop optyczny i skaningowy mikroskop elektronowy.

Słowa kluczowe

EN

aluminized steel plate; coatings; thickness; inter-metallic layer; roughness; surface

PL

aluminiowana taśma stalowa; powłoki; warstwy międzymetaliczne; powierzchnia; chropowatość

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2010
• Tom: Vol. 55, iss. 1
• Strony: 151--162
• Opis fizyczny: Bibliogr. 14 poz., rys., tab.

Twórcy

autor

Żaba K.

• Faculty of Non-Ferrous Metals, AGH University of Science and Technology, 30-059 Kraków, 30 Mickiewicza Str., Poland

Bibliografia

• [1] ASM Handbook: Surface Engineering, ASM International, Handbook Committee 5, 346 (1994).
• [2] ASTM A463/A463M - 06.
• [3] EN 10346:2009.
• [4] Y. Inoue, M. Kikuchi, Nippon Steel Technical Report 88, 62-69 (2003).
• [5] S. Kobayashi, T. Yakou, Materials Science and Engineering A 338, 1-2, 44-53 (2002).
• [6] M. Suehiro, K. Kusumi, T. Miyakoshi, J. Maki, M. Ohgami, Nippon Steel Technical Report 88, 16-21 (2003).
• [7] W. Chaur-Jeng, Ch. Shih-Ming, Surface and Coatings Technology 200, 22-23, 6601-6605 (2006).
• [8] K. Żaba, S. Nowak, S. Kąc, M. Wróbel, Research on temperaturę time and atmospheric impact on Al-Si coat of low-carbon steel strips, International Conference: Problems of modern techniąues in aspect of engineering and education, Pedagogical University Cracow, Institute of Technology - Cracow, Monography 73-78 (2006).
• [9] K. Żaba, S. Nowak, S. Kąc, Badania stanu powłoki Al.-Si na stalowych taśmach i rurach przeznaczonych na elementy układów wydechowych, poddanej działaniu temperatury 150°C i czasu, Rudy i Metale Nieżelazne R52, 7, 410-418 (2007).
• [10] K. Żaba, Pomiar temperatury w linii technologicznej zgrzewania stalowych rur z powłoką Al-Si, Rudy i Metale Nieżelazne R 52, 8, 473-481 (2007).
• [11] W. Deqing, Applied Surface Science 254, 10, 3026-3032 (2008).
• [12] K. Żaba, S. Kąc, Badania efektów działania wysokiej temperatury, czasu i atmosfery na użytkowe własności powłoki Al-Si na stalowych rurach przeznaczonych na elementy układów wydechowych, Rudy i Metale Nieżelazne R 53, 11, 694-704 (2008).
• [13] K. Żaba, Archives of Civil and Mechanical Engineering 9, 2, 145-152 (2009)
• [14] ISO 4287:1999/AC:2009.