Influence of the Ceramic Moulds Insulation on the Quality of Gas Turbine Blades Made From the Inconel 713C - Nickel-Based Superalloy

• Autorzy: Pieczaba D. , Jach A. , Guzik E. , Sieniawski J.

Warianty tytułu

PL

Wpływ ocieplania form ceramicznych na jakość odlewów łopatek turbiny z nadstopu Inconel 713C

• Języki publikacji: EN

Abstrakty

EN

The influence of mould insulation on the microstructure of the nickel-based superalloy - Inconel 713 C, used in gas turbinę blades, was investigated. Turbinę blade castings were madę in industrial conditions. Three varieties of moulds insulation were used. Based on macroscope, fluorescence (surface defects) and radiographic investigations (internal defects) the quality of the castings was estimated. For selected castings light microscopy observations of cross sections of blades were carried out, as well. The average size and morphology of grains were estimated. It has been found, that the kind of the mould insulation influences the ąuality of castings and should be adjusted to the type of blade.

PL

W pracy ustalono wpływ ocieplenia formy na mikrostrukturę odlewów łopatek turbiny ze stopu Inconel 713C. Wykonano w warunkach przemysłowych odlewy łopatek o szerokości pióra 22 i 30 mm oraz jego długości 50 mm. Stosowano trzy rodzaje ocieplenia form ceramicznych. Jakość odlewów określono na podstawie badań makroskopowych, fluorescencyjnych (wady powierzchniowe) i rentgenowskich (wady wewnętrzne). Dla wybranego odlewu łopatki wykonano badania mikroskopowe. Określono średnią średnicę ziaren i ich rozmieszczenie na przekroju odlewu łopatki. Stwierdzono wpływ sposobu ocieplenia formy na mikrostrukturę pióra łopatek wykonanych ze stopu Inconel 713C. Wyniki badań stanowią podstawę dla dalszych prac dotyczących wpływu ocieplenia form na jakość odlewów łopatek turbin.

Słowa kluczowe

EN

turbine blade; ceramic mould; mould insulation; Inconel 713C; microstructure

PL

łopatki turbiny; forma ceramiczna; forma izolacji; mikrostruktura

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2010
• Tom: Vol. 55, iss. 1
• Strony: 37--43
• Opis fizyczny: Bibliogr. 13 poz., rys., tab.

Twórcy

autor

Pieczaba D.

autor

Jach A.

autor

Guzik E.

autor

Sieniawski J.

• DEPARTMENT OF MATERIAL SCIENCE, THE FACULTY OF MECHANICAL ENGINEERING AND AERONAUTICS, RZESZÓW UNIVERSITY OF TECHNOLOGY, 35-959 RZESZÓW, 2 W POLA STR., POLAND

Bibliografia

• [1] A. Hernas, Żarowytrzymałość stali i stopów. Wydawnictwo Politechniki Śląskiej, Gliwice 2000.
• [2] E. Fraś, Krystalizacja metali. Wydawnictwa Naukowo-Techniczne, Warszawa 2003.
• [3] J. Ryś, Stereologia materiałów. Fotobit - Design, Kraków 2005.
• [4] C. T. Sims, N. S. Stoloff, W. C. Hagel, Super-alloys II. John Wiley & Sons, Inc., New York 1987.
• [5] J. Zych, Analiza wad odlewów. Wydawnictwa Naukowo-Techniczne, Kraków 2004.
• [6] Cz. Adamski, A. Górski, S. Kobyliński, Systematyka wad odlewów metali nieżelaznych. Warszawa, PWT 1956.
• [7] L. Wojnar, K. J. Kurzydłowski, J. Szala, Praktyka analizy obrazu. Polskie Towarzystwo Stereologiczne, Kraków 2002.
• [8] N. Boutarek, D. Saidi, M. A. Acheheb, M. Iggui, S. Bouterfaia, Materials Characterization 59, 951-956 (2008).
• [9] H. Farhangi, S. Norouzi, M. Nili-Ahmadabadi, Journal of Materials Processing Technology 153-154, 209-212 (2004).
• [10] T. Antonsson, H. Fredriksson, Metallurgical and Materials Transactions B 36B, 86-95 (2005).
• [11] D. Pieczba, A. soJach, Ocena mikrostruktury dendrytycznej odlewów łopatek turbin z nadstopu In-conel 713C, Materiały konferencyjne XXVII Szkoły Inżynierii Materiałowej, Kraków-Krynica 2009.
• [12] A. Jach, Wpływ warunków odlewania na strukturę pióra łopatki o szerokości 22 mm, praca dyplomowa, AGH Kraków 2008.
• [13] D. Pieczaba, Wpływ warunków odlewania na strukturę pióra łopatki o szerokości 30 mm, praca dyplomowa, AGH Kraków 2008