Electrodeposition of Ni/SiC composite coating aluminium

• Autorzy: Burzyńska L. , Rudnik E. , Ćwięka K.

Warianty tytułu

PL

Elektrolityczne współosadzania powłok kompozytowych Ni/SiC na aluminium

• Języki publikacji: EN

Abstrakty

EN

A hydrometallurgical method for production of Ni/SiC composite coating on aluminium was developed. The following consecutive stages were proposed: zincating of aluminium substrate for 5 min in alkaline zincate solution, electroless nickel deposition for 1 h by immersion in nickel-acetate solution with sodium hypophosphite as a reductant and, finally, electrodeposition of Ni/SiC composite from a chloride-sulphate bath for 6 h at current density of 1 A/dm2. The stages were essential to achieve good adherence of the multilayer system to the aluminium surface. Microscopic observations showed uniform thickness of the individual layers over cross-sections of the sample. Microhardness of the composite was approx. 770 HV.

PL

Opracowano hydrometalurgiczną metodę wytwarzania powłok kompozytowych Ni/SiC na aluminium. Proces obejmuje następujące główne etapy: nakładanie powłoki cynkowej na aluminium na drodze cementacji w roztworze alkalicznym przez okres 5 min; bezprądowe (autokatalityczne) osadzanie powłoki niklowej przez okres 1 godz. przy użyciu podfosforynu sodu jako reduktora; elektrolityczne współosadzanie powłok kompozytowych Ni/SiC z kąpieli chlorkowo-siarczanowej przez okres 6 godz. przy gęstości prądu 1 A/dm2. Wymienione etapy pozwalają na uzyskanie układu wielowarstwowego o dobrej wzajemnej przyczepności poszczególnych warstw. Obserwacje mikroskopowe przekrojów poprzecznych próbek wykazały tworzenie się warstewek o równomiernej grubości. Mikrotwardość powłoki kompozytowej nałożonej na aluminium wynosiła ok. 770 HV.

Słowa kluczowe

EN

nickel; composite; electrodeposition; aluminium

PL

nikiel; kompozyt; współosadzanie elektrolityczne; aluminium

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2009
• Tom: Vol. 54, iss. 3
• Strony: 845--851
• Opis fizyczny: Bibliogr. 13 poz. rys., tab.

Twórcy

autor

Burzyńska L.

autor

Rudnik E.

autor

Ćwięka K.

• AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, FACULTY OF NON – FERROUS METALS DEPARTMENT OF PHYSICAL CHEMISTRY AND METALLURGY OF NON-FERROUS METALS LABORATORY OF PHYSICAL CHEMISTRY AND ELECTROCHEMISTRY, AL. MICKIEWICZA 30, 30-059 CRACOW, POLAND

Bibliografia

• [1] L. F. Mondolfo, Aluminium alloys: structures and properties, Butter Worths, London, 1976.
• [2] E. Khan, C. F. Oduoza, T. Pearson, J. Appl. Electrochem. 37, 1375-1381 (2007).
• [3] F. Delaunois, J. P. Petitjean, P. Lienard,M. Jacob - Duliere, Surf. Coat.Technol. 124, 201-209 (2000).
• [4] I. Apachitei, J. Duszczyk, Surf. Coat. Technol. 132, 89-98 (2000).
• [5] J. M. Molina, R. A. Saravanan, J. Narciso, E. Louis, Mater. Sci. Eng. A 383, 299-306 (2004).
• [6] E. Rudnik, K. Kokoszka, A. Łapsa, Surf.Coat. Technol. 202, 2584-2590 (2008).
• [7] C. T. J. Low, R. G. A. Wills, F. C. Walsh, Surf.Coat.Technol. 201, 371-383 (2000).
• [8] L. Burzynska, E. Rudnik, L. Błaz, M. Kotula, Z. Sierpiński, W. Szymński, Trans. Inst. Met. Finish. 81(6), 194-199 (2003).
• [9] L. Burzynska, E. Rudnik, J. Koza, L. Błaz, W. Szymanski, Surf. Coat. Technol. 202, 2545-2556(2008).
• [10] S. Rudy, Plat. Surf. Fin. 93(11), 32-51 (2006).
• [11] G. Mallory, J. B. Hajdu, Electroless Plating: Fundamentals And Applications, American Electroplaters and Surface Finishers Society, Norwich, New York, United States, (1996).
• [12] K. M. Gorbunova, A. A. Nikiforova, Fiziko-khimicheskie osnovy processa khimicheskovo nikelirovaniya, 1960, Izd.Akad.Nauk SSSR, Moskow, (In Russian).
• [13] E. Rudnik, J. Gorgosz, Surf. Coat. Technol. 201(16-17), 6953-6959 (2007).