Numerical modeling of the microstructure during 50x20 mm flat bars rolling process

• Autorzy: Stefanik A. , Szota P. , Dyja H.

Warianty tytułu

PL

Numeryczne modelowanie mikrostruktury podczas walcowanie prętów płaskich 50x20 mm

• Języki publikacji: EN

Abstrakty

EN

In this work theoretical analysis of the microstructure change in the material during normalizing rolling of the 50x20 mm flat bars was presented. Theoretical analysis was made with computer program Forge 2007, based on the finite-element method. An analysis was made for two cases of accelerated cooling during rolling process. Based on the numerical results of 50x20 flat bars rolling process the average recrystallized austenite diameter and basic energy and force parameters. Proposed modification of the 50x20 mm flat bars rolling technology involving accelerated cooling, results in the reduction of average austenite diameter, which could cause improving strength of the final product.

PL

W pracy przeprowadzono badania numeryczne, których celem było modelowanie zmian strukturalnych zachodzących w odkształcanym pasmie podczas walcowania normalizującego prętów płaskich 50x20 mm. Badania przeprowadzono przy użyciu programu komputerowego Forge 2007, umożliwiającego modelowanie zmian mikrostruktury. Rozważano dwa warianty przyspieszonego chłodzenia. Na podstawie przeprowadzonych badań procesu walcowania prętów płaskich 50x20 mm określono średnia wielkość zrekrystalizowanego ziarna austenitu oraz podstawowe parametry energhetyczno – siłowe. Zaproponowane midyfikacje technologii walcowania prętów płaskich 50x20 mm polegające na wprowadzeniu dodatkowego przyspieszenia chłodzenia wodnego walcowanego pasma w ciągu walcowniczym powodują zmniejszenie wielkości ziarna austenitu, co wpłynie na zwiększenie wutrzymałości gotowych wyrobów.

Słowa kluczowe

EN

normalizing rolling; accelerated cooling; microstructure

PL

walcowanie normalizujące; przyspieszone chłodzenie; mikrostruktura

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2009
• Tom: Vol. 54, iss. 3
• Strony: 589--596
• Opis fizyczny: Bibliogr. 7 poz., rys.

Twórcy

autor

Stefanik A.

autor

Szota P.

autor

Dyja H.

• CZESTOCHOWA UNIVERSITY OF TECHNOLOGY, FACULTY OF MATERIAL PROCESSING TECHNOLOGY AND APPLIED PHYSICS, INSTITUTE OF MODELLING AND AUTOMATION OF PLASTIC WORKING PROCESSES, UL. ARMII KRAJOWEJ 19, 42-200 CZESTOCHOWA, POLAND

Bibliografia

• [1] B. Koczurkiewicz, The model of prediction of the microstructure austenite C-Mn steel. Archives of materiale science and engineering. 28, 421-424 (2997).
• [2] Forge3 Reference Guide, Realese 6.2, Transvalor S.A. November 2002.
• [3] G. Stradomski, Modelowanie procesów rozwoju mikrostruktury podczas regulowanego walcowania prętów ze stali konstrukcyjnej spawalnej w ciągłej walcowni bruzdowej, Praca doktorska, Politechnika Częstochowska, Częstochowa 2007.
• [4] B. Koczurkiewicz, P. Korczak, H. Dyja, Assesment of the strain history impaction the after-rolling microstructural parameters and mechanical properties of steel. 5th International Conference Form. Brno 2000 s. 179-185.
• [5] C. M. Sellars, Mathematical modeling of hot rolling of steel. Processing Symposium, 1990 s. 1-18.
• [6] P. D. Hodgson,Microstrukture modeling for property prediction and control. Journal of Materials Processing Technology 60, 1996.
• [7] C. Qiu, J. Sietsma, S. Van der Zwaag, Ferrite growth austenite in C - Mn steels during continuous cooling, Ironmaking and Steelmaking 26, 3, 1999.