Microstructure and phase composition of sintered cobalt-iron materials

• Autorzy: Romański A.

Warianty tytułu

PL

Mikrostruktura i skład fazowy spiekanych materiałów kobalt-żelazo

• Języki publikacji: EN

Abstrakty

EN

This paper describes the effect of the sintering parameters, e.g. temperature and atmosphere, on the microstructure and phase composition of the cobalt-iron materials. Investigations were carried out on the specimens made of the mixtures of elemental cobalt and iron powders, containing 3, 6, 10, 15 and 25 wt.% iron addition. Samples were obtained by cold pressing under 400 MPa then sintered at 900 and 1150 °C for an hour. As a sintering atmospheres both flowing, purified hydrogen and nitrogen was used. The obtained results have shown that density of Co-Fe materials strongly depends on iron content, whereas sintering atmosphere has a minor effect on their hardness. Microstructural investigations have shown that applied sintering atmosphere plays a significant role if grain size and cobalt’s phase composition are taken under consideration.

PL

W artykule przedstawiono wyniki badan poświeconych wpływowi parametrów spiekania, tj. temperatury i atmosfery ochronnej na mikrostrukturę i skład fazowy materiałów kobalt-żelazo. Badaniom poddano próbki wykonane z mieszek elementarnych proszków kobaltu i żelaza, zawierających 3, 6, 10, 15 i 25% wag. Fe. Próbki wykonano techniką jednostronnego prasowania pod ciśnieniem 400 MPa i spiekania w temperaturze 900 oraz 1150 °C przez okres 1 godziny. Jako atmosfery ochronne zastosowano zarówno przepływający wodór, jak i azot. Otrzymane wyniki wykazały, że gęstość spieków Co-Fe jest silnie związana z zawartością żelaza, natomiast rodzaj atmosfery spiekania nie ma znaczącego wpływu na ich twardość. Badania strukturalne wykazały natomiast, że rodzaj zastosowanej atmosfery ochronnej ma zasadnicze znaczenie na wielkość ziarna spieków Co-Fe oraz skład fazowy spiekanego kobaltu.

Słowa kluczowe

EN

cobalt-iron materials; sintering; microstructure; phase composition

PL

spiekanie; spieki kobalt-żelazo; mikrostruktura

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2009
• Tom: Vol. 54, iss. 2
• Strony: 449--454
• Opis fizyczny: Bibliogr. 6 poz., rys.

Twórcy

autor

Romański A.

• AGH-UNIVERSITY OF SCIENCE AND TECHNOLOGY, 30-059 KRAKOW, 30 MICKIEWICZA AV., POLAND

Bibliografia

• [1] J. Konstanty, A. Romanski, H. Frydrych, Effect of mechanical properties of the matrix on its diamond retention capacity and wear characteristics during sawing hard stone by means of diamond impregnated tools, PM 2000 Powder Metallurgy World Congress & Exhibition, Kyoto, Japan, part 2, 1629 (2000).
• [2] J. Konstanty, W. Ratuszek, J. Jamrozek, I. Olszewska, Properties of hot pressed near-stoichiometric FeCo alloys, International Journal of Powder Metallurgy 40, 1, 41 (2000).
• [3] J. Konstanty, W. Ratuszek, J. Jamrozek, Microstructures and properties of near-stoichiometric iron-cobalt alloys, World PM 2004 Conference, Vienna, Austria 3, 669 (2004).
• [4] H. Frydrych, A. Romanski, J. Konstanty, The Influence of Iron Content and Powder Metallurgy Processing Route on Microstructure and Mechanical Properties of Cobalt-Iron Materials Archive of Metallurgy, 49, 4, 957 (2004).
• [5] J. Konstanty, A. Bunsch, Hot pressing of cobalt powders, Powder Metallurgy 34, 3, 195 (1991).
• [6] J. Konstanty, A. Bunsch, A. Ciaś, Factors affecting hardness and ductility of hot-pressed cobalt powders, Powder Metallurgy International 23, 6, 354 (1991).