Characteristics of defects present in industrial steel castings due to metal-mould reactions

• Autorzy: Kalandyk B. , Zapała R. , Rakowska A.

Warianty tytułu

PL

Charakterystyka wad powstałych na przemysłowych odlewach staliwnych w wyniku oddziaływania metal-forma

• Języki publikacji: EN

Abstrakty

EN

Studies were made on surface defects formed in industrial steel castings. It has been concluded that the defects are formed due to an interaction between molten metal and moulding sand constituents. The microscopic analysis indicated strong non-homogeneity of the examined defects in respect of both structure and chemical composition. Basing on the examinations carried out under the scanning electron microscope, it was observed that within each defect two characteristic regions could be distinguished. One of them was formed of the silica sand grains, while the other contained a complex oxide phase, the chemical composition of which depended on the type of protective coating and the cast steel grade.

PL

Przeprowadzono badania wad powierzchniowych powstałych na przemysłowych odlewach staliwnych. Stwierdzono, że powstałe wady są rezultatem oddziaływania ciekłego metalu ze składnikami masy formierskiej. Przeprowadzona analiza mikroskopowa wskazuje na silną niejednorodność badanych wad pod względem budowy i składu chemicznego. Na podstawie badań przeprowadzonych z wykorzystaniem elektronowego mikroskopu skaningowego stwierdzono, że w obrębie każdej z nich można wyróżnić dwa charakterystyczne obszary. Jeden z nich tworzą ziarna piasku kwarcowego, natomiast drugi obszar stanowi złożona faza tlenkowa, której skład chemiczny zależy od rodzaju powłoki ochronnej i gatunku staliwa.

Słowa kluczowe

EN

steel casting; casting defects

PL

odlewanie stali; wady odlewów

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2009
• Tom: Vol. 54, iss. 2
• Strony: 289--297
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Kalandyk B.

autor

Zapała R.

autor

Rakowska A.

• DEPARTMENT OF CAST ALLOYS AND COMPOSITE ENGINEERING, FACULTY OF FOUNDRY ENGINEERING AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, 30-059 KRAKÓW, 23 REYMONTA STR., POLAND

Bibliografia

• [1] T. Elbel, K. Stransky, F. Havlicek, P. Jelinek, Vznik sekundarni struskovitosti u ocelovych odlitku; Slevarenstvi 9, 370-380 (1987).
• [2] M. Holtzer, Badanie mechanizmu i stopnia wzajemnego oddziaływania ciekłego staliwa Hadfielda i masy formierskiej, Zeszyty Naukowe, 142, (1992), ISSN 0372-9443.
• [3] L. Lewandowski, Tworzywa na formy odlewnicze, Wydawnictwo Akapit, (1997), ISBN 83-7108-21-2.
• [4] J. Zych, Non-destructive examination of kinetics of phenomena in near-surface layers of wet moduls after their pouring with molten metal, Archives of Foundry 4, 11, 306-316 (2004).
• [5] J. Zych, Miulding sands surface layer – kinetics of the changes its property, Srchives of Foundry 6, 20, 77-84 (2006).
• [6] J. Zych, Analiza odlewów wybrane zagadnienia – labolatorium, Wydawnictwo AGH, (2001), ISSN 0239-6114.
• [7] B. Kalandyk, J. Głownia, Wady wtórnego zażużlenia na przemysłowych odlewach ze staliwa, Archiwum Odlewnictwa 6, 22, 254-259 (2007).
• [8] B. Kalandyk, J. Głownia, E. Olejnik, Identyfikacja zażużleń w odlewach ze staliwa węglowego i niskostopowego, Wyd. Akapit, 45-50 (2007).
• [9] Sprawozdanie z badań statutowych, AGH nr 11.11.170.318, (2007) – niepublikowane.
• [10] B. Kalandyk, R. Zapała, A. Rakowska, Wady powierzchni przemysłowych odlewów ze staliwa Hadfielda, Wyd. Akapit, 37-44 (2008).