Texture inhomogeneity in titanium deformed by ECAP

• Autorzy: Skrotzki W. , Kloden B. , Lankau A. , Chulist R. , Kopylov V. , Brokmeier H.-G.

Warianty tytułu

PL

Niejednorodność tekstury w tytanie odkształconym metodą ECAP

• Konferencja: SOTAMA Symposium on Texture and Microstructure Analysis (2; 26-28.09.2007; Cracow, Poland)
• Języki publikacji: EN

Abstrakty

EN

Titanium of commercial purity was deformed by equal channel angular pressing (ECAP) with back-pressure at 380°C using 4 passes of route Bc. Billets of 120 mm length were pressed at 0.4 mm s -1 through square channels (14 mm x 14 mm) intersecting sharply at an an gle of 90°. The global texture measurements of the starting and ECAP processed material were done by neutron diffraction. To investigate the texture inhomogeneity after ECAP the local texture was measured with high-energy synchrotron radiation at different positions in the cross-section of the billet. The texture gradient with regard to intensity and orientation of the dominant texture component is characterized and discussed.

PL

Tytan o czystości przemyslowej (klasa 2) zostal odkształcony w procesie wyciskania w kanale kątowym (ECAP) z przeciwciśnieniem w temperaturze 380°C w 4 przepustach wg. drogi BC. Wlewki 120 mm długości byly wyciskane przy predkości 0.4 mm s-1 przez prostokątny kanał kwadratowy (14 x 14 mm2 ). Pomiary tekstury globalnej w materiale wejściowym i po odkształceniu wykonano metodą dyfrakcji neutronów. Aby zbadać niejednorodność tekstury po odksztalłeniu zmierzono tekstury lokalną przy wykorzystaniu promieniowania synchrotronowego o wysokiej energii w różnych obszarach przekroju poprzecznego wlewka. Wskazane zostały zalety tej metody ujawnienia gradientu tekstury. Omówione zostały intensywności odchylenia dominujących składowych tekstury w odniesieniu do ich idealnych położeń wynikających z prostego ścinania.

Słowa kluczowe

EN

titanium; equal-channel angular pressing (ECAP); microstructure; texture; inhomogeneity

PL

tytan; proces wyciskania w kanale kątowym (ECAP); mikrostruktura; tekstura; niejednorodność

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2008
• Tom: Vol. 53, iss. 1
• Strony: 29--32
• Opis fizyczny: Bibliogr. 12 poz., rys.

Twórcy

autor

Skrotzki W.

autor

Kloden B.

autor

Lankau A.

autor

Chulist R.

autor

Kopylov V.

autor

Brokmeier H.-G.

• INSTITUT FUR STRUKTURPHYSIK, TECHNISCHE UNIVERSITAT DRESDEN, D-01062 DRESDEN, GERMANY

Bibliografia

• [1] R. Z. Valiev, T. G. Langdon, Principles of equal channel angular pressing as a processing tool for grain refinement. Prog. Mater. Sci. 51, 881-981 (2006).
• [2] W. Skrotzki, N. Scheerbaum, C.-G. Oertel, R. Arruffat-Massion, S. Suwas, L.S. Tóth, Microstructure and texture gradient in copper deformed by equal channel angular pressing. Acta Mater. 55, 2013-2024 (2007).
• [3] W. Skrotzki, N. Scheerbaum, C.-G. Oertel, H.-G. Brokmeier, S. Suwas, L.S. Tóth, Recrystallization of high-purity aluminium during equal channel angular pressing. Acta Mater. 55, 2211-2218 (2006).
• [4] V. I. Kopylov, Application of ECAP-technology for producing nano- and microcrystalline materials. In: Investigations and Applications of Severe Plastic Deformation, T. C. Lowe and R.Z. Valiev (eds.), Kluwer Academic Publishers, Netherlands, 23-27 (2000).
• [5] H.-G. Brokmeier, Texturanalyse mittels winkeldispersiver neutronographischer Kernstreuung, Habilitation thesis, TU Clausthal (1995).
• [6] W. Skrotzki, B. Klöden, R. Tamm, C.-G. Oertel, U. Garbe, E. Rybacki, Torsion texture measurements with high-energy synchrotron radiation on NiAI. Textures Microstruct. 35, 163-173 (2003).
• [7] A. K. Singh, R. A. Schwarzer, Texture and anisotropy of mechanical properties in titanium and its alloys. Z. Metallkd. 91, 702-716 (2000).
• [8] S. H. Yu, D. H. Shin, S. K. Hwang, Evolution of grain boundary character distribution in ECA-pressed pure titanium. In: Ultrafine Grained Materials III, Y.T. Zhu, T.G. Langdon, R.Z. Valiev, S.L. Semiatin, D.H. Shin and T.C. Lowe (eds.), TMS (The Minerals, Metals & Materials Society) 227-234 (2004).
• [9] J. Bonarski, I. A. Alexandrov, Severely plastically deformed Ti from the standpoint of texture changes. In: Nanomaterials by Severe Plastic Deformation, M.J. Zehetbauer and R.Z. Valiev (eds.) Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim 309-314 (2004).
• [10] L. Tóth, Texture evolution in severe plastic deformation by equal channel angular extrusion. Adv. Eng. Mat. 5, 308-316 (2003).
• [11] B. Beausir, L. S. Tóth, K. W. Neale, Ideal orientations and persistence characteristics of hexagonal close packed crystals in simple shear. Acta Mater. 55, 2695-2705 (2007).
• [12] B. Beausir, S. Suwas, L. S. Tóth, K. W. Neale, J.-J. Fundenberger, Analysis of texture evolution in magnesium during equal channel angular extrusion. Acta Mater. (2007), in press.