Thermal stability and behaviour during compression of the Cu68:5Ni12P19:5 alloy

• Autorzy: Ziewiec K. , Kurtyka P. , Bryła K. , Kąc S.

Warianty tytułu

PL

Stabilność cieplna i przebieg procesu prasowania stopu Cu68;5Ni12P19;5

• Języki publikacji: EN

Abstrakty

EN

Copper-nickel-phosphorus Cu68:5Ni12P19:5 alloy was cast using melt spinning with a linear rate of 23 m/s (approximate cooling rate 105 K/s). In order to study the thermal stability of the metallic glass the ribbon in the as-cast state was tested by DSC and X-ray diffraction at different temperatures. Then the as-cast melt-spun ribbon was preliminarily compacted using 60 MPa to form 5 g samples. After pre-pressing, the samples were compressed between plates at different temperatures and stresses required for a given deformation were assessed. In order to find the progress of consolidation the cross-sections were studied using SEM and EDS. It was found that at higher compression temperatures the samples were consolidated with the presence of the crystalline phases.

PL

Stop miedź-nikiel-fosfor Cu68;5Ni12P19;5 odlewano koło wirujące s liniową prędkością 23 m/s (szacunkowa szybkość chłodzenia 105 K/s). W celu zbadania stabilności termicznej taśmy z otrzymanego szkła metalicznego w stanie po odlewaniu zastosowano różnicową kalorymetrię skaningową (DSC), przeprowadzono rentgenowskie pomiary dyfraktometryczne przy różnych temperaturach. Następnie taśma w stanie po odlewaniu na wirujące koło była wstępnie prasowana przy użyciu 60 MPa w celu uzyskania 5 gramowych próbek. Po wstępnym prasowaniu, próbki były prasowane pomiędzy płytami maszyny wytrzymałościowej, przy różnych temperaturach oraz oszacowano naprężenia wymagane do odkształcenia próbki o ustaloną wartość. W celu zbadania przebiegu konsolidacji wykonano badania przekrojów poprzecznych prasowanych próbek przy użyciu skaningowego mikroskopu elektronowego (SEM) wyposażonego w EDS. Stwierdzono, że przy wyższych temperaturach prasowania próbki zostały skonsolidowane, a w ich strukturze stwierdzono występowanie faz krystalicznych.

Słowa kluczowe

EN

compression; DSC; copper-nickiel-phosphorus alloy; thermal stability

PL

prasowanie; DSC; stop miedź-nikiel-fosfor; stabilność cieplna

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2007
• Tom: Vol. 52, iss. 1
• Strony: 73--76
• Opis fizyczny: Bibliogr. 12 poz., rys.

Twórcy

autor

Ziewiec K.

autor

Kurtyka P.

autor

Bryła K.

autor

Kąc S.

• Faculty of Mathematics, Physics and Technical Sciences, Pedagogical University, 30-084 Kraków, Podchorążych 2 Str., Poland

Bibliografia

• [1] H. Warlimont, Materials Science and Engineering A304-306, 61-61 (2001).
• [2] T. Masumoto, Materials Science and Engineering A181-182, 8 (1994).
• [3] T. Kulik, Journal of Non-Crystalline Solids 287, 145-161 (2001).
• [4] W. L. Johnson, MRS Bull., Oct. 42-56 (1995).
• [5] A. Inoue, A. Takeuchi, B. Shen, Mater. Trans. 6, 42 (2001).
• [6] K. Ziewiec, R. Gajerski, J. Dutkiewicz, J. Król, METALLURGY AND FOUNDRY ENGINEERING 28, 2, 149-156 (2002).
• [7] K. Ziewiec, P. Olszewski, R. Gajerski, A. Małecki, Journal of Alloys and Compounds, 373, 115-121 (2004).
• [8] JCPDS-International Centre for Diffraction Data v. 2.00, (1998).
• [9] Y. K awamura, T. Shibata, A. Inoue, T. Masumoto, Acta materialia 46, 253-263 (1998).
• [10] Y. Kawamura, Y. Ohno, Scripta Materialkia 45, 279-285 (2001).
• [11] M. H. Lee, D. H. Bae, W. T. Kim, D. H. Kim, E. Roshkova, P. B. Wheelock, D. J. Sordelet, Journal of Non-Crystalline Solids 315, 89-96 (2003).
• [12] D. J. Sordelet, E. Roshkova, M. F. Besser, M. J. Kramer, Journal of Non-Crystalline Solids 317, 137-143 (2003).