Calculations of oxide inclusions composition in the steel deoxidized with Mn, Si and Ti

• Autorzy: Podorska D. , Drożdż P. , Falkus J. , Wypartowicz J.

Warianty tytułu

PL

Obliczanie składu wydzieleń tlenkowych w stali odtlenianej przy pomocy Mn, Si i Ti

• Języki publikacji: EN

Abstrakty

EN

The work deals with the determination of the composition of liquid oxide solution MnO-SiO2-TiO2-Al2O3, present as an inclusion in liquid steel during its solidification. The region of compositions at which oxide solution remains entirely liquid at the temperatures 1523 K and 1673 was calculated by means of FACT program. The evolution of oxide phase chemical composition in thermodynamic equilibrium with liquid steel during its equilibrium solidification was calculated. The procedure of calculations may be applied in the determination of the conditions for acicular ferrite formation, which nucleates at oxide inclusions.

PL

Praca zajmuje się określeniem zmian składu ciekłego roztworu tlenkowego MnO-SiO2-TiO2-Al2O3 znajdującego się w postaci wtracenia w ciekłej stali w trakcie jej krzepnięcia. Obliczono przy pomocy programu FACT zakres składów roztworu tlenkowego, przy jakim pozostaje on całkowicie ciekły przy temperaturach 1523 i 1673 K. Wyznaczono ewolucje składu chemicznego fazy tlenkowej pozostającej w równowadze termodynamicznej z ciekłą stalą w trakcie jej równowagowego krzepnięcia. Procedura obliczeniowa może być zastosowana do określania warunków tworzenia ferrytu iglastego zarodkującego na wydzieleniach tlenkowych.

Słowa kluczowe

EN

steel deoxidisation; solidification; oxide inclusions; thermodynamic equilibrium; acicular ferrite

PL

stal odtleniana; krzepnięcie; wydzielenia tlenkowe; równowaga termodynamiczna; ferryt iglasty

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2006
• Tom: Vol. 51, iss. 4
• Strony: 581--586
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Podorska D.

autor

Drożdż P.

autor

Falkus J.

autor

Wypartowicz J.

• Faculty of Metals Engineering and Industrial Informatics, AGH University of Science and technology, 30-059 Kraków, 30 Mickiewicza Ave, Poland

Bibliografia

• [1] F. Ishikawa, T. Takahashi, T. Ochi, Met. Mater. Trans. A 25A, 929-936 (1994).
• [2] J. M. Gregg, H. K. Bhadeshia, Acta Mater. 45, 739-748 (1997).
• [3] I. Madriaga, J. L. Romero, I. Gutierrez, Met. Mater. Trans. A 29A, 1003-1015 (1998).
• [4] J.-H. Shim,Y. W. Cho, S. H. Chung, J.-D. Shim, D. N. L e e, Acta Mater. 47, 2751-2760 (1999).
• [5] H. S. Kim, H.-G. Lee, K.-S. Oh, Met. Mater. Trans. A 32A, 1519-1525 (2001).
• [6] K. Oikawa, K. Ishida, T. Nishizawa, ISIJ Int. 37, 332-338 (1997).
• [7] M. Ohta, N. Sano, K. Morita, ISIJ Int. 40, Suppl. S87-S91 (2000).
• [8] Z. Ma, D. Janke, ISIJ Intern. 38, 46-52 (1998).
• [9] M. Suzuki, R. Yamaguchi, K. Murakami, M. Nakada, ISIJ Int. 41, 247-256 (2001).
• [10] J. Wypartowicz, D. Podorska, Hutnik - Wiadomości Hutnicze 73, 91-96 (2006).