Phase and structural transformations in Ti-Ta alloys in wide region of compositions

• Autorzy: Dobromyslov A. V. , Dolgikh G. V. , Dutkiewicz J. , Trenogina T. L.

Warianty tytułu

PL

Przemiany fazowe i strukturalne w stopach Ti-Ta w szerokim zakresie składów

• Języki publikacji: EN

Abstrakty

EN

Optical microscopy, X-ray diffraction, transmission electron microscopy, and hardness measurements were used to study the structure of quenched Ti-Ta alloys containing 1-40 at.% tantalum. Two martensitic phases, Α' and Α'', are formed in quenched Ti-Ta alloys. The type of martensite crystal structure is determined by the composition of the alloy. The Α'-phase is formed in the alloys containing up to 10 at.% tantalum. The orthorhombic Α''-phase was found in the alloys containing 15-30 at.% Ta. The concentration dependence of the lattice parameters of the Α''-phase is given. Omega-phase precipitation were not found in quenched alloys. The alloys of 35-40 at.% Ta consist of metastable Β-phase only upon quenching. The electron diffractions patterns of the Ti-Ta alloys containing from 25 to 35 at.% tantalum exhibit diffuse scattering. It was established that stress-induced {110}Β and {332}Β twinning appeared in metastable Β-phase.

PL

Struktury stopów Ti-Ta zawierających 1-40% at. Ta badano metodami mikroskopii optycznej, dyfrakcji rentgenowskiej i transmisyjnej mikroskopii elektronowej. Dwie fazy martenzytyczne Α' i Α'', zidentyfikowano w tych stopach. Rodzaj struktury martenzytu zależy w pierwszym rzędzie od składu chemicznego. Faza Α' tworzy się w stopach zawierających do 10% at. Ta, a fazę ortorombową Α'' zidentyfikowano w stopach zawierających 15-30% at. Ta. Zmierzono zależność parametru fazy Α od składu chemicznego. Nie zidentyfikowano natomiast fazy ω. Stopy z zakresu 35-40% Ta zawierają po hartowaniu metastabilna faze Β. Dyfrakcje elektronowe wykonane ze stopów zawierających 25-35% Ta wykazują rozmyte refleksy, które jak ustalono wynikają z bliźniakowania na płaszczyznach {110}Β i {332}Β wywołanego naprężeniem w metastabilnej fazie Β.

Słowa kluczowe

EN

Ti-Ta alloys; martensitic transformation; crystal structures

PL

stopy Ti-Ta; przemiany martenzytyczne

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2006
• Tom: Vol. 51, iss. 4
• Strony: 547--550
• Opis fizyczny: Bibliogr. 7 poz., rys.

Twórcy

autor

Dobromyslov A. V.

autor

Dolgikh G. V.

autor

Dutkiewicz J.

autor

Trenogina T. L.

• Institute of Metal Physics, Ural division Of Russian Academy of Sciences, Ekaterinburg, Russia

Bibliografia

• [1] A. V. Dobromyslov, Phase transformation in binary titanium-base alloys with metals of Groups I, IV-VIII of the Periodic Table. Titanium 99, Science&Technology, ed. LV. Gorynin e.a. CRISM "Prometey" 1, 97-106.
• [2] D. J. Maykuth, H. R. Ogden, R. I. Jaffe, Titanium-Tungsten and Titanium-Tantalum Systems. Trans. AIME Journal of Metals 231-237 (1953).
• [3] K. A. Bywater, J. W. Christian, Martensitic transformations in titanium-tantalum alloys. Phil.mag.A. 25, 1249-1273 (1972).
• [4] S. G. Fedotov,T. V. Chelidze, Y. K. Kovneristyy, V. V. Sanadze, Fiz. metal.metalloved. 60, 3, 567-570 (1985).
• [5] J. D. Collon, J. F. Bingert, R S. Dunn, R. A. Patterson, The structure and mechanical properties of Ti-40wt Pet Ta (Ti-15 at. pet Ta). Metallurgical and materials transactions A 25A, 461-472 (1994).
• [6] T. Yamane, J. Ueda, Transmission electron microscope structure of a Ti-9 wt.% Ta alloy ąuenched from P region. Acta met. 14, 438-439 (1966).
• [7] R. A. Spurling,C. G. Rodes, J. C. Williams, Met. Trans. 5, 2597-2600 (1974).