Determination of thermal and mechanical properties of Ni63Cu9Fe8P20 amorphous alloy

• Autorzy: Ziewiec K. , Kurtyka P.

Warianty tytułu

PL

Badanie właściwości cieplnych i mechanicznych amorficznego stopu Ni63Cu9Fe8P20

• Języki publikacji: EN

Abstrakty

EN

Nickel-copper-iron-phosphorus Ni63Cu9Fe8P20 alloy was cast using melt spinning method. The ribbons in as cast state are characterized with use of TEM and X-ray diffraction. Then the ribbons were heated in DTA up to different temperatures and then characterized with use of X-ray diffraction to see the change of the microstructure after heating to elevated temperatures. The melt-spun ribbons in as-cast state were preliminarily compacted in a die and then compressed. The mechanical characteristics of the compacted ribbons at different temperatures were registered.

PL

Stop niklu, miedzi, żelaza i fosforu o składzie Ni63Cu9Fe8P20 odlewano metodą „melt spinning”. Otrzymane taśmy w stanie po odlewaniu były badane przy pomocy transmisyjnego mikroskopu elektronowego (TEM) oraz dyfraktometru rentgenowskiego. Następnie taśmy nagrzewano w różnicowym analizatorze termicznym (DTA) do różnych temperatur a następnie były one ponownie badane przy pomocy dyfraktometru rentgenowskiego. Po odlewaniu metodą „melt spinning” taśmy były wstępnie prasowane w matrycy w celu otrzymania pastylek a następnie poddawane próbie ściskania. Rejestrowano charakterystyki mechaniczne prasowanych taśm przy różnych temperaturach.

Słowa kluczowe

EN

melt-spinning; metallic glass; glass forming ability; thermal stability; crystallization; mechanical properties

PL

szkło metaliczne; właściwości cieplne; krystalizacja; właściwości mechaniczne

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2006
• Tom: Vol. 51, iss. 2
• Strony: 217--220
• Opis fizyczny: Bibliogr. 16 poz., rys.

Twórcy

autor

Ziewiec K.

autor

Kurtyka P.

• Faculty of Mathematics, Physics and Technical Sciences, Pedagogical University, 30-084 Kraków, Podchorążych 2 Str.

Bibliografia

• [1] A. Inoue, T. Nakamura, N. Nishiyama, T. Masumoto, Mater. Trans. JIM 33, 937 (1990).
• [2] A. Peker, W. L. Johnson, Appl. Phys. Lett. 63, 2342 (1993).
• [3] Y. He, R. B. Schwarz, J. I. Archuleta, Appl. Phys. Lett. 69, 1861 (1996).
• [4] K. Russew, B. J. Zappel, F. Sommer, Scripta Metallurgica et Materialia 32, 271-276 (1995).
• [5] Q. Wang.J. J. Blandin.M. Suery.J.M. Pelletier, Mat. Res. Soc. Symp. Proc. 754, 315 (2003).
• [6] Y. Kawamura, T. Shibata, A. Inoue, T. Masumoto, Acta Mater. 46, 253-263 (1998).
• [7] S. N. Nathaudhu, J. T. Im, R. E. Barber, I. E. Anderson, I. Karaman, K. T. Hartwig, Mat. Res. Soc. Symp. Proc. 754, 191 (2003).
• [8] Z. P. Lu, T. T. Goh, Y. Li, S. C. Ng, Acta Mater. 47 (7), 2215-2224 (1999).
• [9] G. J. Fan, W. Loeser, S. Roth, J. Eckert, L. Schullz, J. Mater. Res. 15 (7), 1556-1563 (2000).
• [10] C. C. Hays.J. Schroers, W. L. Johnson, Appl. Phys. Lett. 79 (11), 1605-1607 (2001).
• [11] Y. Zhang, D. Q. Zhao, B. C. Wei. P. Wen, M. X. Pan, W. H. Wang, J. Mater. Res. 16 (6), 1675-1679 2001.
• [12] R. Willnecker.K. Wittmann, G. P. Gorler, Journal of Non-Crystalline Solids, 156-158 (1993) 450.
• [13] A. Inoue, N. Nishiyama, Materials Science and Engineering A226-228, 401-405 (1997).
• [14] Z. P. Lu, Y Li, S. C. Ng, Journal of Non-Crystalline Solids 270, 103-114(2000).
• [15] P. Villars, A. Prince, H. Okamoto, Handbook of Ternary Alloy Phase Diagrams, vols. 8 & 10, ASM International, The Materials Information Siciety, 1995.
• [16] K. Ziewiec, P. Olszewski, R. Gajerski, S. Kac, A. Ziewiec, Z. Kędzierski, Journal of Non-Crystalline Solids 343, 150-153 (2004).