The converter slag reduction process at different ways of reducer adding

• Autorzy: Karbowniczek M. , Dziarmagowski M. , Migas P.

Warianty tytułu

PL

proces redukcji zuzla konwertorowego przy różnych sposobach wprowadzania reduktora

• Języki publikacji: EN

Abstrakty

EN

Findings of laboratory tests of the converter slag reduction process in an electric arc furnace are presented in this paper. Slag premixed with carbon reducer was used for the tests, reducer was also injected in an air jet with a lance. Based on the tests performed it was found that injection of the reducer slowed down the reduction process due to poorer utilisation of the reducer. It was also found that the reduction process rate increased along with the growth in Al2O3 content in the phase reduced. At the same time its content in the resulting non-metallic phase increased. Therefore the mass of the Al.2O3 added should be subject to its content in the converter slag.

PL

W artykule przedstawiono wyniki badań procesu redukcji żużla konwertorowego w elektrycznym piecu łukowym, w warunkach laboratoryjnych.W czasie badań stosowano żużel wymieszany z reduktorem węglowym, a także wdmuchiwano reduktor przy pomocy lancy w strumieniu powietrza. Na podstawie przeprowadzonych badań stwierdzono, że wdmuchiwanie reduktora powoduje zmniejszenie szybkości procesu redukcji z powodu gorszego wykorzystania reduktora. Stwierdzono również, że szybkość procesu redukcji wzrasta wraz ze wzrostem zawartości Al2O3 w redukowanej fazie. Jednocześnie wzrasta również zawartość tego składnika w otrzymywanej fazie niemetalicznej. Z tego powodu masa wprowadzanego Al2O3 powinna być uzależniona od jego zawartości w żużlu konwertorowym.

Słowa kluczowe

EN

converter slag reduction process

PL

redukcja żużla konwertorowego

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2006
• Tom: Vol. 51, iss. 1
• Strony: 156--160
• Opis fizyczny: Bibliogr. 9 poz., rys. tab.

Twórcy

autor

Karbowniczek M.

autor

Dziarmagowski M.

autor

Migas P.

• Faculty of Metallurgy and Materials Science, AGH University of Science and Technology, 30-059 Kraków, Al. Mickiewicza 30

Bibliografia

• [1] S. Kubodera, T. Koyama,R. Ando, R. Kondo, Transactions of the Iron and Steel Institute of Japan 19, 7, 419-427 (1979).
• [2] J. Piret, A. Dralants, Stahl und Eisen 104, 16, 774-778 (1984)
• [3] G. A. Li, F. Zhang, L. Zhang, Z. T. Sui, Journals of Materials and Metallurgy 2, 3, 167-172 (2003).
• [4] M. Dziarmagowski, M. Karbowniczek, M. Pyzalski, J. Okoń, Ironmaking and Steelmaking 19, 1, 45-49 (1992).
• [5] M. Dziarmagowski, Archives of Metallurgy and Materials 47, 3, 287-295 (2002).
• [6] M. Dziarmagowski, Archives of Metallurgy and Materials 48, 2, 201-207 (2003).
• [7] M. Dziarmagowski, Archives of Metallurgy and Materials 49, 1, 73-81 (2004).
• [8] M. Dziarmagowski, Archives of Metallurgy and Materials 49, 3, 699-704 (2004).
• [9] J. Geisseler, 6th International Conference on Molten Slags, Fluxes and Salts, Stockholm-Helsinki, 12-17 June, 2000, 1-14.