Recovery of copper and cobalt from lime originated from amoniacal leaching of high copper Cu-Co-Fe alloy

• Autorzy: Burzyńska L. , Rudnik E. , Partyka J.

Warianty tytułu

PL

Odzysk miedzi i kobaltu ze szlamu otrzymanego w procesie amoniakalnego ługowania wysoko miedziowego stopu Cu-Co-Fe

• Języki publikacji: EN

Abstrakty

EN

The slime produced during ammoniacal leaching of Cu90-Co5-Fe5 alloy was treated in order to recover cobalt and copper. The chemical composition of the slime was determined. The slime was a mixture of Co-Fe-(Cu) alloy and CoO·Fe2O3· xH2O. Slime was dissolved in HCl acid, and then iron was removed from solution by iron compound precipitation with concentrated ammonia. Copper was electrodeposited from purified, acidic solution. After copper recovery, solution was alkalized and series of electrolysis was carried out in order to recover cobalt. Since iron precipitates still contained some amounts of copper and cobalt, they were dissolved in H2SO4 and iron removal was repeated. From ammoniacal solution both copper and cobalt as Co-Cu alloy were electrowon. Total recovery of copper and cobalt was 40% and 55%, respectively.

PL

Przeprowadzono odzysk miedzi i kobaltu ze szlamu otrzymanego w procesie amoniakalnego ługowania stopu Cu90-Co-5-Fe5. Określono skład chemiczny szlamu — stanowił on mieszaninę stopu Co-Fe-(Cu) i CoO·Fe2O3·xH2O. Szlam roztworzono w kwasie solnym, a z uzyskanego roztworu wytrącono związki żelaza za pomocą stężonego roztworu amoniaku. Z oczyszczonego roztworu wydzielono katodowo miedź. Odmiedziowany roztwór zalkalizowano, po czym prowadzono odzysk kobaltu na drodze elektrolizy. Ze względu na współstrącenie się z żelazem znacznych ilości jonów miedzi i kobaltu, osad zwiazków żelaza rozpuszczono w kwasie siarkowym, po czym strącanie przeprowadzono ponownie. Z uzyskanego roztworu amoniakalnego przeprowadzono katodowe współosadzanie stopu Co-Cu. Całkowity odzysk miedzi i kobaltu wynosił, odpowiednio: 40% i 55%.

Słowa kluczowe

EN

cobalt; copper; electrowinning; slime

PL

kobalt; miedź; elektrolityczne otrzymywanie metali; szlam

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2005
• Tom: Vol. 50, iss. 4
• Strony: 1027--1039
• Opis fizyczny: Bibliogr. 14 poz., rys., tab.

Twórcy

autor

Burzyńska L.

• Wydział Metali Nieżelaznych, AGH, 30-059 Kraków, Al. Mickiewicza 30

autor

Rudnik E.

• Wydział Metali Nieżelaznych, AGH, 30-059 Kraków, Al. Mickiewicza 30

autor

Partyka J.

• Wydział Metali Nieżelaznych, AGH, 30-059 Kraków, Al. Mickiewicza 30

Bibliografia

• [1] A. N. Banza, E. Gock, K. Kongolo, Base metals recovery from copper smelter slag by oxidizing leaching and solvent extraction. Hydrometallurgy 67, 63-69 (2002).
• [2] L. Burzyńska, W. Gumowska, E. Rudnik, Recovery of copper from Cu-Co-Fe alloy. Part I. Leaching in ammoniacal solutions. Rudy i Metale Niezelazne 48(4), 166-169 (2003).
• [3] L. Burzyńska, W. Gumowska, E. Rudnik, E. Ziomek, Recovery of copper from Cu-Co-Fe alloy. Part II. Recovery of copper from solution after ammoniacal leaching. Rudy i Metale Niezelazne. 49(2), 69-73 (2004a).
• [4] L. Burzyńska, W. Gumowska, E. Rudnik. Influence of the composition of Cu-Co-Fe alloys on their dissolution in ammoniacal solutions, Hydrometallurgy 71(3-4), 447-455 (2004b).
• [5] L. Burzyńska, E. Rudnik, W. Gumowska, The influence of phase structure on the dissolution of Cu-Co-Fe alloys in sulphuric acid solution and the metals recovery, Hydrometallurgy 71(3-4), 457-463 (2004c).
• [6] S. J. Clark, J. D. Donaldson, Z. I. Khan, Heavy metals in the environment. Part VI: Recovery of cobalt values from spent cobalt/manganese bromide oxidation catalysts. Hydrometallurgy 40, 381-392 (1996).
• [7] S. C. Das, P. Gopala Krishna, Effect of Fe(ITI) during copper electrowinning at higher current density. Int.J.Miner.Process. 46, 91-105 (1996).
• [8] W. Gumowska, 2002, unpublisched results.
• [9] K. N. Han, E. Narita, F. Lawson. The coprecipitation behavior of Co(II) and Ni(II) with Fe(III), Cr(IH) and Al(III) from aqueous ammoniacal solutions. Hydrometallurgy 8, 365-377 (1982).
• [10] E. Ingier-Stocka, W. Szymański, L. Rycerz. Recovery of cobalt from waste following strap processing of hard alloys. Rudy i Metale Niezelazne. 30(2), 60-63 30(3), 109-112 (1985).
• [11] L. B. Sukla, S. C. Panda, P. K. Jena, Recovery of cobalt, nickel and copper from converter slag through roasting with ammonium sulphate and sulphuric amid. Hydrometallurgy 16, 153-165 (1986).
• [12] S. X. Tan, Y. F. Shen, Recovery of nickel and cobalt from waste alloys. Engineering Chemistry and Metallurgy 21(3), 294-297 (2000).
• [13] F. Tumen, N. T. Bailey, Recovery of metals values from copper smelter slag by roasting with pyrite. Hydrometallurgy 44, 261-267 (1994).
• [14] C. Vu, K. N. Han, Leaching behaviour of cobalt in ammonia solutions. Trans. Inst. Min. Metall. 86(9), C119-C125 (1977).