Rolling texture development in duplex type steel with strong initial texture

• Autorzy: Ryś J. , Ratuszek W. , Witkowska M.

Warianty tytułu

PL

Rozwój tekstur walcowania w stali typu duplex o silnej teksturze wyjściowej

• Języki publikacji: EN

Abstrakty

EN

The present examination concerns a development of deformation textures in stainless steel of duplex type with strong initial texture. The ferritic-austenitic steel was subjected to cold-rolling within the range up to 90% of reduction. Different rolling conditions were applied employing three variants of rolling reductions per pass. The investigations included texture measurements, X-ray phase analysis and microstructure observations by means of optical microscopy. The occurrence of strong initial textures of both component phases was found after the preliminary thermo-mechanical treatment. Ferrite exhibited the {100}<001> cubic texture and the dominant component of the austenite texture was the {110}< 001> Goss orientation. The crystallographic relation between the major texture components of both phases was described by Bain orientation relationship. The experimental results indicate that formation of the ferrite-austenite banded structure in the course of cold-rolling along with the plastically compatible deformation of both phases result in the stability of major texture components up to high reductions and exert significant effect on the final rolling textures of ferrite and austenite.

PL

Przedstawione badania dotyczą rozwoju tekstur odkształcenia w stali nierdzewnej typu duplex o silnej teksturze wyjściowej. Stal ferrytyczno-austenityczną poddano walcowaniu na zimno zakresie do 90% deformacji. Zastosowano różne warunki walcowania wykorzystując trzy warianty odkształceń częściowych. Przeprowadzone badania obejmowały pomiary tekstur, rentgenowską analizę fazową oraz obserwacje mikrostruktury za pomocą mikroskopii świetlnej. Po wstępnej obróbce cieplno-mechanicznej stwierdzono występowanie silnej wyjściowej tekstury obu składowych faz. Ferryt wykazywał teksturę sześcienną {100}< 001> a w teksturze austenitu dominującą składową stanowiła orientacja Gossa {110}<001>. Relacje krystalograficzną pomiędzy głównymi składowymi wyjściowej tekstury obu faz opisywała zależność Baina. Uzyskane wyniki wskazują, że tworzenie się pasmowej struktury ferrytu i austenitu w trakcie walcowania na zimno przy równoczesnym plastycznie zgodnym odkształceniu obu faz prowadzi do stabilności głównych składowych tekstury do wysokich stopni odkształcenia wywiera istotny wpływ na końcowe tekstury walcowania ferrytu i austenitu.

Słowa kluczowe

EN

rolling texture; stainless steel; ferritic-austenitic steels; cold rolling

PL

tekstura walcowania; stal nierdzewna; stale ferrytyczno-austenityczne; walcowanie na zimno

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2005
• Tom: Vol. 50, iss. 4
• Strony: 857--870
• Opis fizyczny: Bibliogr. 16 poz., rys., tab.

Twórcy

autor

Ryś J.

autor

Ratuszek W.

autor

Witkowska M.

• Wydział Metalurgii i Inżynierii Materiałowej, AGH, 30-059 Kraków, Al. Mickiewicza 30

Bibliografia

• [1] N. Akdul, J. Foct, Microstructure and Deformation Behaviour of High Nitrogen Duplex Stainless Steel, 1SU International 36, 883 (1996).
• [2] J. Keichel, J. Foct, G. Gottstein, Deformation and Annealing Behavior of Nitrogen Alloyed Duplex Stainless Steels. Part I: Rolling, IS1J International 43, 1781 (2003).
• [3] N. Akdut, J. Foct, Phase Boundaries and Deformation in High Nitrogen Duplex Stainless Steels, I.- Rolling Texture Development, II.- Analysis of Deformation Mechanisms by Texture Measurements, Scripta Metall. et Mater. 32, 103 & 109 (1995).
• [4] N. Akdut, J. Foct, G. Gottstein, Cold Rolling Texture Development of (a/y) Duplex Stainless Steel, Steel Research 67, 450 (1996).
• [5] W. Ratuszek, J. Ryś, K. Chruściel, Texture Development in Cold-rolled Austenitic- Ferritic Steel, Proc. 12-th ICOTOM, Canada, p. 1071 (1999).
• [6] W. Ratuszek, J, Ryś, K. Chruśiciel, Effect of Deformation Mode on Texture Development in Cold-rolled Duplex Steel. Archives of Metallurgy 44, 305 (1999).
• [7] D. Raabe, K. Lucke. Textures of Ferritic Stainless Steels, Mater. Science and Techn. 9,302(1993).
• [8] K. Lucke, M. Holscher, Rolling and Recrystallization Textures of BCC Steels, Textures and Microstructures 14-18, 585 (1991).
• [9] C Donadille, R. Valle, P. Dervin, R. Penelle, Development of Texture and Microstructure During Cold -Rolling and Annealing of fee Alloys: Example of an Austenitic Stainless Steel, Acta Metall. 37, 1547 (1989).
• [10] D. Raabe. Texture and Microstructure Evolution during Cold Rolling of a Strip Cast and of a Hot Rolled Austenitic Stainless Steel, Acta Materialia 45, 1137 (1997).
• [11] A. Tselikov, Stress and Strain in Metal Rolling, Mir Publishers. Moscow (1967).
• [12] H. O. Asbeck, H. Mecking, Influence of Friction and Geometry of Deformation on Texture Inhomogeneities During Rolling of Cu Single Crystals as an Example, Mater. Science and Engng. 34.-111 (1978).
• [13] R. K. Ray, J. J. Jonas, Transformation Textures in Steels, Int. Materials Reviews 35, 1 (1990).
• [14] J. Kyi, Compatibility Effects at Phase Interfaces in Duplex Steel (a/y) Bicrystals, Journal of Mater. Process, and Techn. 64, 343 (1997).
• [15] M. Blicharski, Structure of Deformed Ferrite-Austenite Stainless Steel, Metal Science 18, 92 (1984).
• [16] D. Goodchild, W. T. Roberts, D. V. Wilson, Plastic Deformation and Phase Transformation in Textured Austenitic Stainless Steel, Acta Metallurgica 18, 1137 (1970).