Study of superplastic phenomenon in Fe3Al intermetallic alloy

• Autorzy: Zachman M. , Przetakiewicz W. , Jóźwiak S. , Komorek Z.

Warianty tytułu

PL

Możliwości nadplastycznego odkształcania stopów na osnowie fazy międzymetalicznej Fe3Al

• Konferencja: Scientific Seminar Integrated Study on the foundations of Plastic Deformation of Metals PLASTMET'04 (4; 16-19.11.2004; Łańcut, Poland)
• Języki publikacji: EN

Abstrakty

EN

This paper deals with a study of superplastic phenomenon in Fe3Al intermetallic alloy. The investigated alloy was prepared by melting and casting in an induction furnace in argon atmosphere. The ingots were hammered at 1100&degC and warm rolled at the temperature ranging from 650 to 750&degC. The hot and warm deformed rods were then recrystallized at the temperature ranging from 600 to 900&degC. As a result of this treatment, fine- or coarse-grained microstructure was obtained. Elevated temperature tensile tests were conducted in the air at 850, 900 and 1000&degC. The testing was accomplished at constant velocities ranging from 1.67 x 10ˇ4 to 1.67 x 10ˇ2 sˇ1 in a universal testing machine. The superplastic deformation was observed in both fine- and coarse-grained specimens.

PL

W pracy przedstawiono wyniki badań zjawiska nadplastyczności w stopie na osnowie fazy międzymetalicznej Fe3Al. Badany stop otrzymano na drodze topienia i odlewania w piecu indukcyjnym w atmosferze argonu. Otrzymane wlewki poddano procesowi młotkowania w temperaturze 1100&degC i walcowania na ciepło w zakresie temperatury od 650 do 750&degC. Odkształcone na gorąco i ciepło pręty poddano następnie procesowi rekrystalizacji w zakresie temperatury od 600 do 900&degC. W wyniku przeprowadzonej obróbki uzyskano drobnoziarnistą lub grubokrystaliczną mikrostrukturę. Próby rozciągania w podwyższonej temperaturze przeprowadzono w powietrzu w temperaturze 850, 900 i 1000&degC. Badania realizowano przy stałej prędkości odkształcenia w zakresie od 1.67 x10-4 to 1.67 x 10-2 s-1 przy użyciu uniwersalnej maszyny wytrzymałościowej. W próbkach o mikrostrukturze drobnoziarnistej i grubokrystalicznej obserwowano zjawisko płyniecia nadplastycznego.

Słowa kluczowe

EN

intermetallic phases; superplasticity

PL

fazy międzymetaliczne; nadplastyczność

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2005
• Tom: Vol. 50, iss. 3
• Strony: 691--696
• Opis fizyczny: Bibliogr. 11 poz., rys.

Twórcy

autor

Zachman M.

• Institute of Materials Science and Applied Mechanics Military University of Technology, 00-908 Warsaw, Kaliskiego 2, Poland

autor

Przetakiewicz W.

• Institute of Materials Science and Applied Mechanics Military University of Technology, 00-908 Warsaw, Kaliskiego 2, Poland

autor

Jóźwiak S.

• Institute of Materials Science and Applied Mechanics Military University of Technology, 00-908 Warsaw, Kaliskiego 2, Poland

autor

Komorek Z.

• Institute of Materials Science and Applied Mechanics Military University of Technology, 00-908 Warsaw, Kaliskiego 2, Poland

Bibliografia

• [1] P. J. Maziasz, D. J. Alexander, J. L. Intermeiallics 5 547 (1997).
• [2] C. G. McKamcy, D. H. Pierce, Scripia Metall. Mater. 28, 1173 (1993).
• [3] D. G. Morris, M. Leboeuf. Acta Metall. Mater. 42, 1817 (1994).
• [4] M. W. Grabski, Nadplastyczność strukturalna metali. Wydaw. Śląsk Katowice 1973.
• [5] T. G. Nieh, J. Wadsworth, O. D. Sherby. Superplasticity in Metals and Ceramics, Cambridge University Press, s. 125, Cambridge UK (1997).
• [6] D. Lin, A. Shan, D. Li, Scripta Metall. Mater. 31,1455 (1994).
• [7] D. Lin, A. Shan, Y. Liu, D. Lin, Scripta Metall. Mater. 33, 681 (1995).
• [8] D. Lin, A. Shan, M. Chen, Intermetallics. 4,489 (1996).
• [9] D. Lin, A. Shan, M. Chen, Intermetallics. 6, 243 (1998).
• [10] J. P. Chu, I. M. Liu, J. H. Wu, W. Kai, J. Y. Wang, K. Inoue, Mater. Sci. Eng. A. 258, 236-242(1998).
• [11] D. C. Gao.W. Y. Yang, X. Huang, Z. Q. Sun, Scripta Mater. 44, 501-505 (2001).