Texture evolution and microstructure of ECAP Cu determined by XRD and EBSD

• Autorzy: Schafler E. , Tarkowski L. , Bonarski J. , Kopacz I. , Pippan R. , Stuwe H. P.

Warianty tytułu

PL

Rozwój tekstury i mikrotekstury w Cu po procesie ECAP określonej technikami dyfrakcji rentgenowskiej oraz EBSD

• Konferencja: Symposium on Texture and Microstructure Analysis of Functionally Graded Materials SOTAMA-FGM (03-07.10.2004 ; Kraków, Poland)
• Języki publikacji: EN

Abstrakty

EN

The equal channel angular pressing (ECAP) as a method of severe plastic deformation imposes high strains to the materials deformed. The consequence is the crystal fragmentation of the material leading to an ultrafine or even nanograined structure yielding various improved properties. Since ECAP can achieve extraordinarily high plastic strain of material, the evolution of crystallographic texture, misorientation distribution and crystal size are of high interest. These properties have been investigated for the example of room temperature deformation by ECAP under variation of pass number (up to 16) as well as route type (A, BC and C). Based on the orientation distribution function (ODF) in the Euler angles space, the development of texture and periodical changes of its main components has been analyzed. The evolution of misorientation of the deformed microstructure accompanied with its fragmentation was observed by electron back scatter diffraction (EBSD) in terms of changeable parameters of deformation. The obtained orientation maps also reflect the influence of the macroscopic shear conditions on the development of microstructure.

PL

Metoda silnej deformacji plastycznej ECAP (equal channel angular pressing) pozwala osiagnąć bardzo duże odkształcenie materiału. Konsekwencją zastosowania takiego sposobu odkształcenia jest fragmentacja krystalitów prowadząca do struktury ultradrobnoziarnistej lub nanokrystalicznej poprawiającej znacznie właściwosci mechaniczne materiału. Z uwagi na szczególnie silne odkształcenie plastyczne materiału, interesujący staje się rozwój tekstury krystalograficznej, rozkład wzajemnych dezorientacji krystalitów jak i ich rozmiar. Parametry te były badane na przykładzie próbek Cu odkształconych metodą ECAP w temperaturze pokojowej. Zastosowano różną liczbę przepustów (maksymalnie 16) według drogi A, BC i C. Na podstawie funkcji rozkładu orientacji (FRO) przeanalizowano rozwój tekstury i periodyczne zmiany jej głównych składowych. Zmiany w rozkładzie dezorientacji i mikrostrukturze towarzyszące fragmentacji krystalitów były obserwowane techniką EBSD w zależności od parametrów deformacji. Uzyskane mapy orientacji odzwierciedlają również wpływ makroskopowych warunków ścinania na mikrostrukture odkształcanej miedzi.

Słowa kluczowe

EN

texture; microstructure; ECAP; EBSD; XRD

PL

tekstura; miedź; mikrostruktura; ECAP; EBSD; dyfrakcja rentgenowska

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2005
• Tom: Vol. 50, iss. 2
• Strony: 435--443
• Opis fizyczny: Bibliogr. 18 poz., rys., tab.

Twórcy

autor

Schafler E.

• Wrich Schmid Institute of Materials Science, Austrian Academy of Sciences, A-8700 Leoben, Austria
• Institute of Materials Physics, University of Viena, A-1090 Wien, Austria

autor

Tarkowski L.

• Instytut Metalurgii i Inżynierii Materiałowej im. A. Krupkowskiego, Polska Akademia Nauk, 30-059 Kraków, ul. Reymonta 25

autor

Bonarski J.

• Instytut Metalurgii i Inżynierii Materiałowej im. A. Krupkowskiego, Polska Akademia Nauk, 30-059 Kraków, ul. Reymonta 25

autor

Kopacz I.

• Wrich Schmid Institute of Materials Science, Austrian Academy of Sciences, A-8700 Leoben, Austria

autor

Pippan R.

• Wrich Schmid Institute of Materials Science, Austrian Academy of Sciences, A-8700 Leoben, Austria
• Christian Doppler Laboratory of Local Analysis of Deformation and Fracture, A-8700 Leoben, Austria

autor

Stuwe H. P.

• Wrich Schmid Institute of Materials Science, Austrian Academy of Sciences, A-8700 Leoben, Austria

Bibliografia

• [1] R. Z. Valiev, I. V. Islamgaliev, I. V. Alexandrov, Progr. Mater. Sci. 45, 103 (2000).
• [2] H. Gleiter, Progr. Mater. Sci. 33, 223 (1989).
• [3] Y. Iwahashi, Z. Horita, M. Nemoto, T. G. Langdon. Acta Mater. 46, 3317 (1998).
• [4] M. Furukawa, Y. Iwahashi, Z. Horita, M. Nemoto, T. G. Langdon, Mater. Sci. Eng. A 257, 328 (1998).
• [5] S. C. Vogel, I. J.Beyerlein, M. A. M. Bourke, C. N. Tome, P. Rangaswamy, C. Xu, T. G. Langdon, Mater. Sci. Forum 408-412, 673-468 (2002).
• [6] R. D. Field, K. T. Hartwig,C. T. Necker, J. F. Bingert, S. R. Agnew.Metal. Mater. Trans. A, 33A 965-972 (2002).
• [7] S. R. Agnew, U. F. Kocks. K. T. Hartwig, J. R. Weertman, Proc. 19th Riso Int. Symp. Mater. Sci., Eds. J.V. Carstensen et al., Riso Nat. Lab., Roskilde, DK, 201-207 (1998).
• [8] S. R. Agnew, Proc. 12th Conf. on Textures of Materials, Montreal, August 9-13 (Ed. J. A. Szpunar), 575-580 (1999).
• [9] J. Kuśnierz, Mater. Sci. Forum 426-432, 2807-2812, (2003).
• [10] S. C. Vogel, D. J. Alexander, I. J. Beyerlein, M. A. M. Bourke, D. W. Brown, B. Clausen, C. N. Tome, R. B. Von-Dreele, C. Xu, T. G. Langdon, Mater. Sci. Forum 426-432, 2661-2666, (2003).
• [11] M. A. Gibbs, K. T. Hartwig, L. R. Cornwell, R. E. Goforth, E. A. Payzant, Scripta Mater. 39, 1699-1704 (1998).
• [12] W. J. Kim, S. I. Hong, Y. S. Kim, S. H. Min, H. T. Jeong, J. D. Lee. Acta Mater. 51, 3293-3307, (2003).
• [13] S. R. Agnew, J. A. Horton, T. M. Lillo, D. W. Brown, Scripta Mater. 50, 377-381 (2004).
• [14] G. M. Stoica, S. R. Agnew, E. A. Payzan, D. A. Carpenter, L. J. Chen, P. K. Liaw, TMS Proc. Ultrafine-Grained-Materials-3-Symposium; Eds: Y.T. Zhu, T.G. Langdon, R.Z. Valiev, S.L. Semiatin, D.H. Shin, T.C. Lowe, 427-432. (2004).
• [15] W. Skrotzki, R. Tamm, R. Klemm, E. Thiele, C. Holste, H. Baum, Mater. Sci. Forum 408-412, 667-472 (2002).
• [16] S. H. Yu, D. H. Shin, N. J . Park, M. Y. Huh, S. K. Hwang. Mater. Sci. Forum 408-412. 661-666 (2002).
• [17] S. H. Yu, D. H. Shin, S. K. Hwang, TMS Proc. Ultrafine-Grained-Materials-3-Symposium; Eds: Y.T. Zhu, T.G. Langdon, R.Z. Valiev, S.L. Semiatin, D. H. Shin, T. C. Lowe, 227-234. (2004).
• [18] A. Vorhauer, diploma thesis, University of Leoben, Austria.