The effect of substrate texture and microstructure on the oxidation kinetics of Zr-2.5Nb alloy

• Autorzy: Lin J. , Li H. , Szpunar J. A.

Warianty tytułu

PL

Wpływ tekstury i mikrostruktury podkładu na kinetykę utleniania stopu Zr-2,5Nb

• Konferencja: Symposium on Texture and Microstructure Analysis of Functionally Graded Materials SOTAMA-FGM (October 3-7, 2004 ; Kraków, Poland)
• Języki publikacji: EN

Abstrakty

EN

Measurement of oxidation kinetics of as-received Zr-2.5Nb samples, texture modified Zr-2.5Nb samples, and pure zirconium were carried out by using thermo gravimetric analysis (TGA). A role of substrate texture, substrate microstructure on oxidation kinetics and mechanism of oxidation processes was discussed. The substrate exhibits better corrosion resistance after heat treatment at 560C, while the corrosion resistance becomes worse after heat treatment at 855C. The improvement of oxidation resistance of the substrate is due to the decomposition of Beta-Zr phase, rather than the minor change of texture of alfa-Zr phase induced by the heat treatment. Among the samples tested, Zr-2.5Nb substrate after heat treatment at 560C shows the best oxidation resistance, followed by as-received Zr-2.5Nb sample and the Zr-2.5Nb samples with heat treatment at 855C.

PL

Analiza termograwimetryczna (TGA) była uzyta do pomiaru kinetyki utleniania technicznego stopu Zr-2,5Nb wyjściowego, jak również po zmodyfikowaniu jego tekstury i dla czystego cyrkonu. Rozważana jest rola tekstury i mikrostruktury podkładu na kinetykę oraz mechanizm procesu utleniania. Podkład staje sie lepiej odporny na korozje po obróbce cieplnej w temperaturze 560C, a najmniej odporny po obróbce cieplnej w temperaturze 855C. Polepszenie się odporności na utlenianie podkładu wynika raczej z rozkładu fazy beta-Zr niż z nikłej zmiany tekstury fazy alfa-Zr wynikającej z obróbki cieplnej. Wśród badanych próbek podkład Zr-2,5Nb po obróbce cieplnej w temperaturze 560C wykazuje najlepszą odporność na utlenianie. Gorsze własności wykazują próbki dostarczonego technicznego stopu Zr-2,5Nb oraz Zr-2,5Nb po obróbce cieplnej w temperaturze 855C.

Słowa kluczowe

EN

Zr-2.5Nb; texture; microstructure; oxidation kinetics

PL

Zr-2.5Nb; tekstura; mikrostruktura; kinetyka utleniania

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2005
• Tom: Vol. 50, iss. 1
• Strony: 159--165
• Opis fizyczny: Bibliogr. 9 poz., rys.

Twórcy

autor

Lin J.

• Department of Metals and Materials Engineering, McGill University, Montreal, Quebeck, Canada H3A 2B2

autor

Li H.

• Department of Metals and Materials Engineering, McGill University, Montreal, Quebeck, Canada H3A 2B2

autor

Szpunar J. A.

• Department of Metals and Materials Engineering, McGill University, Montreal, Quebeck, Canada H3A 2B2

Bibliografia

• [1] E. F. Ibrahim, B. A. Cheadle. Can. Metall. Q. 24, 273 (1985).
• [2] M. G. Glavicic, A. A. Szapunar, Y. Pl. Lin, J. Nucí. Mater. 245, 147 (1997).
• [3] J. Lin, H. Li, J. A. Szpunar, R. Bordoni, A. M. Olmedo, M. Villegas, A. J. G. Maroto, Mater. Sci. Eng. A, 381, 104 (2004).
• [4] M. Gri ffiths, R. A. Holt, J. Li, S. Saimoto. Microstructural Science 26, 26-29 (1998).
• [5] H. Li, Textools Software, Resmat. Corp. (1998-2004).
• [6] Y.-R, Lin, J. De Luca, J. Nucí. Mater. 265, 1 (1999).
• [7] N. Petigny,R. Barberis, C. Lemaignan, Ch. Valot, M. Lallemant, J. Nucí. Mater. 280, 318 (2000).
• [8] A. J. G. Maroto, R. Bordoni, M. Villegas, A. M. Olmedo, M. A. Blesa, A. Iglesias, P. Koenig, J. Nucí. Mater. 229, 79 (1996).
• [9] A. Yilmazbayhan, A. T. Motta, R. J. Comsiock, G. P. Sabol, B. Lai, Z. Cai, J. Nucí. Mater. 324, 6 (2004).