Phase formation in the system Ti-Sn-Si

• Autorzy: Vassilev G. P.

Warianty tytułu

PL

Tworzenie się faz w układzie Ti-Sn-Si

• Konferencja: International Conference on Phase Diagram Calculation and Computational Thermochemistry (May 30 - June 4, 2004; Kraków, Poland)
• Języki publikacji: EN

Abstrakty

EN

The phases formed in the system Ti-Sn-Si have been studied by optical and scanning electron microscopy. Two kinds of experiments have been used for the preparation of the alloys: arc-melting in argon atmosphere, and direct chemical interaction between titanium and silicon oxide. A non-stoichiometric ternary compound corresponding approximately to the formula Ti3SnSi has been observed. Data about the mutual solubility of tin and silicon in the ternary extensions of their binary compounds with Ti have been obtained: Ti5Sn3 and Ti2Sn dissolve up to around 9 at.% Si; Ti5Si 4 and Ti5Si3 dissolve up to 6 at.% Sn and 2 at.% Sn, respectively. The silicon does not dissolve into the tin-rich liquid solution, practically. Data about the homogeneity ranges of the solid solution phases have been acquired as well. An isothermal section of the Ti-Sn-Si phase diagram, at 600°C, based on the present work has been constructed.

PL

Stosując mikroskop optyczny oraz skaningowy mikroskop elektronowy przeprowadzono badania tworzących się faz w układzie Ti-Sn-Si. Stopy do badań przygotowano dwoma metodami: poprzez topienie łukiem elektrycznym w atmosferze argonu oraz z bezpośredniej reakcji chemicznej pomiedzy tytanem i tlenkiem krzemu. Zaobserwowano istnienie niestechiometrycznego związku trójskładnikowego o formule zbliżonej do TiSnSi. Uzyskano dane odnośnie wzajemnej rozpuszczalności cyny i krzemu w dwuskładnikowych fazach z tytanem, wynoszące:do ok. 9%at Si w przypadku Ti5Sn3 i Ti2Sn; do 6%at Sn w przypadku ti5Si4 oraz 2%at Sn dla Ti5Si5. Stwierzono praktyczny brak rozpuszczalności krzemu w bogatych w cynę ciekłych roztworach. Zebrano dane odnośnie zakresów rozpuszczalności występujacych roztworów stałych. W oparciu o uzyskane wyniki badań skonstruowano przekrój izotermiczny układu Ti-Sn-Si dla 600st. C.

Słowa kluczowe

EN

Ti-Sn-Si system

PL

stop Ti-Sn-Si

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2004
• Tom: Vol. 49, iss. 3
• Strony: 519--527
• Opis fizyczny: Bibliogr. 21 poz., rys., tab.

Twórcy

autor

Vassilev G. P.

• University of Sofia, Faculty of Chemistry, J. Bourchier Avenue 1, 1164 Sofia, Bulgaria

Bibliografia

• [1] C. R. F. Azevedo, H. M. Flower 26 (3). 353 (2002).
• [2] M. Bulanova, A. Soroka. P. Zheltov, V. Vereshchaka, K. Meleshevich, Z. Metallkd. 90 (7). 505 (1999).
• [3] M. Bulanova, L. Tretyachenko, K. Meleshevich, V. Saltykov, V. Vereshehaka, O. Galadzhyl, L. Kulak. S. Firstov, JALCOM 350, 164 (2003).
• [4] T. Massalski, CD ROM: Binary Alloy Phase Diagrams, ASM International. OH, USA, 1996.
• [5] C. Kupe ,. W. Peng, A. Pisch, F. Goesmann, R. Schmid-Feizer, Z. Metallkd.89(12). 855 (1998).
• [6] H. King. Bull. Alloy Phase Diagr. 2, 401 (1981).
• [7] P. Rogl, Titanium : Physico-chemical Properties of its compounds and Alloys, IAEA, Vienna.1983.
• [8] P. Villars, L. Calvertt, Pearson's Handbook of Crystallographic Data for Intermetallic Phases, ASM, Metals Park. Ohio, 1985.
• [9] B. Kunne n, W. Jeitschko, G. Kotzyba, B. Mosel, Z. Naturforsch. 55b. 425 (2000).
• [10] W. Jeitschko, Metallurgical Transactions 1 (11). 3159 (1970).
• [11] J. Kaiser, M. Haase, W. Jeitschko, Z. Anorg. Allg. Chem. 627. 2369 (2001).
• [12] G. P. Vassilev, JALCOM 365 (1-2). 164 (2004).
• [13] G. P. Vassilev, K. Ishida, JALCOM 376 (1-2), 125 (2004).
• [14] G. P. Vassilev, X. J. Liu, K. Ishida, JALCOM 375 (1-2), 162 (2004).
• [15] G. P. Vassilev, Cryst. Reas. Techn. 39 (9). 763 (2004).
• [16] R. Swalin, Thermodynamics of Solids. John Wiley &Sons, N.Y.-London, 1961.
• [17] I. Barin, Thermochemical Data of Pure Substances, VCH Verlags, Weinheim. 1993.
• [18] Materials Properties Handbook: Titanium Alloys, ASM International, 1994.
• [19] A. Kodentsov, G. Bastin, F. J. J, van Loo, JALCOM 320, 207 (2001).
• [20] K. Ronka, F. van Loo, J. Kivilahti, Scripta Materialia 37, 1575 (1997).
• [21] Chemicool periodic table. http://www-tech.mil.edu/Chemicool/index.html.