Density and molar volume of Al-Li-Mg solid alloys

• Autorzy: Gąsior W. , Moser Z. , Pstruś J.

Warianty tytułu

PL

Gęstość oraz objętość molowa stałych stopów Al-Li-Mg o dużym stężeniu aluminium

• Języki publikacji: EN

Abstrakty

EN

Using the dilatometric method the densities of the solid Al-Li-Mg alloys were measured for two constant values of t=0.85 and 0.95 and for li concentrations changing from 0 to 0.25 mole fraction. The experiments were carried out in the temperature ranges: 293-818K and 293-718K for t=0.05 and 0.15, respectively. The temerature dependences of density were described by the parabolic equation of the form y=a+bT+cT2. The parameters a, b and c were calculated using the least squares method. It was found that the density isoterms for t=0.95 show slight nagative from the linear behaviour, while for t=0.85 an almost linear change is observed when plotting the density from Al-Mg alloys to pure Li density. The molar volume isotherms of Al-Li-Mg solid alloys calculated at the same temperatures as for the density are characterised by slow decreasing with the increase of Li content, except that calculated at 700K for t=0.85 showing an opposite trend.

PL

Stosując metodę dylatometryczną zmierzono gęstość stopów Al-Li-Mg dla stopów charakteryzujących się stałym stosunkiem aluminium do magnezu wynoszącym 0.95 oraz 0.85. Pomiary prowadzono dla stopów, w których stężenie litu zmieniało się od 0 do 0.25 ułamka molowego oraz w zakresie temperatur od 293-818K dla t=0.95 oraz od 293-718 dla t=0.85. Zmiany gęstości z temeraturą zostały opisane zależnościami parabolicznymi postaci y=a+bT+cT2 a parametry a, b i c zostały wyliczone metodą najmniejszych kwadratów. Obliczone izotermy gęstości w 293K oraz 800K dla t=0.95 oraz w 293K dla t=0.85 charakteryzują się słabym ujemnym odstępstwem od zmiany liniowej między gęstością stopu dwuskładnikowego Al-Mg i gęstością Li.Natomiast, wyznaczone w tych samych temperaturach izotermy objętości molowej pokazują nieznaczny spadek z zawartościa litu z wyjatkiem izotermy dla T=700K oraz t=0.85, która charakteryzuje się bardzo słabą wzrostową tendencją.

Słowa kluczowe

EN

Al-Li-Mg alloy; molar volume alloys

• Wydawca: Wydawnictwo Naukowe PWN SA
• Czasopismo: Archives of Metallurgy
• Rocznik: 2003
• Tom: Vol. 48, iss. 4
• Strony: 497--505
• Opis fizyczny: Bibliogr. 23 poz., rys., tab.

Twórcy

autor

Gąsior W.

• Instytut Metalurgii i Inżynierii Materiałowej im. A. Krupkowskiego PAN, 30-059 Kraków, ul. Reymonta 25

autor

Moser Z.

• Instytut Metalurgii i Inżynierii Materiałowej im. A. Krupkowskiego PAN, 30-059 Kraków, ul. Reymonta 25

autor

Pstruś J.

• Instytut Metalurgii i Inżynierii Materiałowej im. A. Krupkowskiego PAN, 30-059 Kraków, ul. Reymonta 25

Bibliografia

• [1] J. F. Smith, Z. Moser, J. Nuci. Mater. 59, 158-174 (1976).
• [2] Z. Moser, W. Gąsior, F. Sommer, G. Schwitzgebel, B. Predel, Met. Trans. 17B, 791-795 (1986).
• [3] Z. Moser, F. Sommer, B. Predel, Z. Metallkde 790, 705-711 (1988).
• [4] Z. Moser, F. Sommer. J. J. Lec, B. Predel, Thermochim. Acta 142, 117-125 (1989).
• [5] W. Gąsior, Z. Moser, J. Chim. Phys. 90, 387-397 (1993).
• [6] W. Gąsior, G. Schwitzgebel, Archives of Metallurgy 37, 25-36 (1992).
• [7] W. Gąsior, G. Schwitzgebel, H. Ruppersberg, Archives of Metallurgy 39, 26-33 (1994).
• [8] W. Gąsior, Z. Moser, W. Zakulski, Archives of Metallurgy 39, 355-369 (1994).
• [9] W. Gąsior, Z. Moser, W. Zakulski, J. Non-Crystalline Solids 205-207, 379-382 (1996).
• [10] W. Gąsior, Z. Moser. Archives of Metallurgy 44, 83-91 (1999).
• [11] W. Gąsior, Z. Moser, W. Zakulski, G. Schwitzgebel, Met. Materials Trans. A 27A, 2419-2428 (1996).
• [12] W. Gąsior, Z. Moser, J. Nuci. Mater. 249, 77-83 (2001).
• [13] Z. Moser, R. Agarwal, F. Sommer, B. Predel, Z. Metallkde, 82, 317-321 (1991).
• [14] Z. Moser, W. Gąsior, F. Sommer, W. Zakulski, H. J. Seifert, H. L. Lukas, CALPHAD XXIV, Kyoto. Japan, 21-26 May 1995, Programm & Abstracts, p. 29.
• [15] Z. Moser, W. Gąsior, B. Onderka, J. Phase Equilibria 23, 127-133 (2002).
• [16] W. Gąsior, Z. Moser, J. Pstruś, J. Phase Equilibria 19, 234-238 (1998).
• [17] W. Gąsior, Z. Moser, J. Pstruś, J. Phase Equilibria 19, 568-571 (1998).
• [18] W. Gąsior, Z. Moser, J. Pstruś, J. Phase Equilibria 21, 167-171 (2000).
• [19] W. Gąsior, Z. Moser, Archives of Metallurgy 46, 455-463 (2001).
• [20] W. Gąsior, Z. Moser, Archives of Metallurgy 46, 269-277 (2001).
• [21] W. Gąsior, Z. Moser, Scandinavien Journal of Metallurgy 31, 353-358 (2002).
• [22] W. Wołczyński, W. Gąsior, Z. Moser, Archives of Metallurgy 47, 223-234 (2002).
• [23] P. Villars, A. Prince, H. Okamoto, Handbook of Ternary Alloy Phase Diagrams. ASM International 4. 3845-65 (1995).