Calculation of the liquidus surface in ternary Co-Cu-Si system

• Autorzy: Zabdyr L.

Warianty tytułu

PL

Obliczenie powierzchni likwidus w układzie trójskładnikowym Co-Cu-Si

• Języki publikacji: EN

Abstrakty

EN

Constituent binary subsystems Co-Cu, Co-Si and Cu-Si were described briefly, and their calculated phase diagrams were presented and invariant reactions of the liquid phase, as well. Thermodynamic parameters for Co-Si and Cu-Si systems were taken from the former own assessments and coefficients for binary system Co-Cu were accepted from the one of the most recent literature evaluations. Tdb file was then set up by means of binary formalism. Equilibrium calculations resulted in the parameters of all invariant reactions with liquid phase involved, and the S c h e i l reaction scheme was constructed as well. Graphical representation of the calculated liquidus surface was shown as the projection onto the G i b b s triangle plane.

PL

Podano zwięzłe charakterystyki składowych układów podwójnych Co-Cu, Co-Si, Cu-Si oraz zaprezentowano ich obliczone wyktesy fazowe i parametry równowag niezmienniczych fazy ciekłej. Parametry termodynamiczne dla układów Co-Si i Cu-Si zaczerpnieto z wcześniejszych opracowań własnych a dla ukladu Co-Cu zaakceptowano wyniki jednego z najnowszych opracowań z literatury. Termodynamiczną bazę danych dla rozpatrywanego układu potrójnego zestawiono za pomocą tzw. formalizmu dwójkowego. W wyniku obliczeń równowagowych uzyskano parametry równowag niezmienniczych z udziałem fazy ciekłej; obliczoną powierzchnię likwidus przedstawiono w postaci projekcji politermicznej na płaszczyznę trójkąta Gibbsa oraz skonstruowano schemat reakcji Scheila dla tego układu trójskładnikowego.

Słowa kluczowe

EN

liquidus surface; Co-Cu; Co-Si; Cu-Si; binary formalism

PL

powierzchnia likwidusu; układ Co-Cu; układ Co-Si; Cu-Si; formalizm dwójkowy

• Wydawca: Wydawnictwo Naukowe PWN SA
• Czasopismo: Archives of Metallurgy
• Rocznik: 2002
• Tom: Vol. 47, iss. 3
• Strony: 321--334
• Opis fizyczny: Bibliogr. 17 poz., rys., tab.

Twórcy

autor

Zabdyr L.

• Instytut Metalurgii i Inżynierii Materiałowej im. A. Krupkowskiego, PAN, 30-059 Kraków, ul. Reymonta 25

Bibliografia

• [1] J. Gronostajski, Rudy i Metale Nieżelazne 13, 4, 164 (1968).
• [2] K. Fitzner, unpublished data.
• [3] L. Kaufman, CALPHAD 2, 117 (1979).
• [4] M. Hasebe, K. Oikawa, T. Nishizawa, CALPHAD 4, 83 (1980).
• [5] K.C.H. Kumar, P. Wollants, Calphad XXVIII. Grenoble, 2-7 May, 1999.
• [6] J. Kubista, J. Vrestal, J. Phase Equilibria 21 (2), 125 (2000).
• [7] L. Kaufman, CALPHAD 3, 45 (1979).
• [8] K. Ishida, T. Nishizawa, Journal of Phase Equilibria 12, 578 (1991).
• [9] S.-D. Choi, CALPHAD 16, 151 (1992).
• [10] L. Zabdyr, E. Foryst, G. Garzeł, M. Kopyto, K. Fitzner, IMIM Annual Report 2000, 1/3.
• [11] A. Dinsdale, CALPHAD 15 (4), 317 (1991).
• [12] R. W. Olesinski, G. Abbaschian, Bull. Alloy Phase Diagrams 7 (2), 170 (1986).
• [13] D. Luedecke, CALPHAD 11(2), 135 (1987).
• [14] M.H.G. Jacobs, P.J. Spencer, J. Chim. Phys. 90, 167 (1993).
• [15] T Jantzen, S.G. Fries, I. Hurtado, M.H.G. Jantzen, P.J. Spencer, final COST Meeting proceedings. Vaals, March 1997.
• [16] L. Zabdyr, B. Onderka, M. Kopyto, K. Fitzner, IMIM Annual Report 1999, 9/2.
• [17] T. Jantzen, H.L. Lukas, I. Hurtado, S.G. Fries, TOFA 2000, May 8-11, 2000, Stockholm.