Temperature of vacuum cast knock out from plaster mould

• Autorzy: Pawlak M.
• Języki publikacji: EN

Abstrakty

EN

The results of investigations on knocking out temperature of CuSn10, CuSn5Zn5Pb5 and AlSi11 castings vacuum prepared in gypsum moulds. The experimental castings were p rep ared in form of rings of diameters [...] 30, 20 and 10 mm, width 10mm and wall thickness g= 0,6; 0,8; 1,0 and 2,0 mm respectively. Casting temperatures were 1120 and 1200 for bronzes and 700 and 800 C for silumin. The crack sensitivity of the rings was evaluated. It can be stated, on the base of the tests, that casting should be knocked out as soon as possible after pouring basin crystallizes. In case of tested castings the limiting dimensions of the rings are diameter [...] 30 mm and and thickness g=0,8 for CuSn10. Castings made of CuSn5Zn5Pb5 and AlSi11 do not reveal the crack sensitivity.

Słowa kluczowe

EN

innovative foundry technologies; innovative foundry material; precision casting; plaster mould; temperature of casting knock out

PL

innowacyjne technologie odlewnicze; innowacyjne materiały odlewnicze; odlewanie precyzyjne; forma odlewnicza

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2011
• Tom: Vol. 11, iss. 4
• Strony: 97--102
• Opis fizyczny: Bibliogr. 5 poz., rys., tab., wykr.

Twórcy

autor

Pawlak M.

• Department of Materials Engineering and Production Systems, Technical University of Lodz 1/15 Stefanowskiego Str., 90-924 Łódź, Poland,

Bibliografia

• [1] Wiktorski M., Pawlak M., Niedźwiedzki Z.: Stanowisko do badania współczynnika przewodzenia ciepła materiałów stosowanych na formy gipsowe w odlewnictwie precyzyjnym. Archiwum Odlewnictwa, PAN, 2004, nr 13, s. 232-240.
• [2] Pawlak M.: Ability of the CuSn10 and CuSn5Zn5Pb5 bronzes fullfilment of plaster mould cavity during underpressure casting, Archives of Foundry Engineering, Vol. 10, Issue 4, October-December 2010, p. 163-168.
• [3] PN-86/B-04360 Spoiwa gipsowe. Metody badań. Oznaczanie cech fizycznych (Bindersbased on calciumsulfate. Method of tests for physicalproperties).
• [4] Pawlak M., Niedźwiedzki Z.: Computer aided process of dimensional distortion determination of bounded plaster plaster, Part II (Komputerowe wspomaganie procesu określania zmiany wymiarowej związanej gipsowej masy formierskiej, cz. II). Archives of FoundryEnginerring,Vol. 10, Issue 1, January - March 2010, p. 105-108.
• [5] Pawlak M., Niedźwiedzki Z.: Computer aided process of dimensional distortion determination of bounded plaster plaster, (Komputerowe wspomaganie procesu określania zmiany wymiarowej związanej gipsowej masy formierskiej) Archives of Foundry Engineering, Vol. 9, Issue 3, July - September 2009, p. 261-266.