The influence of heat treatment on selected physical properties of aluminized steel strips

• Autorzy: Żaba K.

Warianty tytułu

PL

Wpływ obróbki cieplnej na wybrane właściwości fizyczne aluminiowanych taśm stalowych

• Języki publikacji: EN

Abstrakty

EN

The selected examinations of physical properties of the aluminised steel strips intended for elements of exhaust systems are characterized in the paper. Strips in their initial state and after the heat treatment, at temperatures from 250 to 700 C for 30 to 1440 minutes, were investigated. The macro and microscopic observations of the surface of the coating before and after heating are presented. The most of attention was dedicated to investigations of the erosion resistance in a stream of solid particles, simulating the behaviour of the coating exposed to various kinds of fine-grained particles. The results are presented as the mass losses, changes of the coating thickness and observations of the effect of the abrasive-penetrating agent. Examinations of microhardness and microscopic observations at the cross-section of the coating were also performed.

PL

W artykule scharakteryzowano wybrane badania własności fizycznych, aluminiowanych taśm stalowych, przeznaczonych m. in. na elementy układów wydechowych. Badaniom poddano taśmy w stanie bez i po obróbce cieplnej w temperaturze 250-700 C w czasie 30-1440 min. Przedstawiono obserwacje makro i mikroskopowe powierzchni powłoki przed i po nagrzewaniu. Najwięcej uwagi poświęcono badaniom odporności na erozję w strumieniu cząstek stałych, symulujących zachowanie się powłoki narażonej na działanie różnego rodzaju elementów drobnoziarnistych. Wyniki przedstawiono w postaci ubytku masy, zmian grubości powłoki oraz obserwacji po działaniu czynnika ścierno-penetrującego. Wykonano także badania mikrotwardości oraz obserwacji mikroskopowych powłoki na przekroju.

Słowa kluczowe

EN

Al-Si coating; erosion resistance in a stream of solid particles; microhardness

PL

obróbka cieplna; aluminiowe taśmy stalowe

• Wydawca: Springer ; Wrocław University of Science and Technology
• Czasopismo: Archives of Civil and Mechanical Engineering
• Rocznik: 2010
• Tom: Vol. 10, no 4
• Strony: 107--118
• Opis fizyczny: Bibliogr. 16 poz., rys., wykr.

Twórcy

autor

Żaba K.

• University of Science and Technology, al. Mickiewicza 30, 30-059 Kraków, Poland

Bibliografia

• [1] ASTM A463/A463M - 06: Standard specification for steel sheet, aluminium-coated, by the hot-dip process.
• [2] ASM Handbook: Surface engineering, ASM International, Handbook Committee, Vol. 5, 1994, pp. 346.
• [3] EN 10346:2009: Continuously hot-dip coated steel flat products. Technical delivery conditions.
• [4] Inoue Y., Kikuchi M.: Present and future trends of stainless steel for automotive exhaust system, Nippon Steel Technical Report, No. 88, 2003, pp. 62-69.
• [5] Kawase H., Takezoe A.: Peeling of coated metal due to severe press-forming in aluminized steel sheet, Transactions of the Iron and Steel Institute of Japan, Vol. 22, No. 5, 1982, pp. 371-376.
• [6] Kobayashi S., Yakou T.: Control of intermetallic compound layers at interface between steel and aluminium by diffusion-treatment, Materials Science and Engineering: A, Vol. 338, No. 1-2, 2002, pp. 44-53.
• [7] Żaba K., Nowak S., Kąc S., Wróbel M.: Research on temperature time and atmospheric impact on Al-Si coat of low-carbon steel strips, International Conference: Problems of modern techniques in aspect of engineering and education, Pedagogical University of Cracow, Institute of Technology - Cracow, Monography, 2006, pp. 73-78.
• [8] Wang Chaur-Jeng, Chen Shih-Ming: The high-temperature oxidation behaviour of hotdipping Al-Si coating on low carbon steel, Surface and Coatings Technology, Vol. 200, No. 22-23, 2006, pp. 6601-6605.
• [9] Gul Hameed Awan, Faiz ul Hasan: The morphology of coating/substrate interface In hot-dip-aluminized steels, Materials Science and Engineering: A, Vol. 472, No. 1-2, 2007, pp. 1-9.
• [10] Kee-Hyun Kim, Van-Daele Benny, Van-Tendeloo Gustaaf, Young-Sug Chung, Jong Ku Yoon: Analysis of the intermetallic compound formed in hot dip aluminized steel, Advanced Materials Research, Vol. 15-17, 2007, pp. 159-163.
• [11] Gul Hameed Awan, Faiz ul Hasan: The morphology of coating/substrate interface in hotdip-aluminized steels, Materials Science and Engineering: A, Vol. 472, No. 1-2, 2008, pp. 157-165.
• [12] Wang Deqing: Phase evolution of an aluminized steel by oxidation treatment, Applied Surface Science, Vol. 254, No. 10, 2008, pp. 3026-3032.
• [13] Żaba K., Kąc S.: Badania efektów działania wysokiej temperatury, czasu i atmosfery na użytkowe własności powłoki Al-Si na stalowych rurach przeznaczonych na elementy układów wydechowych, Rudy i Metale Nieżelazne, Vol. 53, No. 11, 2008, pp. 694-704.
• [14] Żaba K.: The influence of annealing temperature and time on the structure and features of the Al-Si coatings on steel sheets, purposed for pressured welded pipes applied in exhaust systems, Archives of Civil and Mechanical Engineering, Vol. 6, No. 2, 2006, pp. 145-152.
• [15] Żaba K.: The influence of temperature and time of exhibition on a change of Al-Si coating thickness and surface texture on the steel plates, Archives of Metallurgy and Materials, Vol. 55, No. 1, 2010, pp. 151-162.
• [16] PN-EN ISO 4516:2004 Powłoki metalowe i inne nieorganiczne. Badania mikrotwardości metodą Vickersa i Knoopa.