Effect of phosphorus on vacuum carburising depth of iron compacts

• Autorzy: Widanka K.

Warianty tytułu

PL

Wpływ fosforu na głębokość nawęglania próżniowego wyprasek żelaznych

• Języki publikacji: EN

Abstrakty

EN

The work was aimed at determining the effect of phosphorus on vacuum carburising of iron compacts with density over 7.2 gcm-3. An attempt was made to determine the effectiveness of phosphorus on carbon diffusion rate into the material of compacts with no additional effect of interconnected porosity. Vacuum carburising of compacts, made with a blend of powders ASC100.29 and PASC60, was carried out at 1050 °C in a laboratory vacuum furnace. The effect of phosphorus content within 0.1% to 0.6% on the vacuum carburising depth was analysed. It was found that the phosphorus addition up to 0.4% increased the carburising depth by ca. 20% in comparison with the compacts of pure iron.

PL

Celem pracy było określenie wpływu fosforu na przebieg nawęglania próżniowego wyprasek żelaznych o gęstości powyżej 7,2 gcm-3. Podjęto próbę oceny efektywności oddziaływania fosforu na szybkość dyfuzji węgla w głąb materiału wyprasek bez dodatkowego wpływu porowatości otwartej. Nawęglanie próżniowe wyprasek, wykonanych z mieszanki proszków żelaza ASC100.29 i PASC60, przeprowadzono w temperaturze 1050 °C, w laboratoryjnym piecu próżniowym. Analizowano wpływ dodatku fosforu, o zawartości z zakresu 0,1-0,6%, na głębokość nawęglania próżniowego badanych wyprasek. Wykazano, że fosfor dodany do proszku żelaza w ilości 0,4% zwiększa głębokość nawęglania wyprasek o ok. 20% w porównaniu do wyprasek z czystego żelaza.

Słowa kluczowe

EN

phosphorus; vacuum carburising; iron compacts

PL

fosfor; próżnia; żelazo

• Wydawca: Springer ; Wrocław University of Science and Technology
• Czasopismo: Archives of Civil and Mechanical Engineering
• Rocznik: 2010
• Tom: Vol. 10, no 1
• Strony: 85--91
• Opis fizyczny: Bibliogr. 11 poz., rys., tab., wykr.

Twórcy

autor

Widanka K.

• Wrocław University of Technology, Institute of Materials Science and Applied Mechanics, Materials Science Division, Wrocław, Poland

Bibliografia

• [1] Dautzenberg N.: Properties of sintered steels made of water atomised prealloyed and alloyed steel powders, Archiv Eisenhuttennw, 1969, Vol. 40, No. 4, pp. 351–357.
• [2] Lindskog P., Carlsson A.: Sintered alloys on matrix of sponge iron powder with ferrophosphorus addition, Powder Metallurgy (polish edition), 1975, Vol. 8, No. 1, pp. 9–15.
• [3] Beiss P., Ruthardt R., Warlimont H.: Powder metallurgy data, Landolt–Börnstein Online, Vol. 2A1, 2003, Springer Berlin Heidelberg.
• [4] Herling D.H., Hansen P.T.: Heat treating ferrous P/M parts, Advanced Materials & Processes, 1998, Vol. 153, No. 4, pp. 44CC–44GG.
• [5] Herring D.H.: Pros and cons of atmosphere and vacuum carburizing, Industrial Heating, 2002, January, pp. 45–48.
• [6] Weber R.G.: Vacuum carburizing and carbonitriding of P/M ferrous alloys, Int. J. of Powder Metall., 1983, Vol. 15, No. 2, pp. 383–391.
• [7] Kula P., Pietrasik R., Dybowski K.: Vacuum carburizing-process optimisation, Journal of Materials Processing Technology, 2005, Vol. 164–165, pp. 876–881.
• [8] Preisser F., Seemann R., Zenker W.R.: Update on vacuum-based carburizing, Advanced Materials & Processes, 1998, Vol. 153, No. 6, pp. 84II–84LL.
• [9] Beauchensne D., Kenosha, Wis, Doussot X.: Vacuum carburizing: A technology whose time has come, Industrial Heating, 2003, January, pp. 29–33.
• [10] Larsen R.M.: On phosphorus as additive in iron based soft PM magnets, Powder Metallurgy, 2004, Vol. 47, No. 4, pp. 332–334.
• [11] Raghaven V.: C-Fe-P(carbon-iron-phosphorus), Journal of Phase Equilibria and Diffusion, 2004, Vol. 25, No. 6, pp. 541–542.