Modelling of casting, hot-charge rolling and cold-strip production from high-carbon steel

Wybrane pełne teksty z tego czasopisma
Identyfikatory
Warianty tytułu
PL
Symulacja odlewania, walcowania z jednoczesnym nagrzewaniem oraz produkcji na zimno taśmy ze stali wysokowęglowej
Języki publikacji
EN
Abstrakty
EN
Structure development of steel with 0.62 wt. % C during its laboratory casting, conventional as well as hot-charge rolling, cold-strip rolling and soft annealing in controlled atmosphere was studied. Effect of changes of processing parameters on final mechanical properties of a strip was determined. It was confirmed that microstructure and properties of strip produced by the effective and energy-saving hotcharge rolling could be more beneficial than after conventional rolling. Grain size seems to be more intensively effected by cooling rate and heating time of the casting than by phase transformations occurred before conventional rolling. As to final mechanical properties of thin strip from the steel applied, the ferrite fraction in the hot-rolled microstructure plays a key role. Due to higher ferrite content resulting from the finer austenite grain size, samples obtained after laboratory remelting and casting are characterized by lower yield stress and strength, together with higher ductility, which should be advantageous for subsequent processing of real strips in question.
PL
Badano rozwój struktury stali z zawartością węgla 0.62% podczas laboratoryjnego odlewania, walcowania konwencjonalnego i walcowania z jednoczesnym nagrzewaniem, walcowania taśmy na zimno oraz wyżarzania w atmosferze definiowanej. Ustalono, jak zmiany parametrów obróbki wpływają na końcowe właściwości mechaniczne. Stwierdzono, że mikrostruktura oraz właściwości taśmy produkowanej metodą efektywnego oraz energooszczędnego walcowania z jednoczesnym nagrzewaniem mogą być korzystniejsze niż po walcowaniu konwencjonalnym. Na wielkość ziarna prawdopodobnie znacznie silniej wpływa szybkość ochładzania podczas odlewania i czas nagrzewania niż transformacje fazowe poprzedzające walcowanie konwencjonalne. Zasadniczy wpływ na mechaniczne właściwości końcowe cienkiej taśmy z badanej stali ma frakcja ferrytyczna zawarta w mikrostrukturze walcowanej na gorąco. Z powodu większej zawartości ferrytu, wynikającej z drobnoziarnistej struktury austenitycznej, próbki uzyskane w trakcie laboratoryjnego przetapiania i odlewania charakteryzuje niższa granica sprężystości i wytrzymałości oraz większa sprężystość, co powinno być zaletą w obróbce wspominanych taśm.
Rocznik
Strony
103--113
Opis fizyczny
Bibliogr. 13 poz., rys., wykr.
Twórcy
autor
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
autor
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
autor
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
autor
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
autor
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
autor
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
autor
  • Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15, 70833 Ostrava, Czech Republic
autor
  • ISPAT NOVA HUT, a.s., 707 02 Ostrava – Kuncice, Czech Republic
autor
  • ISPAT NOVA HUT, a.s., 707 02 Ostrava – Kuncice, Czech Republic
Bibliografia
  • [1] Bleck W.: Metallkundliche Auswirkungen von Energiesparmassnahmen im Bereich des Warmbandwerkes auf die Eigenschaften von kaltgewaltzten Stählen, ECSC report EUR No. 13935 DE, Brussels, 1992.
  • [2] Kopp R. et al.: Casting and rolling in one heat, Steel research, 2002, Vol. 73, No. 8, 321.
  • [3] http://www.fmmi.vsb.cz/model/.
  • [4] Schindler I. et al.: Laboratory modelling of direct rolling of steel thin slabs, Proc. of the 5th International ESAFORM Conference on Material Forming, Akapit, Kraków, 2002, 387.
  • [5] Schindler I. et al.: Dal getto alle lamine in acciaio, Fonderia Pressofusione, 2003, Vol. 53, No. 4, 32.
  • [6] Schindler I., Kure F.: Potentialities of Physical Modelling of Flat Rolling Processes at VSB – Technical University of Ostrava, Proc. of the 6th International Conference STEEL STRIP 2001, Steel Strip Society, Ostrava, 2001, 375.
  • [7] Schindler I. et al.: Laboratory casting, one-heat processing and cold strip rolling of a high-carbon steel, Proc. of FORMING 2003, Politechnika Slaska, Katowice, 2003, 147.
  • [8] Groch A.G.: TSP – The Steckel mill enters the thin slab game, Steel Times, 1994, Vol. 222, No. 1, 28.
  • [9] Ramaswamy V., Benner F.G., Rosenthal D.: Advanced hot strip Steckel mills for special steel, Metallurgical Plant and Technology International, 1996, Vol. 19, No. 2, 70.
  • [10] Kramer S., Kneppe G., Rosenthal D.: Technology and performance of modern Steckel mills, Iron and Steel Engineer, 1997, Vol. 74, No. 7, 17.
  • [11] Chowaniec F. et al.: Latest result from the production of peritectic steel grades in a medium-slab caster and a tandem Steckel mill at Nova Hut, Czech Republic, Proc. of VAI 8th Continuous Casting Conference, Voest Alpine Linz, 2000.
  • [12] Cerny L., Schindler I., Boruta J.: Research of Possibilities of Dynamic Recrystallization Initiation at Hot Rolling of Low-Carbon Steel at Two-Stand Steckel Rolling Mill, Proc. of TECHNOLOGY 2003, SF STU Bratislava, 2003, abstract 113 + CD-ROM.
  • [13] Schindler I. et al.: Structure Development at Hot Rolling of a 13Cr25 Ferritic steel, Proc. of TECHNOLOGY 2003, SF STU Bratislava, 2003, abstract 140 + CD-ROM.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPZ2-0019-0025
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.